摘要:
Polypropylene based resins and compositions comprising the resin having extremely high stiffness, heat resistance and impact strength, with these properties being well-balanced, are provided. The polypropylene based resins are characterized by comprising:(1) a propylene polymer having a content of alpha-olefin other than propylene of not more than 4 mole percent, and the following properties (2), (3) and (4):(2) a pentad fraction (mmmm fraction) measured by .sup.13 C-NMR of not less than 96.0 percent,(3) a main elution fraction peak position of not less than 118.0.degree. C. and a peak half value width of less than 4.0, these values being measured by the temperature raising separation method, and(4) an intrinsic viscosity of not less than 0.5 dl/g, but not more than 5.0 dl/g; and,(5) a rubber content measured by pulse NMR of more than 25 percent.
摘要:
A polyolefinic resin which is a homopolymer of an olefin or a copolymer of olefins, has (i) intrinsic viscosity �.eta.! measured in decaline at the temperature of 135.degree. C. in the range of 0.5 to 10 deciliter/g and (ii) content of insoluble fraction in boiling n-heptane (W) in the range of 10 to 99 weight % and shows (iii) relation between relaxation time of rubber component measured by pulse NMR at the temperature of 30.degree. C. �T.sub.2H.sup.R (30):.mu.s!, relaxation time of rubber component measured by pulse NMR at the temperature of 80.degree. C. �T.sub.2H.sup.R (80):.mu.s! and the content of insoluble fraction in boiling n-heptane (W) satisfying the following equations: T.sub.2H.sup.R (80).ltoreq.670-2.2.times.W T.sub.2H.sup.R (80)/T.sub.2H.sup.R (30).ltoreq.8.8+0.086.times.W and a propylenic resin composition comprising (A) 10 to 95 weight % of the polyolefinic resin, particularly a propylenic resin which is at least one kind selected from a homopolymer of propylene and copolymers of propylene containing 4 mol % or less of other olefinic units, and (B) 90 to 5 weight % of a propylenic random copolymer having intrinsic viscosity �.eta.! measured in decaline at the temperature of 135.degree. C. in the range of 0.5 to 10 deciliter/g and containing 10 to 80 mol % of olefinic units other than the propylenic unit are disclosed. The polyolefinic resin and the composition have high heat resistance and excellent mechanical properties in a wide range of modulus, show small temperature dependence of the mechanical properties and do not cause stickiness on the surface of molded articles.
摘要:
A propylenic resin which is a homopolymer of propylene or a copolymer of propylene, has (i) intrinsic viscosity [.eta.] measured in decaline at the temperature of 135.degree. C. in the range of 0.5 to 10 deciliter/g and (ii) content of insoluble fraction in boiling n-heptane (W) in the range of 10 to 99 weight % and shows (iii) relation between relaxation time of rubber component measured by pulse NMR at the temperature of 30.degree. C. [T.sub.2H.sup.R (30): .mu.s], relaxation time of rubber component measured by pulse NMR at the temperature of 80.degree. C. [T.sub.2H.sup.R (80): .mu.s] and the content of insoluble fraction in boiling n-heptane (W) satisfying the following equations:T.sub.2H.sup.R (80).ltoreq.670-2.2.times.WT.sub.2H.sup.R (80)/T.sub.2H.sup.R (30).ltoreq.8.8+0.086.times.Wand a propylenic resin composition comprising (A) 10 to 95 weight % of the propylenic resin, particularly a propylenic resin which is at least one kind selected from a homopolymer of propylene and copolymers of propylene containing 4 mol % or less of other olefinic units, and (B) 90 to 5 weight % of a propylenic random copolymer having intrinsic viscosity [.eta.] measured in decaline at the temperature of 135.degree. C. in the range of 0.5 to 10 deciliter/g and containing 10 to 80 mol % of olefinic units other than the propylenic unit are disclosed. The polyolefinic resin and the composition have high heat resistance and excellent mechanical properties in a wide range of modulus, show small temperature dependence of the mechanical properties and do not cause stickiness on the surface of molded articles.
摘要:
A solid electrolyte including a lithium (Li) element, a phosphorus (P) element and a sulfur (S) element, the 31P MAS NMR spectrum thereof having a peak ascribed to a crystal at 90.9±0.4 ppm and 86.5±0.4 ppm; and the ratio (xc) of the crystal in the solid electrolyte being from 60 mol % to 100 mol %.
摘要翻译:包含锂(Li)元素,磷(P)元素和硫(S))元素的固体电解质,具有归属于90.9±0.4ppm和86.5±0.4ppm的晶体的峰的31P MAS NMR光谱; 固体电解质中的结晶比例(xc)为60〜100摩尔%。
摘要:
A system includes a multivariable mass flow rate transmitter having a mass flow rate computation section, and a flow rate setting tool which performs setup of the mass flow rate computation section, the flow rate setting tool including a parameter generation section, a condition input section, a model computation section, a first mass flow rate display section which displays an output value of the model computation section, a second mass flow rate display section which displays the computation result, and a diagnosing display screen which displays the first and second mass flow rate display sections on the same screen.
摘要:
A solid electrolyte including a lithium (Li) element, a phosphorus (P) element and a sulfur (S) element, the 31P MAS NMR spectrum thereof having a peak ascribed to a crystal at 90.9±0.4 ppm and 86.5±0.4 ppm; and the ratio (xc) of the crystal in the solid electrolyte being from 60 mol % to 100 mol %.
摘要翻译:包含锂(Li)元素,磷(P)元素和硫(S))元素的固体电解质,具有归属于90.9±0.4ppm和86.5±0.4ppm的晶体的峰的31P MAS NMR光谱; 固体电解质中的结晶比例(xc)为60〜100摩尔%。
摘要:
Glass includes an aggregate of solid electrolyte particles including Li, P, and S, wherein when a Raman spectrum of the glass is repeatedly measured and a peak at 330 to 450 cm−1 in each Raman spectrum is separated to waveforms of individual components, a standard deviation of a waveform area ratio of each component is less than 4.0.
摘要:
A retainer for use in measuring a force generated between a photocurable resin and a pressing member by a detector includes: a pressing member that has light transmission characteristics and is pressed to the photocurable resin; and a light irradiation block that is provided between the detector and the pressing member and irradiates light emitted from an external light source onto the pressing member in a state of being not contacting a light source and an optical transmission line including an optical fiber.
摘要:
A multivariable transmitter has a microprocessor for executing a computation processing task with using a plurality of physical quantity signals. The microprocessor executes a processing for obtaining data from a sensor every computation processing task and executes the computation processing task in a time-division manner.
摘要:
Provided are a propylene-ethylene block copolymer having MFR of from 0.01 to 1.0 g/10 min and comprised of (A) from 85 to 97% by weight a 25° C. xylene-insoluble fraction and (B) from 3 to 15% by weight of a 25° C. xylene-soluble fraction, wherein the fraction (A) is such that its stereospecificity index measured through 13C-NMR is at least 98.0%, its intrinsic viscosity [&eegr;] falls between 2.5 and 5.5 dl/g, and its weight-average molecular weight, Mw, measured through GPC and the content, S, of the fraction having a molecular weight of at most 104.5 therein satisfy S (wt. %)≦−5.3×10−6 Mw+7.58, and the fraction (B) is such that its ethylene unit content measured through 13C-NMR falls between 30 and 70% by weight, and its intrinsic viscosity [&eegr;] falls between 2.5 and 9.0 dl/g; and its blow-molded articles. The copolymer has good heat resistance, high rigidity, good impact resistance and good drawdown resistance, and its blow-molded articles have well-balanced rigidity and low-temperature barrier resistance.