摘要:
An anionically polymerized impact-modified polystyrene has a yield stress of at least 24 MPa, measured at 23° C. to DIN 53455 and a hole impact strength of at least 11 kJ/m2, measured at 23° C. to DIN 53753, measured in each case on a specimen produced to ISO 3167. A preparation process is described.
摘要翻译:阴离子聚合的冲击改性聚苯乙烯具有至少24MPa的屈服应力,在23℃下根据DIN 53455测量,并且在23℃根据DIN 53753测量的孔冲击强度为至少11kJ / m 2,测量 在每种情况下都是根据ISO 3167生产的样品。描述了制备过程。
摘要:
In a process for the homopolymerization of vinylaromatic monomers or the copolymerization of vinylaromatic monomers and dienes in the presence of at least one alkali metal compound and at least one compound of an element of group 3a of the Periodic Table of the elements, the compounds contain, based on the sum of molar equivalents of alkali metal and elements of group 3a, in each case a) from 0.1 to 3.9 molar equivalents of oxygen, sulfur, nitrogen or phosphorus and b) from 0.1 to 3.9 molar equivalents of an organyl ligand.
摘要:
In a process for the homopolymerization of vinylaromatic monomers or the copolymerization of vinylaromatic monomers and dienes, the monomers are polymerized in the presence of at least one alkali metal organyl, at least one magnesium organyl and at least one aluminum organyl. The invention also provides an initiator composition for carrying out the process.
摘要:
Disclosed are a process for the preparation of an initiator composition comprising an alkali metal organyl and an aluminum organyl and a process for the polymerization of anionically polymerizable monomers.
摘要:
A process for the continuous anionic polymerization or copolymerization of styrene or diene monomers using an alkali metal alkyl compound as polymerization initiator is carried out in the presence of an alkyl- or arylmetal compound of an element which occurs in at least divalent form as rate regulator, preferably under non-isothermal conditions and without back-mixing in a tubular or tube-bundle reactor, preferably using an alkyl- or arylmetal compound A of the formula R1M1 and an alkyl- or arylmetal compound B of the formula R2nM2 in a molar ratio between B and A of from 0.1:1 to 500:1, where M1 is Li, Na or K; R1 is hydrogen, C1-C20-alkyl, C6-C20-aryl, or C7-C20-alkyl-substituted aryl; M2 is an n-valent element from group 2a, 2b or 3a of the Periodic Table; and R2 is hydrogen, halogen, C1-C20-alkyl or C6-C20-aryl; and a special anionic polymerization initiator containing no Lewis base.
摘要:
In a process for the preparation of block copolymers from vinylaromatic monomers and dienes, the monomers are polymerized in the presence of at least one alkali metal organyl or alkali metal alkoxide and at least one magnesium, aluminum or zinc organyl.
摘要:
In a process for polymerizing dienes in a solvent comprising vinylaromatic monomers, the polymerization is carried out in the presence of a metal compound of Ti, Zr, Hf, V, Nb, Ta, Cr, Mo or W as catalyst and a Lewis acid as cocatalyst and, if desired, an alkylating agent and, if desired, a regulator. This process can be used for preparing high-impact polystyrene, acrylonitrile-butadiene-styrene copolymers or methyl methacrylate-butadiene-styrene copolymers.
摘要:
The anionic polymerization of dienes or copolymers of dienes and vinylaromatic monomers in a vinylaromatic monomer or monomer mixture to give homopolydienes or copolymers or mixed homopolydienes and copolymers is carried out in the presence of a metal alkyl or aryl of an element having a valence of at least two without addition of Lewis bases.
摘要:
A process prepares impact-modified thermoplastic molding compositions which comprise a soft phase made from a rubber dispersed in a hard matrix composed of vinylaromatic monomers, where the hard matrix is prepared by anionic polymerization in the presence of a metal alkyl compound or a metal aryl compound of an element of the second or third main group, or of the second subgroup, of the Periodic Table.
摘要:
In a process for the anionic polymerization of vinylaromatic monomers or dienes in the presence of a lithium organyl or lithium alcoholate and a magnesium and/or an aluminum compound, a sterically hindered phenol or amine is added.