The present invention provides carbon fiber paper consisting of an organic high-molecular compound as a binder and carbon fibers, characterized in that the carbon fibers contain thin fibers with an average diameter smaller than 5 μm and an average fiber length of 3 to 10 mm; a porous carbon electrode substrate for a fuel cell having a thickness of 0.05 to 0.5 mm and a bulk density of 0.3 to 0.8 g/cm3, also having a bending strength of 10 MPa or higher and a deflection of 1.5 mm or more at the time of bending, measured by a three-point bending test in conditions of using a sample width of 1 cm, a strain rate of 10 mm/min, and a distance between supporting points of 2 cm; and a method of producing a porous carbon electrode substrate for a fuel cell by impregnating the carbon fiber paper with a thermosetting resin, curing the thermosetting resin by heating and pressing treatment, and then carbonizing the paper. The electrode substrate of the present invention is excellent in flexibility and bending strength and able to be rolled on a roll and thus has high productivity, and the carbon fiber paper of the present invention is suitable for producing the electrode substrate.
摘要翻译:本发明提供由作为粘合剂的有机高分子化合物和碳纤维组成的碳纤维纸,其特征在于,所述碳纤维含有平均直径小于5μm,平均纤维长度为3〜10mm的细纤维; 具有厚度为0.05〜0.5mm,体积密度为0.3〜0.8g / cm 3的燃料电池用多孔碳电极基板,其弯曲强度为10MPa以上,偏转 在使用1cm的样品宽度,10mm / min的应变速度和2cm的支撑点之间的距离的条件下,通过三点弯曲试验测定弯曲时的1.5mm以上的1.5mm以上。 以及通过用热固性树脂浸渍碳纤维纸来制造用于燃料电池的多孔碳电极基板的方法,通过加热和压制处理固化热固性树脂,然后碳化碳纸。 本发明的电极基板的柔软性和弯曲强度优异,能够在辊上滚动,因此具有高生产率,本发明的碳纤维纸适用于制造电极基板。
摘要:
The present invention provides carbon fiber paper consisting of an organic high-molecular compound as a binder and carbon fibers, characterized in that the carbon fibers contain thin fibers with an average diameter smaller than 5 &mgr;m and an average fiber length of 3 to 10 mm; a porous carbon electrode substrate for a fuel cell having a thickness of 0.05 to 0.5 mm and a bulk density of 0.3 to 0.8 g/cm3, also having a bending strength of 10 MPa or higher and a deflection of 1.5 mm or more at the time of bending, measured by a three-point bending test in conditions of using a sample width of 1 cm, a strain rate of 10 mm/min, and a distance between supporting points of 2 cm; and a method of producing a porous carbon electrode substrate for a fuel cell by impregnating the carbon fiber paper with a thermosetting resin, curing the thermosetting resin by heating and pressing treatment, and then carbonizing the paper. The electrode substrate of the present invention is excellent in flexibility and bending strength and able to be rolled on a roll and thus has high productivity, and the carbon fiber paper of the present invention is suitable for producing the electrode substrate.
摘要翻译:本发明提供由作为粘合剂的有机高分子化合物和碳纤维组成的碳纤维纸,其特征在于,所述碳纤维含有平均直径小于5μm,平均纤维长度为3〜10mm的细纤维; 具有厚度为0.05〜0.5mm,体积密度为0.3〜0.8g / cm 3的燃料电池用多孔碳电极基板,弯曲强度为10MPa以上,偏转为1.5mm以上 在弯曲时,使用1cm的样品宽度,10mm / min的应变速度和2cm的支撑点之间的距离,通过三点弯曲试验测定。 以及通过用热固性树脂浸渍碳纤维纸来制造用于燃料电池的多孔碳电极基板的方法,通过加热和压制处理固化热固性树脂,然后碳化碳纸。本发明的电极基板是优异的 柔软性和弯曲强度,并且能够在辊上滚动并因此具有高生产率,并且本发明的碳纤维纸适用于制造电极基材。
摘要:
The present invention provides carbon fiber paper consisting of an organic high-molecular compound as a binder and carbon fibers, characterized in that the carbon fibers contain thin fibers with an average diameter smaller than 5 μm and an average fiber length of 3 to 10 mm; a porous carbon electrode substrate for a fuel cell having a thickness of 0.05 to 0.5 mm and a bulk density of 0.3 to 0.8 g/cm3, also having a bending strength of 10 MPa or higher and a deflection of 1.5 mm or more at the time of bending, measured by a three-point bending test in conditions of using a sample width of 1 cm, a strain rate of 10 mm/min, and a distance between supporting points of 2 cm; and a method of producing a porous carbon electrode substrate for a fuel cell by impregnating the carbon fiber paper with a thermosetting resin, curing the thermosetting resin by heating and pressing treatment, and then carbonizing the paper.
