摘要:
An antistatic expandable styrene polymer in bead form, containinga) a styrene polymer,b) from 0.5 to 3% by weight, based on a), of a coating containingb1) from 10 to 70% by weight of finely divided silica;b2) from 20 to 80% by weight of a hydroxy-containing quaternary ammonium salt and, if desired, p1 b3) from 0.05 to 20% by weight of a conventional coupling agent and/orc) from 1 to 8% by weight, based on a), of a C.sub.3 to C.sub.6 hydrocarbon as blowing agent,and, if desired,d) conventional additives in effective amounts.
摘要:
A composition and a method for coating metallic surfaces with a silane/silanol/siloxane/polysiloxane-containing composition, whereby the composition contains a) at least one compound selected from the silanes, silanols, siloxanes and polysiloxanes, b) at least two compounds selected from titanium-, hafnium-, zirconium-, aluminum- or boron-containing compounds, optionally c) at least one type of cation selected from cations of metals of the 1st to 3rd and 5th to 8th sub-groups including the lanthanides and the 2nd main group of the periodic table of the elements or at least one corresponding compound, d) at least one organic compound selected from monomers, oligomers, polymers, copolymers and block copolymers or e) at least one substance affecting the pH value, water and optionally at least one organic solvent.
摘要:
A brake device of a vehicle, containing an eddy current disk brake having a rotationally fixed stator and a rotating rotor, wherein the rotor or the stator bears an eddy current path and the stator or the rotor bears a magnetic arrangement, the magnetic field lines of which induce eddy currents in the eddy current path for generating a braking torque upon a relative movement of the rotor with respect to the stator, and a friction disk brake having at least one brake disk and brake pads cooperating with the brake disk for generating a braking friction torque between the brake disk and the brake pads, wherein the rotor of the eddy current disk brake is formed by the brake disk of the friction disk brake.
摘要:
A process for producing a repair coating on a metallic surface coated with a corrosion protecting coating A applied with a pretreatment composition, an organic composition or a silicon compound containing composition. Corrosion protecting coating A has been at least partially removed in the area Z, and a thin corrosion protecting coating B containing a silicon compound is applied with a solution or dispersion containing a silane, a silanol, a siloxane, a polysiloxane or a mixture thereof on at least a part of the area Z. A further corrosion protecting coating C which is generated with an organic composition like a primer, a wet-primer, an e-coat, a powder coat, a base-coat or a clear-coat or a composition which is the same or another siloxane composition as for the thin film B may also be applied to coating B.
摘要:
A process for producing a repair coating on a metallic surface coated with a corrosion protecting coating A applied with a pretreatment composition, an organic composition or a silicon compound containing composition. Corrosion protecting coating A has been at least partially removed in the area Z, and a thin corrosion protecting coating B containing a silicon compound is applied with a solution or dispersion containing a silane, a silanol, a siloxane, a polysiloxane or a mixture thereof on at least a part of the area Z. A further corrosion protecting coating C which is generated with an organic composition like a primer, a wet-primer, an e-coat, a powder coat, a base-coat or a clear-coat or a composition which is the same or another siloxane composition as for the thin film B may also be applied to coating B.
摘要:
A compositon and a method for coating metallic surfaces with a silane/silanol/siloxane/polysiloxane-containing composition, whereby the composition contains a) at least one compound selected from the silanes, silanols, siloxanes and polysiloxanes, b) at least two compounds selected from titanium-, hafnium-, zirconium-, aluminum- or boron-containing compounds, optionally c) at least one type of cation selected from cations of metals of the 1st to 3rd and 5th to 8th sub-groups including the lanthanides and the 2nd main group of the periodic table of the elements or at least one corresponding compound, d) at least one organic compound selected from monomers, oligomers, polymers, copolymers and block copolymers or e) at least one substance affecting the pH value, water and optionally at least one organic solvent.
摘要:
The invention relates to a process for coating metallic surfaces with a composition containing silane/silanol/siloxane/polysiloxane, wherein, in addition to a) at least one compound selected from silanes, silanols, siloxanes and polysiloxanes, b) at least one compound containing titanium, hafnium, zirconium, aluminium and/or boron, and c) at least one type of cation selected from cations of metals of subgroups 1 to 3 and 5 to 8, including lanthanides, and of main group 2 of the periodic table of the elements, and/or at least one corresponding compound, the composition contains at least one substance d) selected from: d1) silicon-free compounds having at least one amino, urea and/or ureido group in each case, d2) anions of nitrite and/or compounds having at least one nitro group, d3) compounds based on peroxide, and d4) phosphorus-containing compounds, anions of at least one phosphate and/or anions of at least one phosphonate, as well as e) water, and f) optionally also at least one organic solvent. The invention further relates to corresponding aqueous compositions.
摘要:
Expandable styrene polymers of high expandability comprisea) a styrene polymer having a viscosity, measured in toluene, of from 55 to 80 [ml/g] and a melt flow index MFI (190.degree. C., 3.8 kp) of from 7.5 to 30 [g/10 min],b) from 1 to 10% by weight, based on a), of a C.sub.3 - to C.sub.6 -hydrocarbon as blowing agent, and, if desired,c) conventional assistants in effective amounts.
摘要:
Polyoxymethylene molding materials having improved heat stability and consisting of(A) one or more polyoxymethylene homopolymers and/or copolymers and(B) one or more antioxidants having a sterically hindered phenolic structure,(C) with or without additives, contain(D) as an additive, one or more alkaline earth metal silicates and/or alkaline earth metal glycerophosphates, advantageously in an amount of from 0.002 to 2.0% by weight, based on the weight of component (A),for improving the heat stability, reducing the tendency to discoloration and minimizing the free formaldehyde content.To prepare the novel polyoxymethylene molding materials, the components are advantageously melted in an extruder at from 150.degree. to 260.degree. C.The polyoxymethylene molding materials are useful for the production of films or, preferably, moldings, which are used, for example, in the automotive, electrical appliances and electronics industries.