摘要:
In an electrode drying process in which the electrode is molded in a sheet shape by kneading activated carbon powder, a binding material and an organic solvent for lubrication and a polarizing property electrode is formed by heating and removing the organic solvent for lubrication in the molded electrode, the organic solvent for lubrication included in the electrode is removed in a state in which the above electrode is widened in the sheet shape. In a manufacturing method of an electrode sheet for the electrical double layer capacitor, continuous drying and vacuum drying are performed in a drying process.
摘要:
In an electrode drying process in which the electrode is molded in a sheet shape by kneading activated carbon powder, a binding material and an organic solvent for lubrication and a polarizing property electrode is formed by heating and removing the organic solvent for lubrication in the molded electrode, the organic solvent for lubrication included in the electrode is removed in a state in which the above electrode is widened in the sheet shape. In a manufacturing method of an electrode sheet for the electrical double layer capacitor, continuous drying and vacuum drying are performed in a drying process.
摘要:
In an electrode drying process in which the electrode is molded in a sheet shape by kneading activated carbon powder, a binding material and an organic solvent for lubrication and a polarizing property electrode is formed by heating and removing the organic solvent for lubrication in the molded electrode, the organic solvent for lubrication included in the electrode is removed in a state in which the above electrode is widened in the sheet shape. In a manufacturing method of an electrode sheet for the electrical double layer capacitor, continuous drying and vacuum drying are performed in a drying process.
摘要:
By using the polarized electrode for electric double layer capacitor of the present invention, which is produced by mixing powdery activated carbon with a binder, and is characterized by the concentration of an organic compound being not more than 300 (ppm), the amount of organic compounds which remain in the pore of the powdery activated carbon decrease, and a possibility of forming the electric double layer by adsorption of electrolytic ion can be prevented. Thereby, an electric double layer is sufficiently formed inside the pore of the powdery activated carbon, and the diffusion resistance between the powdery activated carbon and the electrolyte becomes low. By constituting as such, an electric double layer capacitor with a large electrostatic capacity and a little internal resistance can be obtained.
摘要:
By using the polarized electrode for electric double layer capacitor of the present invention, which is produced by mixing powdery activated carbon with a binder, and is characterized by the concentration of an organic compound being not more than 300 (ppm), the amount of organic compounds which remain in the pore of the powdery activated carbon decrease, and a possibility of forming the electric double layer by adsorption of electrolytic ion can be prevented. Thereby, an electric double layer is sufficiently formed inside the pore of the powdery activated carbon, and the diffusion resistance between the powdery activated carbon and the electrolyte becomes low. By constituting as such, an electric double layer capacitor with a large electrostatic capacity and a little internal resistance can be obtained.
摘要:
To produce activated carbon for an electrode of an electric double-layer capacitor, the following steps are carried out sequentially: a step of subjecting a massive mesophase pitch to a pulverizing treatment to provide a pulverized powder; a step of subjecting the pulverized powder to an infusibilizing treatment under conditions of a temperature in a range of 300° C. (inclusive) to 450° C. (inclusive) in the atmospheric air current, a step of subjecting the pulverized powder to a carbonizing treatment under conditions of a temperature in a range of 600° C. (inclusive) to 900° C. (inclusive) in an inert gas current to provide a carbonized powder, a step of subjecting the carbonized powder to an alkali activating treatment under conditions of a temperature in a range of 500° C. (inclusive) to 1,000° C. (inclusive) in an inert gas atmosphere, followed by the post treatments, thereby producing alkali-activated carbon, and a step of subjecting the alkali-activated carbon to a pulverizing treatment. If an electrode is produced using the activated carbon, the electrode density can be increased.
摘要:
An electrochemical capacitor is provided having double-layer electrode elements interposed with a separator. The electrode elements being made of activated carbon and impregnated with a nonaqueous electrolytic liquid yields a capacitor with low internal resistance, greater capacitance and higher energy density. Methods for producing the activated carbon electrodes and the capacitor assembly are also described.
摘要:
Activated carbon for use in an electric double layer capacitor is in the form of particles produced by crushing activated carbon or fibers of activated carbon. The particles have a surface covered at least partly with a laminated structure layer of graphite formed along the surface.
摘要:
Activated carbon for an electrode of an electric double-layer capacitor is produced by subjecting a carbon material sequentially to a carbonizing treatment and an alkali activating treatment, and by using a carbon material. The carbon material used is a condensed polycyclic aromatic compound (CPAC) which has a condensed ring (CR) and at least one aliphatic hydrocarbon radical (R) bonded to said condensed ring (CR). The condensed ring (CR) includes at least one alicyclic hydrocarbon structure moiety (ALC). In an analysis chart resulting from a 13C-NMR spectroscopy of the condensed polycyclic aromatic compound, a signal intensity ratio IL/IR is equal to or larger than 0.2, and a signal intensity ratio IC/IR is equal to or larger than 0.14, wherein IR represents a signal intensity of an aromatic peak; IL represents a signal intensity of an aliphatic hydrocarbon peak; and IC represents a signal intensity of an alicyclic hydrocarbon peak. Thus, activated carbon of a low electrostatic capacity revealing voltage and a high electrostatic capacity density (F/cc) can be produced by using a particular carbon material.
摘要:
To produce activated carbon for an electrode of an electric double-layer capacitor, the following steps are carried out sequentially: a step of subjecting a massive mesophase pitch to a pulverizing treatment to provide a pulverized powder; a step of subjecting the pulverized powder to an infusibilizing treatment under conditions of a temperature in a range of 300° C. (inclusive) to 450° C. (inclusive) in the atmospheric air current, a step of subjecting the pulverized powder to a carbonizing treatment under conditions of a temperature in a range of 600° C. (inclusive) to 900° C. (inclusive) in an inert gas current to provide a carbonized powder, a step of subjecting the carbonized powder to an alkali activating treatment under conditions of a temperature in a range of 500° C. (inclusive) to 1,000° C. (inclusive) in an inert gas atmosphere, followed by the post treatments, thereby producing alkali-activated carbon, and a step of subjecting the alkali-activated carbon to a pulverizing treatment. If an electrode is produced using the activated carbon, the electrode density can be increased.