摘要:
A method for the production of a water-absorbent agent comprises mixing an absorbent resin containing a carboxyl group with an additive soluble in the aqueous solution of at least one member selected from the group consisting of inorganic acids, organic acids, and polyamino acids and a cross-linking agent capable of reacting with the carboxyl group. A water-absorbent agent obtained by adding from 0.005 to 8 parts by weight of an epoxy compound to 100 parts by weight of a water-absorbent resin, exhibiting an absorption capacity without load of at least 45 (g/g), an absorption capacity under load of 20 g/cm2 of not less than 30 (ml/g) and having a residue amount of an epoxy compound of not more than 2 ppm. A water-absorbent composition comprises a polyamino acid (salt) and a water-absorbent resin containing a carboxyl group.
摘要:
The present invention provides: a process for producing a water-absorbing agent at low temperature in a short time, wherein the water-absorbing agent has excellent balance between the absorption capacity without load and the absorption capacity under a load, high fluidity under a hygroscopic atmosphere, and excellent safety; and a novel water-absorbing agent and a novel crosslinking agent particularly suitable for crosslinking water-absorbent resins. The water-absorbing agent, having excellent balance between the absorption capacity without load and the absorption capacity under a load, high fluidity under a hygroscopic atmosphere, and excellent safety, can be obtained by using an oxetane compound and/or an imidazolidinone compound for a water-absorbent resin.
摘要:
The present invention provides: a process for producing a water-absorbing agent at low temperature in a short time, wherein the water-absorbing agent has excellent balance between the absorption capacity without load and the absorption capacity under a load, high fluidity under a hygroscopic atmosphere, and excellent safety; and a novel water-absorbing agent and a novel crosslinking agent particularly suitable for crosslinking water-absorbent resins. The water-absorbing agent, having excellent balance between the absorption capacity without load and the absorption capacity under a load, high fluidity under a hygroscopic atmosphere, and excellent safety, can be obtained by using an oxetane compound and/or an imidazolidinone compound for a water-absorbent resin.
摘要:
The present invention provides a water-swellable crosslinked polymer composition which comprises an anionic crosslinked polymer and a cationic crosslinked polymer, and is excellent in the desalting property and further in the absorption properties under load, and is therefore highly practicable. In a water-swellable crosslinked polymer composition which is particulate and comprises a cationic crosslinked polymer and an anionic crosslinked polymer, the improvement satisfies the following requirements (1) and/or (2): (1) At least either one of the cationic crosslinked polymer and the anionic crosslinked polymer has a bulk density of not more than 0.5 g/ml. (2) The water-swellable crosslinked polymer composition has a bulk density of not more than 0.5 g/ml.
摘要:
A base film for a thermal transfer ribbon which is a biaxially oriented polyester film comprising polyethylene-2,6-naphthalene dicarboxylate as a main constitutional element, wherein in a temperature-dimensional change curve under load in a longitudinal direction of the film, the dimensional change from the original length of the film at temperatures of up to 200° C. is 1.0% or less and the dimensional change from the original length of the film at temperatures of up to 230° C. is 3.0% or less. This film may have a coating layer of at least one water-soluble or water-dispersible resin selected from the group consisting of an urethane resin, polyester resin, acrylic resin and vinyl resin-modified polyester resin, on one side thereof. The base film gives a thermal transfer ribbon which has excellent adhesion to a sublimation-type ink layer and excellent printing performance without blurred ink at the time of high-speed printing and without wrinkles formed by friction with a head.
摘要:
The present invention provides a thermal transfer sheet having a color dye layer which has a reduced dye content and a good recording sensitivity and can provide an image having a good black color density. The thermal transfer sheet including a substrate sheet and, provided on the substrate sheet, a black dye layer including particular yellow, magenta, and cyan dyes.
摘要:
A method of preparation of an absorbent composite in which an aqueous solution containing a water-soluble radical polymerization initiator and a water-soluble ethylenically unsaturated monomer which can be converted into an absorbent polymer by polymerization is applied to a substrate, and the monomer is polymerized while the substrate to which the aqueous solution is applied is, on both the sides, held in contact with polymerization-inert surfaces facing each other. A continuous manufacturing method includes the sequential steps of continuously passing a substrate through (1) a region applying to the substrate an aqueous solution containing a water-soluble radical polymerization initiator and a water-soluble ethylenically unsaturated monomer which can be converted into an absorbent polymer by polymerization, and (2) a region of polymerizing the monomer while maintaining the substrate, on both the sides, in contact with polymerization-inert surfaces facing each other.
摘要:
A memory system including a bus 10, 11, a memory 17, a memory controller 16, a first device 13 having a cache, and a second device 15, all connected to the bus, wherein the memory controller includes a buffer 20 for temporarily storing cache data and write data that the second device writes in the memory. The buffer of the memory controller temporarily stores cached data and the write data to be written on write access to the memory by the second device, which enables maintenance of data coherency while avoiding a write access retry by the second device.
摘要:
The present invention provides: a production process for a basic water-absorbent resin to be a main component of a water-absorbing agent which exhibits an excellent water absorption capacity under a load with high productivity; a production process for a water-absorbing agent; and use thereof. The production process for an irregular shape basic water-absorbent resin comprises the step of reacting a basic resin and a crosslinking agent in order to obtain the basic water-absorbent resin, with the process forwarding a crosslinking reaction and pulverizing the resultant product at the same time. The first production process for a water-absorbing agent comprises the step of blending an acidic water-absorbent resin with the basic water-absorbent resin obtained by the above-mentioned process. The second production process for a water-absorbing agent comprises the step of obtaining a mixture of an acidic water-absorbent resin and the basic water-absorbent resin by coexisting with the acidic water-absorbent resin when carrying out the crosslinking reaction and the pulverization in the above-mentioned process.
摘要:
The present invention provides a process in which no surfactant is used, or even if the surfactant is used the amount thereof is as small as possible, thus stably obtaining a suspension to carry out a crosslinking reaction. A production process for a crosslinked polymer particle, comprising the steps of: forming a suspension in which liquid drops of a first phase are dispersed in a second phase by stirring both phases in the presence of an inorganic particle, wherein the first phase includes a high-molecular compound and a crosslinking agent, and wherein the first phase and the second phase are insoluble in each other, and wherein the affinity of the inorganic particle for water is different from that of the high-molecular compound; and carrying out a crosslinking reaction. Furthermore, an approximately spherical crosslinked polymer particle, which is free from a surfactant.