摘要:
A method for producing a silicon steel normalizing substrate comprises steelmaking, hot rolling and normalizing steps. A normalizing furnace is used in the normalizing step, and along a moving direction of strip steel, the normalizing furnace sequentially comprises: a preheating section, a nonoxidizing heating section, a furnace throat, furnace sections for subsequent normalizing processing, and a delivery seal chamber. Furnace pressures of the normalizing furnace are distributed as follows: the furnace pressure of a downstream furnace section adjacent to the furnace throat along the moving direction of the strip steel is the highest, the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an inlet direction of the normalizing furnace, and the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an outlet direction of the normalizing furnace.
摘要:
A method for producing a silicon steel normalizing substrate comprises steelmaking, hot rolling and normalizing steps. A normalizing furnace is used in the normalizing step, and along a moving direction of strip steel, the normalizing furnace sequentially comprises: a preheating section, a nonoxidizing heating section, a furnace throat, furnace sections for subsequent normalizing processing, and a delivery seal chamber. Furnace pressures of the normalizing furnace are distributed as follows: the furnace pressure of a downstream furnace section adjacent to the furnace throat along the moving direction of the strip steel is the highest, the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an inlet direction of the normalizing furnace, and the furnace pressure decreases gradually from the furnace section with the highest furnace pressure to a furnace section in an outlet direction of the normalizing furnace.
摘要:
A non-oriented electrical steel sheet with fine magnetic performance, and a calcium treatment method therefor, including an RH (Ruhrstahl-Heraeus) refinement step. The RH refinement step sequentially comprises a decarbonization step, an aluminum deoxidation step, and a step of adding calcium alloy. In the step of adding calcium alloy, time when the calcium alloy is added satisfies the following condition: time interval between Al and Ca/total time after ΣAl=0.2-0.8. In this method, production cost is reduced, the production process is simple, a normal processing cycle of RH refinement is not affected, the device is convenient in operation and is controllable, and foreign substances are controllable in both shape and quantities. The non-oriented electrical steel sheet prepared according to the present invention has fine magnetic performance, and the method can be used for mass production of the non-oriented electrical steel sheet with fine magnetic performance.
摘要翻译:一种具有细磁性能的无取向电工钢板及其钙处理方法,包括RH(Ruhrstahl-Heraeus)精制步骤。 RH精炼步骤依次包括脱碳步骤,铝脱氧步骤和添加钙合金的步骤。 在添加钙合金的步骤中,添加钙合金的时间满足以下条件:Al与Ca之间的时间间隔/ Al = 0.2-0.8之后的总时间。 在这种方法中,生产成本降低,生产工艺简单,RH精加工的正常加工周期不受影响,设备操作方便,可控,异物在形状和数量上都是可控的。 根据本发明制备的无取向电工钢板具有优良的磁性能,并且该方法可用于批量生产具有优良磁性能的无方向性电工钢板。
摘要:
A non-oriented electrical steel sheet with fine magnetic performance, and a calcium treatment method therefor, including an RH (Ruhrstahl-Heraeus) refinement step. The RH refinement step sequentially comprises a decarbonization step, an aluminum deoxidation step, and a step of adding calcium alloy. In the step of adding calcium alloy, time when the calcium alloy is added satisfies the following condition: time interval between Al and Ca/total time after ΣAl=0.2-0.8. In this method, production cost is reduced, the production process is simple, a normal processing cycle of RH refinement is not affected, the device is convenient in operation and is controllable, and foreign substances are controllable in both shape and quantities. The non-oriented electrical steel sheet prepared according to the present invention has fine magnetic performance, and the method can be used for mass production of the non-oriented electrical steel sheet with fine magnetic performance.
摘要:
Disclosed are a non-oriented electrical steel plate with low iron loss and high magnetic conductivity and a manufacturing process therefor. The casting blank of the steel plate comprises the following components: Si: 0.1-2.0 wt %, Al: 0.1-1.0 wt %, Mn: 0.10-1.0 wt %, C: ≦0.005 wt %, P: ≦0.2 wt %, S: ≦0.005 wt %, N: ≦0.005 wt %, the balance being Fe and unavoidable impurities. The magnetic conductivity of the steel plate meets the following relationship formula: μ10+μ13+μ15≧13982−586.5P15/50; μ10+μ13+μ15≧10000, wherein P15/50 is the iron loss at a magnetic induction intensity of 1.5 T at 50 Hz; μ10, μ13, and μ15 are relative magnetic conductivities at induction intensities of 1.0 T, 1.3 T, and 1.5 T at 50 Hz, respectively. The steel plate can be used for manufacturing highly effective and ultra-highly effective electric motors.
摘要:
An unoriented silicon steel having high magnetic conductivity and low iron loss at a working magnetic density of 1.0-1.5 T and method for manufacturing same. By proper deoxidation control in a RH refining and high-temperature treatment for a short time in a normalizing step, the method can reduce the amount of inclusions in the silicon steel and improve grain shape, so as to improve the magnetic conductivity and iron loss of the unoriented silicon steel at a magnetic density of 1.0-1.5 T.
摘要:
An unoriented silicon steel having high magnetic conductivity and low iron loss at a working magnetic density of 1.0-1.5 T and method for manufacturing same. By proper deoxidation control in a RH refining and high-temperature treatment for a short time in a normalizing step, the method can reduce the amount of inclusions in the silicon steel and improve grain shape, so as to improve the magnetic conductivity and iron loss of the unoriented silicon steel at a magnetic density of 1.0-1.5 T.
摘要:
A method for producing a silicon steel normalizing substrate comprises: steelmaking, hot rolling and normalizing steps. The normalizing step uses a normalizing furnace having a nonoxidizing heating furnace section. The nonoxidizing heating furnace section comprises more than 3 furnace zones. An energy investment ratio of the furnace zones used in the nonoxidizing heating furnace section is adjusted, so as to control an excess coefficient α of the nonoxidizing heating furnace section to be within a range of 0.8≦α
摘要:
A method for producing a silicon steel normalizing substrate comprises: steelmaking, hot rolling and normalizing steps. The normalizing step uses a normalizing furnace having a nonoxidizing heating furnace section. The nonoxidizing heating furnace section comprises more than 3 furnace zones. An energy investment ratio of the furnace zones used in the nonoxidizing heating furnace section is adjusted, so as to control an excess coefficient α of the nonoxidizing heating furnace section to be within a range of 0.8≦α
摘要:
Disclosed are a non-oriented electrical steel plate with low iron loss and high magnetic conductivity and a manufacturing process therefor. The casting blank of the steel plate comprises the following components: Si: 0.1-2.0 wt %, Al: 0.1-1.0 wt %, Mn: 0.10-1.0 wt %, C: ≦0.005 wt %, P: ≦0.2 wt %, S: ≦0.005 wt %, N: ≦0.005 wt %, the balance being Fe and unavoidable impurities. The magnetic conductivity of the steel plate meets the following relationship formula: μ10+μ13+μ15≧13982−586.5P15/50; μ10+μ13+μ15≧10000, wherein P15/50 is the iron loss at a magnetic induction intensity of 1.5 T at 50 Hz; μ10, μ13, and μ15 are relative magnetic conductivities at induction intensities of 1.0 T, 1.3 T, and 1.5 T at 50 Hz, respectively. The steel plate can be used for manufacturing highly effective and ultra-highly effective electric motors.