摘要:
An aluminum alloy brazing sheet having a core material of an aluminum alloy, and a filler material cladded on the core is disclosed. The core material is an aluminum alloy having about 0.05 to about 1.2 mass Si, about 0.05-about 1.0 mass % Fe, about 0.05-about 1.2 mass % Cu, and about 0.6-about 1.8 mass % Mn, balance Al and the inevitable impurities. The, filler material includes an aluminum alloy having about 2.5-about 13.0 mass % Si. Also, there is provided a method of manufacturing such an aluminum alloy brazing sheet.
摘要:
An aluminum alloy sheet material, containing 2.6% by mass or more and less than 3.5% by mass (% by mass is simply denoted by % hereinafter) of Si, 0.05 to 0.5% of Mg, 0.5% or more and less than 1.2% of Cu, 0.6 to 1.5% of Mn, 0.5 to 1.6% of Zn, and 0.3 to 2.0% of Fe, and containing, if necessary, at least one of 0.01 to 0.2% of Cr, 0.01 to 0.2% of Zr, 0.01 to 0.2% of V, and 0.01 to 0.2% of Ti, with the balance of Al and unavoidable impurities. A method of producing the aluminum alloy sheet material, which method contains carrying out specific workings.
摘要:
There is disclosed an aluminum alloy extruded material for structural members of automotive bodies, which is composed of an aluminum alloy containing more than 2.6 wt % but 4.0 wt % or less of Si and more than 0.3 wt % but 1.5 wt % or less of Mg, further, (i) containing Mn, Zn, Cu, and Fe each in a given amount, or (ii) containing Zn, Cu, and Fe each in a given amount and containing at least one selected from among Mn, Cr, Zr, and V in a given amount, and the balance being made of Al and unavoidable impurities, which material has a given conductivity and a given melting start temperature. There is also disclosed a method for producing the extruded material, in which after an aluminum alloy ingot of the above composition is subjected to a homogenizing treatment at given conditions, it is cooled, heated again, and subjected to hot extrusion at given conditions. The extruded material is excellent in spot weldability and surface treatment property, such as the chemical conversion property and degreasing property, and it has high mechanical strength and ductility, and is excellent in impact absorbability and/or bendability.
摘要:
A method for manufacturing an aluminum alloy sheet suitable for high-speed forming includes subjecting the alloy to a homogenization treatment, hot rolling and cold rolling the homogenization treated alloy, thereby obtaining a cold-rolled sheet, and annealing the cold-rolled sheet. The aluminum alloy contains 4.0 to 10.0 wt. % of Mg, 0.2 wt. % of inevitable impurities of Fe and Si, 0.05 wt. % of other impurity elements, and the balance of Al. Another embodiment includes deep drawing the aluminum alloy sheet.
摘要:
An aluminum alloy extruded material for automotive structural members, which contains 2.6 to 5 wt % of Si, 0.15 to 0.3 wt % of Mg, 0.3 to 2 wt % of Cu, 0.05 to 1 wt % of Mn, 0.2 to 1.5 wt % of Fe, 0.2 to 2.5 wt % of Zn, 0.005 to 0.1 wt % of Cr, and 0.005 to 0.05 wt % of Ti, and satisfies relationship of the following expression (I), (Content of Mn (wt %))+0.32×(content of Fe (wt %))+0.097×(content of Si (wt %))+3.5×(content of Cr (wt %))+2.9×(content of Ti (wt %))≦1.36 (I) with the balance being made of aluminum and unavoidable impurities. A method of producing the aluminum alloy extruded material for automotive structural members, which comprises cooling with a refrigerant from outside of a die-exit side, at the time of extrusion.
