摘要:
Flame-resistant metal-containing polyacyloxalamidrazone filaments and a process for their production in which the filaments are treated with one or more solvent-soluble compounds of at least one of the metals zinc, tin, cadmium, barium, strontium, calcium, antimony and tantalum for a period of time sufficient to render the filaments resistant to flame.
摘要:
AN AQUEOUS ALKALI METAL HYDROXIDE SOLUTION IN WHICH THERE IS DISSOLVED A POLYVACYLAXAMIDRAZONE, THE RESULTING ALKALINE POLYMER SOLUTION BEING USEFUL FOR THE PRODUCTION OF HEAT-RESISTANT SHAPED PRODUCTS SUCH AS FILAMENTS, FILM, COATING AND THE LIKE. A PROCESS FOR PRODUCING THESE PRODUCTS INCLUDES THE STEPS OF FORMING THE POLYMER SOLUTION INTO A FILAMENT OR FILM IN CONTACT WITH AN ACID PRECIPITATION BATH, WASHING THE PRECIPITATE AND SUBSEQUENTLY HEATING TO A TEMPERATURE OF APPROXIMATELY 230-350*C.
摘要:
PROCESS FOR THE PRODUCTION OF 2-MERCAPTO-BENZOTHIAZOLE BY REACHING ANILINE AND ELEMENTARY SULFUR WITH TRITHIANE AT AN ELEVATED TEMPERATURE AND PREFERABLY UNDER SUPERATMOSPHERIC PRESSURE. THE PRODUCT IS OBTAINED IN GOOD YIELDS AND PURITY AND IS KNOWN TO BE USEFUL AS A VULCANIZATION ACCELERATOR.
摘要:
As a composition of matter, a dilute aqueous alkaline solution in which there is dissolved a polyhydrazide characterized by recurring polymeric units of the formula -NH-NH-CO-R-CO-NH-NH-COR''-CO-n (I) in which R and R'' represent divalent aromatic or heterocyclic radicals such a phenylene, naphthalene or diphenylether and n is a large integer. This alkaline polymer solution can be used to form shaped products which in turn can be converted by heating into thermally-stable and insoluble polyoxadiazoles.
摘要:
PRODUCTION OF A POLYACHYOXAMIDRAZONE BEARING A METHYL GROUP AS A SUBSTITUENT ON NITROGEN ATOMS IN THE POLYMER CHAINS, THE POLYMER BEING PRODUCED BY REACTION OF N, N''-DIMETHYL OXALIC ACID BISAMIDRAZONE WITH A DICARBOXYLIC ACID DICHLORIDE OR DIBROMIDE IN THE PRESENCE OF AN ACID ACCEPTOR. THE RESULTING POLYCONENSATE EXHIBITS VALUABLE PROPERTIES AS A FIBER-FORMING OR FILM-FORMING PRODUCT.
摘要:
PROCESS FOR THE CATALYTIC PRODUCTION OF DIMETHYL SULFIDE IN WHICH METHANOL AND HYDROGEN SULFIDE CAN BE REACTED IN ABOUT EQUIMOLAR AMOUNT TO ACHIEVE ALMOST QUANTITATIVE YIELDS OF DIMETHYL SULFIDE BY CARRYING OUT THE REACTION IN THE PRESENCE OF A CATALYST CONSISTING ESSENTIALLY OF ALUMININUM OXIDE HAVING A SUPERIMPOSED LAYER OF UP TO ABOUT 10% BY WEIGHT OF SILICA APPLIED THERETO.
摘要:
PRODUCTION OF A POLYACYLOXAMIDRAZONE BEARING PHENYL SUBSTITUTENTS ON THE OXAMIDRAZONE PORTIONS OF THE LINEAR POLYMER CHAIN, THE POLYMER BEING PRODUCED BY REACTION OF N,N''-BIS-(PHENYL)-OXAMIDRAZONE WITH A DICARBOXYLIC ACID DICHLORIDE OR DIBROMIDE IN THE PRESENCE OF AN ACID ACCEPTOR. THE RESULTING POLYCONDENSATE EXHIBITS VALUABLE PROPERTIES AS A FIBER-FORMING OR FILM-FORMING PRODUCT AND IS EASILY CONVERTED INTO THE CORRESPONDING AND MORE STABLE POLY-BIS(1,2,4-TRIAZOLE) WHICH IS ALSO PHENYL-SUBSTITUTED.