摘要翻译:本发明提供由作为粘合剂的有机高分子化合物和碳纤维组成的碳纤维纸,其特征在于,所述碳纤维含有平均直径小于5μm,平均纤维长度为3〜10mm的细纤维; 具有厚度为0.05〜0.5mm,体积密度为0.3〜0.8g / cm 3的燃料电池用多孔碳电极基板,其弯曲强度为10MPa以上,偏转 在使用1cm的样品宽度,10mm / min的应变速度和2cm的支撑点之间的距离的条件下,通过三点弯曲试验测定弯曲时的1.5mm以上的1.5mm以上。 以及通过用热固性树脂浸渍碳纤维纸来制造用于燃料电池的多孔碳电极基板的方法,通过加热和压制处理固化热固性树脂,然后碳化碳纸。
摘要:
The present invention provides carbon fiber paper consisting of an organic high-molecular compound as a binder and carbon fibers, characterized in that the carbon fibers contain thin fibers with an average diameter smaller than 5 μm and an average fiber length of 3 to 10 mm; a porous carbon electrode substrate for a fuel cell having a thickness of 0.05 to 0.5 mm and a bulk density of 0.3 to 0.8 g/cm3, also having a bending strength of 10 MPa or higher and a deflection of 1.5 mm or more at the time of bending, measured by a three-point bending test in conditions of using a sample width of 1 cm, a strain rate of 10 mm/min, and a distance between supporting points of 2 cm; and a method of producing a porous carbon electrode substrate for a fuel cell by impregnating the carbon fiber paper with a thermosetting resin, curing the thermosetting resin by heating and pressing treatment, and then carbonizing the paper. The electrode substrate of the present invention is excellent in flexibility and bending strength and able to be rolled on a roll and thus has high productivity, and the carbon fiber paper of the present invention is suitable for producing the electrode substrate.
摘要翻译:本发明提供由作为粘合剂的有机高分子化合物和碳纤维组成的碳纤维纸,其特征在于,所述碳纤维含有平均直径小于5μm,平均纤维长度为3〜10mm的细纤维; 具有厚度为0.05〜0.5mm,体积密度为0.3〜0.8g / cm 3的燃料电池用多孔碳电极基板,其弯曲强度为10MPa以上,偏转 在使用1cm的样品宽度,10mm / min的应变速度和2cm的支撑点之间的距离的条件下,通过三点弯曲试验测定弯曲时的1.5mm以上的1.5mm以上。 以及通过用热固性树脂浸渍碳纤维纸来制造用于燃料电池的多孔碳电极基板的方法,通过加热和压制处理固化热固性树脂,然后碳化碳纸。 本发明的电极基板的柔软性和弯曲强度优异,能够在辊上滚动,因此具有高生产率,本发明的碳纤维纸适用于制造电极基板。
摘要:
This invention relates to an acrylonitrile-based precursor fiber for the formation of a carbon fiber which is obtained by spinning an acrylonitrile-based copolymer (which contains not less than 90% by weight of acrylonitrile units as monomeric components, contains 5.0×10−5 to 2.0×10−4 equivalent/g of carboxylic acid groups and not less than 0.5×10−5 equivalent/g of sulfate groups and/or sulfonic groups, and has protons and/or ammonium ions as counter ions to the carboxylic acid groups, sulfate groups and sulfonic groups) and treating the resulting coagulated filament, wherein the amount of iodine adsorbable to the acrylonitrile-based precursor fiber is not greater than 0.8% by weight based on the weight of the fiber. By using this precursor fiber, a carbon fiber having a high strength and a high elastic modulus can be easily formed.
摘要:
The present invention provides a unique fibrous sheet for forming a polymer gel electrolyte having ion conductivity, a unique polymer gel electrolyte using such a sheet, and a unique method for the manufacture thereof. More specifically, the present invention provides a unique fibrous sheet for forming a polymer gel electrolyte having excellent ion conductivity and suitable as an electrolyte for various electronic devices such as lithium primary batteries, lithium secondary batteries, and electric double layer capacitors, as well as a unique polymer gel electrolyte using such a sheet, and also a unique method for the manufacture thereof.
摘要:
An electric double layer capacitor containing a polymer gel electrolyte layer provided between polarizable electrodes, wherein the polymer gel electrolyte layer contains a nonaqueous electrolytic solution, and a fibrous sheet material containing mainly a fiber or pulp material capable of forming a polymer gel with the nonaqueous electrolytic solution.
摘要:
An alkali resistant synthetic fiber and a sheeting obtained therefrom are disclosed, the fiber being comprised of a polymer mixture consisting of (A) from 15 to 80% by weight of polysulphone, (B) from 20 to 85% by weight of polyvinyl chloride having a degree of polymerization of from 800 to 2,500, and (C) up to 65% by weight of other vinyl polymer, each based on the total weight of the components (A), (B), and (C). The sheeting is excellent in alkali resistant in high temperatures and liquid retention and is therefore useful as industrial filters, battery separators, and industrial wipers.
摘要:
The present invention provides fibril system fibers which may be employed in filter applications and in artificial leather applications, and also provides an industrially superior manufacturing method for such fibril system fibers, and a spinning nozzle. The fibril fibers of the present invention include at least one macromolecular polymer having a film forming ability, and they have a structure in which fibrillated fibers having a diameter of 10 micrometers or less branch from main fibers having a width within a range of 0.1 micrometers-500 micrometers, and a length within a range of 10 micrometers-10 cm.