摘要:
A high strength thin steel sheet that is mainly used for structural members and inner and outer panels for a vehicle, a galvanized steel sheet, and methods of manufacturing the same. The high strength thin steel sheet for superior press formability includes, by weight percent, 0.06 to 0.4% C, 1.0 to 5.0% Mn, 0.05 to 2.5% Si, 0.01 to 2.0% Ni, 0.02 to 2% Cu, 0.01 to 0.04% Ti, 0.05 to 2.5% Al, 0.005 to 0.1% Sb, 0.0005 to 0.004% B, 0.007% or less N, and balance Fe and inevitable impurities, and meeting relation of Ni+0.5×Mn+0.3×Cu>0.9, which is defined as Ni*, and Al/Ni*
摘要:
A high strength thin steel sheet that is mainly used for structural members and inner and outer panels for a vehicle, a galvanized steel sheet, and methods of manufacturing the same. The high strength thin steel sheet for superior press formability includes, by weight percent, 0.06 to 0.4% C, 1.0 to 5.0% Mn, 0.05 to 2.5% Si, 0.01 to 2.0% Ni, 0.02 to 2% Cu, 0.01 to 0.04% Ti, 0.05 to 2.5% Al, 0.005 to 0.1% Sb, 0.0005 to 0.004% B, 0.007% or less N, and balance Fe and inevitable impurities, and meeting relation of Ni+0.5×Mn+0.3×Cu>0.9, which is defined as Ni*, and Al/Ni*
摘要:
A low specific gravity and high strength steel sheet includes C of 0.2% to 0.8%, Mn of 2% to 10%, P of 0.02% or less, S of 0.015% or less, Al of 3% to 15%, and N of 0.01% or less. A ratio of Mn/Al is 0.4 to 1.0. Retained austenite in a structure is included in the range of 1% or more. The steel sheet further includes one or two or more elements selected from the group consisting of Si of 0.1% to 2.0%, Cr of 0.1% to 0.3%, Mo of 0.05% to 0.5%, Ni of 0.1% to 2.0%, Cu of 0.1% to 1.0%, B of 0.0005% to 0.003%, Ti of 0.01% to 0.2%, Zr of 0.005% to 0.2%, Nb of 0.005% to 0.2%, W of 0.1% to 1.0%, Sb of 0.005% to 0.2%, and Ca of 0.001% to 0.2%.
摘要:
A low specific gravity and high strength steel sheet includes C of 0.2% to 0.8%, Mn of 2% to 10%, P of 0.02% or less, S of 0.015% or less, Al of 3% to 15%, and N of 0.01% or less. A ratio of Mn/Al is 0.4 to 1.0. Retained austenite in a structure is included in the range of 1% or more. The steel sheet further includes one or two or more elements selected from the group consisting of Si of 0.1% to 2.0%, Cr of 0.1% to 0.3%, Mo of 0.05% to 0.5%, Ni of 0.1% to 2.0%, Cu of 0.1% to 1.0%, B of 0.0005% to 0.003%, Ti of 0.01% to 0.2%, Zr of 0.005% to 0.2%, Nb of 0.005% to 0.2%, W of 0.1% to 1.0%, Sb of 0.005% to 0.2%, and Ca of 0.001% to 0.2%.
摘要:
A cold rolled steel sheet and a hot dip galvanized steel sheet, which have high strength and elongation, such as a tensile strength of 980 MPa or more and an elongation of 28% or more, and excellent delayed fracture resistance, and manufacturing methods thereof. The cold rolled steel sheet has a composition including 0.05 to 0.3 weight percent C, 0.3 to 1.6 weight percent Si, 4.0 to 7.0 weight percent Mn, 0.5 to 2.0 weight percent Al, 0.01 to 0.1 weight percent Cr, 0.02 to 0.1 weight percent Ni and 0.005 to 0.03 weight percent Ti, 5 to 30 ppm B, 0.01 to 0.03 weight percent Sb, 0.008 weight percent or less S, balance Fe and impurities. The hot dip galvanized steel sheet has a hot dip galvanized layer or a hot dip galvannealed layer on the cold rolled steel sheet.
摘要:
A cold rolled steel sheet and a hot dip galvanized steel sheet, which have high strength and elongation, such as a tensile strength of 980 MPa or more and an elongation of 28% or more, and excellent delayed fracture resistance, and manufacturing methods thereof. The cold rolled steel sheet has a composition including 0.05 to 0.3 weight percent C, 0.3 to 1.6 weight percent. Si, 4.0 to 7.0 weight percent Mn, 0.5 to 2.0 weight percent Al, 0.01 to 0.1 weight percent Cr, 0.02 to 0.1 weight percent Ni and 0.005 to 0.03 weight percent Ti, 5 to 30 ppm B, 0.01 to 0.03 weight percent Sb, 0.008 weight percent or less S, balance Fe and impurities. The hot dip galvanized steel sheet has a hot dip galvanized layer or a hot dip galvannealed layer on the cold rolled steel sheet.