摘要:
A silicon-containing steel sheet having a low iron loss has such a crystal structure that crystal grains having an inclination angle of {110} face of not more than 10.degree. with respect to the sheet surface are included in an amount of not less than 80 vol % and exhibit a graining surface pattern in which boundaries of these crystal grains form stepwise difference or groove of not less than 0.4 .mu.m as a maximum height. This sheet is produced by subjecting a grain oriented silicon steel sheet after final annealing to a magnetically smoothening treatment by electrolysis in an squeous solution containing at least one of water soluble halides.
摘要:
A grain oriented electromagnetic steel sheet having a very low iron loss is obtained by subjecting a surface of base metal in the sheet after finish annealing to a particular mechanical polishing and has a surface roughness having a center-line average roughness of not more than 0.3 .mu.m after the polishing and the number of abrasive grains embedded in a layer just beneath polished surface of not more than 20,000 grains/cm.sup.2.
摘要:
A grain oriented silicon steel sheet having a low iron loss and not causing degradation of properties even through strain relief annealing is produced by applying ultrasonic vibrations to the surface of the sheet after secondary recrystallization annealing.
摘要:
A steel sheet for cans that has a yield stress of at least 500 Mpa after coating and baking and a method for manufacturing the steel sheet for cans are provided. The steel sheet for cans contains, on the basis of mass percent, C: more than 0.02% but 0.10% or less, Si: 0.10% or less, Mn: 1.5% or less, P: 0.20% or less, S: 0.20% or less, Al: 0.10% or less, N: 0.0120% to 0.0250%, dissolved N being 0.0100% or more, and a remainder of Fe and incidental impurities. A high-strength material can be obtained by maintaining the absolute quantity of dissolved N at a certain value or more and performing hardening by quench aging and strain aging, for example, in a printing process, a film lamination process, or a drying and baking process performed before can manufacturing. In the manufacture, hot rolling is performed at a slab extraction temperature of 1200° C. or more and a finish rolling temperature of (Ar3 transformation temperature—30)° C. or more, and coiling is performed at 650° C. or less.
摘要:
A steel sheet for containers that has a hardness of 500 MPa or more and superior workability and a method for producing the steel sheet are provided. A steel containing, in percent by mass, 0.01% to 0.05% carbon, 0.04% or less silicon, 0.1% to 1.2% manganese, 0.10% or less sulfur, 0.001% to 0.100% aluminum, 0.10% or less nitrogen, and 0.0020% to 0.100% phosphorus, the balance being iron and incidental impurities, is subjected to hot rolling at a finishing temperature of (Ar3 transformation temperatute−30)° C. or more and a coiling temperature of 400° C. to 750° C., is subjected to pickling and cold rolling, is subjected to continuous annealing including overaging treatment, and is subjected to second cold rolling at a reduction rate of 20% to 50%, thus providing a high-strength steel sheet for containers that has a tensile strength of 500 MPa or more and a proof stress difference between width and rolling directions of 20 MPa or less.
摘要:
An organic composite coated steel sheet having excellent chromate dissolution resistance, wet adhesion, and corrosion resistance before and after working. The steel sheet comprises a chromate-silica film on at least one face of a zinc or zinc base alloy plated steel sheet, the silica-added chromate film having about 5 to 500 mg/m.sup.2 in terms of metal Cr content and being formed from a chromate solution containing about 25 to 70 wt % of Cr.sup.+6 based upon total Cr content. A resin coating film is adhered to the chromate-silica film and is formed from an aqueous paint. The aqueous paint includes an aqueous anionic resin and/or an aqueous nonionic resin, a reducing agent, and a water-dispersed silica. The resin coating film is deposited in a dry weight amount of about 0.1 to 3 g/m.sup.2.
摘要翻译:一种在工作前后具有优异的耐铬酸盐溶解性,湿粘合性和耐腐蚀性的有机复合涂层钢板。 所述钢板在锌或锌基合金镀覆钢板的至少一面上含有铬酸二氧化硅膜,所述二氧化硅添加的铬酸盐膜的金属Cr含量为约5〜500mg / m 2,由 铬酸盐溶液含有约25至70重量%的Cr + 6,基于总Cr含量。 将树脂涂膜粘附到铬酸盐 - 二氧化硅膜上,并由水性涂料形成。 水性涂料包括含水阴离子树脂和/或非水性非离子树脂,还原剂和水分散的二氧化硅。 树脂涂膜以约0.1〜3g / m 2的干重量进行沉积。
摘要:
The improved organic composite coated steel plate includes a zinc or zinc alloy plated steel plate as a substrate that has on its surface a chromate film the Cr.sup.6+ content of which is no more than 70% of the total Cr content and which is deposited in an amount of 5-500 mg/m.sup.2 in terms of metallic chromium, the chromate film being overlaid with a resin layer that is deposited in an amount of 0.1-3 g/m.sup.2 on a dry weight basis and which is formed primarily of water-dispersed silica and one organic resin member as selected from the group consisting of an anionic aqueous resin, a nonionic aqueous resin and an anionic aqueous urethane resin. This steel plate is adapted for not contaminating the environment of the earth in the process of its manufacture.
摘要翻译:改进的有机复合涂层钢板包括锌或锌合金镀覆钢板作为基材,其表面上具有Cr6 +含量不超过总Cr含量的70%并以一定量沉积的铬酸盐膜 以金属铬计为5-500mg / m 2,铬酸盐膜覆盖有以干重计为0.1-3g / m 2的量沉积的树脂层,主要由水分散二氧化硅 和一种选自阴离子水性树脂,非离子水性树脂和阴离子水性聚氨酯树脂的有机树脂构件。 该钢板适用于在制造过程中不污染地球的环境。
摘要:
An organic composite coated steel strip having well-balanced corrosion resistance, coating properties including adaptability to electrophoretic coating and water resistant secondary coating adherence, and spot weldability is provided. The organic composite coated strip comprises a zinc or zinc base alloy plated steel substrate; a chromate later on the substrate containing up to 70% by weight of Cr.sup.6+ based on the total chromium quantity, the chromate layer being coated in a weight of 5 to 500 mg/m.sup.2 in terms of elemental chromium; and an organic composite layer on the chromate layer mainly comprising silica and an organic high molecular weight resin. In the organic composite coated steel strip, (a) silica has an average primary particle diameter of 5 to 30 nm; (b) silica is agglomerated into agglomerates of an average thickness of 0.2 to 2 .mu.m and an average apparent diameter of 5 to 300 .mu.m; and (c) the organic composite layer has been coated to a dry weight of 0.1 to 3 g/m.sup.2. The organic composite coated steel strip of the invention has various uses including automobile bodies.
摘要翻译:提供了具有良好平衡的耐腐蚀性,包括对电泳涂层的适应性和耐水二次涂层粘附性的涂层性能和点焊性的有机复合涂层钢带。 有机复合涂层带材包括锌或锌基合金镀钢基材; 铬酸盐层以基于铬的总铬含量高达70重量%的Cr 6+,铬酸盐层以元素铬计为5至500mg / m 2的重量; 以及主要包含二氧化硅和有机高分子量树脂的铬酸盐层上的有机复合层。 在有机复合涂层钢带中,(a)二氧化硅的平均一次粒径为5〜30nm; (b)将二氧化硅凝聚成平均厚度为0.2〜2μm,平均视野直径为5〜300μm的团块; 和(c)有机复合层已被涂覆至干燥重量为0.1至3g / m 2。 本发明的有机复合涂层钢带具有各种用途,包括汽车车身。