摘要:
The present invention is directed to an electrodepositable coating composition comprising a bismuth salt and a stabilizing agent, and wherein the molar ratio of elemental bismuth to the stabilizing agent is not less than 1:0.25.
摘要:
An automotive substrate comprising an electrodepositable coating layer deposited over at least a portion of the automotive substrate and a barrier coating layer deposited over at least a portion of the electrodepositable coating layer.
摘要:
Provided are curable coating compositions comprised of any of a variety of film-forming polymers containing reactive functional groups, a curing agent containing functional groups which are reactive with the functional groups of the polymer, and an exfoliated silicate material derived from a layered silicate which has been exfoliated with a polymer which is compatible with both the film-forming polymer and the curing agent. The inclusion of the exfoliated silicate material enhances coating properties such as adhesion, appearance, crater resistance, and rheology control.
摘要:
An aqueous, cationically electrodepositable coating composition contains a ternary sulfonium or quaternary phosphonium group containing resin, an aminoplast or phenoplast crosslinking agent and a catalytic amount of a non-ionic ester of a sulfonic acid as latent acid catalyst to catalyze the reaction between the sulfonium or phosphonium group containing resin and the aminoplast crosslinking agent.
摘要:
Disclosed are methods for treating metal substrates, including ferrous substrates, such as cold rolled steel and electrogalvanized steel. The methods include depositing an electropositive metal onto at least a portion of the substrate, and then contacting the substrate with a pretreatment composition that is substantially free of crystalline phosphates and chromates. The present invention also relates to coated substrates produced thereby.
摘要:
Disclosed are methods for passivating metal substrates, including ferrous substrates, such as cold rolled steel and electrogalvanized steel. The methods comprise the steps of depositing an electropositive metal onto at least a portion of the substrate, followed immediately by electrophoretically depositing on the substrate a curable, electrodepositable coating composition. The present invention also relates to coated substrates produced by the above methods.
摘要:
The present invention is directed to a method for coating a substrate comprising: (a) applying a caustic cleaner onto at least a portion of the substrate; (b) rinsing at least a portion of the substrate that was subjected to step (a) with water; (c) applying an acid cleaner onto at least a portion of the caustically cleaned substrate; (d) rinsing at least a portion of the substrate that was subjected to step (c) with water; and (e) applying a conversion coating comprising zirconium onto at least a portion of the acid cleaned substrate; and wherein at least one of the materials used in steps (c) and (e) is substantially chrome free. The present invention is also directed to a substrate, such as an aluminum substrate, that has been coated using the aforementioned method.
摘要:
Disclosed are methods for passivating metal substrates, including ferrous substrates, such as cold rolled steel and electrogalvanized steel. The methods comprise the steps of depositing an electropositive metal onto at least a portion of the substrate, followed immediately by electrophoretically depositing on the substrate a curable, electrodepositable coating composition. The present invention also relates to coated substrates produced by the above methods.
摘要:
An electrodepositable composition is provided comprising: a non-gelled, cationic, water-dispersible resin, electrodepositable on a cathode, which is derived from a polyepoxide and which contains in the resin molecule cationic salt groups, beta-hydroxy ester groups, active hydrogen groups including free phenolic hydroxyl groups, and capped isocyanate groups. The composition provides excellent corrosion resistance when electrodeposited over steel substrates, and does not require lead in the formulation nor the use of a conventional chrome rinse for the steel substrate during pretreatment before electrodeposition.
摘要:
An electrodepositable coating composition comprising (i) a film-forming polymer, (ii) a corrosion inhibitor, and (iii) a silane that does not contain an ethylenically unsaturated double bond.