摘要:
The present invention relates to an aluminum alloy for a magnetic disk substrate having a composition consisting of, by percent by weight, 2.0 to 6.0% of Mg, 0.05 to 0.15% of Cu, 0.10 to 0.30% of Zn and 0.05 to 0.12% of Zr, wherein the contents of Cu, Zn and Zr satisfy the relationship: 0.15%.ltoreq.2Cu+6Zr-3Zn.ltoreq.0.32% (wherein Cu, Zr, and Zn respectively represent their contents in terms of percent by weight), and the composition further consists of one or both of 0.01 or more to less than 0.05% of Cr and 0.01 or more to less than 0.05% of Mn, impurities consisting of Si, Fe and Ti, which are respectively regulated to be 0.05% or less, 0.05% or less, and 0.02% or less, and other inevitable impurity elements respectively regulated to be 0.02% or less, with the remainder being Al. The present invention also relates to a clad material for a magnetic disk substrate, in which one or both surfaces of a core material, consisting of at least less than 3.0% of Zn with the remainder being Al and inevitable impurity elements, are clad with a surface material consisting of the aluminum alloy having the above composition. The above aluminum alloy composition makes it possible to manufacture a large storage memory capacity magnetic disk in which there is much less formation of micropits or nodules.
摘要:
A high Mg content Al-Mg alloy sheet for press-forming, having superior strength and deep drawing formability. The alloy has intermetallic compounds containing Cr dispersed into the metal structure thereof. The mean grain diameter of the metal structure ranges from about 5 to 30 .mu.m. The process for manufacturing the alloy is also disclosed. The composition of the alloy includes Al, Mg, Be, Cr, Ti, B, Cu Fe, Si and associated inevitable impurities.
摘要:
Aluminum thin plates which are used as fins of a heat exchanger can be manufactured, as described in the claims, by controlling the composition of an aluminum alloy, which is used as a core material, and controlling the cold rolling reduction ratio of a clad material composed of the core material and a skin material, after hot rolling. The thus manufactured aluminum thin plates for brazing are excellent in high-temperature sagging resistance and sacrificial anodic effect, whereby it is possible to make the fins thinner.
摘要:
An aluminum alloy brazing sheet having a core material of an aluminum alloy, and a filler material cladded on the core is disclosed. The core material is an aluminum alloy having about 0.05 to about 1.2 mass Si, about 0.05-about 1.0 mass % Fe, about 0.05-about 1.2 mass % Cu, and about 0.6-about 1.8 mass % Mn, balance Al and the inevitable impurities. The filler material includes an aluminum alloy having about 2.5-about 13.0 mass % Si. Also, there is provided a method of manufacturing such an aluminum alloy brazing sheet.
摘要:
An aluminum sheet material for automobiles is herein disclosed, having an aluminum alloy composition: (i) comprising 3.5 to 5 wt % of Si, 0.3 to 1.5 wt % of Mg, 0.4 to 1.5 wt % of Zn, 0.4 to 1.5 wt % of Cu, 0.4 to 1.5 wt % of Fe, and 0.6 to 1 wt % of Mn, and one or more members selected from the group of 0.01 to 0.2 wt % of Cr, 0.01 to 0.2 wt % of Ti, 0.01 to 0.2 wt % of Zr, and 0.01 to 0.2 wt % of V, with the balance of aluminum and unavoidable impurities, or (ii) comprising between more than 2.6 wt % and 5 wt % of Si, 0.2 to 1.0 wt % of Mg, 0.2 to 1.5 wt % of Zn, 0.2 to 1.5 wt % of Cu, 0.2 to 1.5 wt % of Fe, and between 0.05 and less than 0.6 wt % of Mn, and one or more members selected from the group of 0.01 to 0.2 wt % of Cr, 0.01 to 0.2 wt % of Ti, 0.01 to 0.2 wt % of Zr, and 0.01 to 0.2 wt % of V, with the balance of aluminum and unavoidable impurities. It is possible to produce an aluminum sheet material for automobiles that has excellent mechanical strength and bending property as well as enhanced weldability, by making the recycling use of recycled aluminum materials.