摘要:
The present invention relates to a container packing structure, characterized in that it comprises a crystalline phase containing 55 to 97% by weight of xonotlite crystallites and 3 to 45% by weight of tobermorite crystallites. It also relates to a method for fabricating such a packing structure, and the container containing same, and its use for storing fluids such as gases.
摘要:
The present invention relates to a container packing structure, characterized in that it comprises a crystalline phase containing 55 to 97% by weight of xonotlite crystallites and 3 to 45% by weight of tobermorite crystallites. It also relates to a method for fabricating such a packing structure, and the container containing same, and its use for storing fluids such as gases.
摘要:
The present invention relates to a container packing structure, characterized in that it comprises a crystalline phase containing 55 to 97% by weight of xonotlite crystallites and 3 to 45% by weight of tobermorite crystallites. It also relates to a method for fabricating such a packing structure, and the container containing same, and its use for storing fluids such as gases.
摘要:
The present invention relates to a packing structure for containers, characterized in that it comprises a material of xonotlite and/or tobermorite and/or foshagite crystal structure crystallized in the form of needles, at least 50% by volume of which have a length ranging from 2 to 10 μm and a thickness ranging from 0.2 to 1 μm. Process for manufacturing such a packing structure and gas container containing it.
摘要:
The present invention relates to a container packing structure, characterized in that it comprises a crystalline phase containing 55 to 97% by weight of xonotlite crystallites and 3 to 45% by weight of tobermorite crystallites. It also relates to a method for fabricating such a packing structure, and the container containing same, and its use for storing fluids such as gases.
摘要:
Container having a lining structure, comprising a crystalline phase containing 55 to 97 wt % of xonotlite crystallites and 3 to 45 wt % of tobermorite crystallites and comprising less than 15 wt % of intermediates of formula CaxSiyOz.wH2O where 1
摘要:
The invention relates to a method for producing a packing structure, characterized in that it includes the following steps: a) a step in which the temperature of an initial mixture of quicklime and silica is raised to a temperature T1 of between 150 and 300° C. over a period of less than 10 hours; b) a step in which hydrothermal synthesis is performed using the mixture of quicklime and silica produced in step (a) at a temperature T1 of between 150 and 300° C. and at a pressure P1 of between 5×105 Pa and 25×105 Pa over a period t1 of between 10 and 70 hours; c) a step in which the mixture produced in step (b) is cooled from temperature T1 to ambient temperature over a period of between 1 and 48 hours at a cooling rate ΔTR1 of between 3 and 200° C./hour; and d) a step in which the mixture produced in step (c) is dried.
摘要:
The invention relates to a method for producing a packing structure, characterized in that it includes the following main steps: a) a step comprising the hydrothermal synthesis of the packing mass, performed using a mixture of quicklime and silica; and b) a step comprising the drying of the packing mass produced in step (a) at a temperature T2 of between 110° C. and 500° C., possibly with at least one intermediate stage performed at a temperature of between 111° C. and 350° C. over a period t2 selected such that the physisorbed water content of the packing mass is less than 0.5%.
摘要:
The invention relates to a method for producing a packing structure, characterized in that it includes the following main steps: a) a step comprising the hydrothermal synthesis of the packing mass, performed using a mixture of quicklime and silica; and b) a step comprising the drying of the packing mass produced in step (a) at a temperature T2 of between 110° C. and 500° C., possibly with at least one intermediate stage performed at a temperature of between 111° C. and 350° C. over a period t2 selected such that the physisorbed water content of the packing mass is less than 0.5%.
摘要:
A coated electrode for welding stainless steels. The electrode when used for welding, produces a low level of fumes, which in turn contains a low level of hexavalent chromium. The electrode has a central metallic core which is made of steel or stainless steel and which is covered with a covering that contains a lithium based compound. The covering does not contain any sodium or potassium based compounds like aluminosilicates. The covering also contains a lithium containing binder and metallic elements in the form of ferro-alloys or individual metallic elements.