公开(公告)号：US06416594B1

公开(公告)日：2002-07-09

申请号：US09680171

申请日：2000-10-05

申请人： Nobuo Yamagami ,  Kunikazu Tomita ,  Yasuyuki Takada ,  Yoshihiko Oda ,  Hideki Matsuoka ,  Tatsuhiko Hiratani ,  Katsumi Nakajima ,  Kenji Tahara

发明人： Nobuo Yamagami ,  Kunikazu Tomita ,  Yasuyuki Takada ,  Yoshihiko Oda ,  Hideki Matsuoka ,  Tatsuhiko Hiratani ,  Katsumi Nakajima ,  Kenji Tahara

IPC分类号： C21D812

CPC分类号： C21D8/0273 ,  C21D8/0226 ,  C21D8/0236 ,  C22C38/004 ,  C22C38/04 ,  C22C38/06 ,  C22C38/14

摘要： A heat shrink band steel sheet of the present invention comprises on the basis of percent in weight C: 0.1% or less, Si: 0.1% or less, Mn: 0.1 to 2%, P: 0.15% or less, S: 0.02% or less, sol Al: 0.08% or less, and N: 0.005% or less, or C: 0.005% or less, Si: 0.1% or less, Mn: 0.1 to 2%, P: 0.15% or less, S: 0.02% or less, sol Al: 0.08% or less, N: 0.005% or less, Ti: 0.02 to 0.06%, and B: 0.0003 to 0.005%, wherein the product of a magnetic permeability at the magnetic field of 0.3 Oe after heat shrinking treatment and a thickness (mm) is at least 350. A color CRT having a sufficient magnetic shielding characteristic and a less amount of color deviation can be realized by the steel sheet.

摘要翻译： 本发明的热收缩带钢基于重量百分比C：0.1％以下，Si：0.1％以下，Mn：0.1〜2％，P：0.15％以下，S：0.02％ 以下，溶胶A1：0.08％以下，N：0.005％以下或C：0.005％以下，Si：0.1％以下，Mn：0.1〜2％，P：0.15％以下，S： 0.02％以下，溶胶Al：0.08％以下，N：0.005％以下，Ti：0.02〜0.06％，B：0.0003〜0.005％，其中磁场的磁导率为0.3Oe的磁导率在 热收缩处理和厚度（mm）至少为350°。通过钢板可以实现具有足够的磁屏蔽特性和较少颜色偏差的彩色CRT。

公开(公告)号：US06554917B1

公开(公告)日：2003-04-29

申请号：US09744139

申请日：2001-03-19

申请人： Nobuo Yamagami ,  Kunikazu Tomita ,  Yasuyuki Takada ,  Yoshihiko Oda ,  Chohachi Sato ,  Teruo Takeuchi ,  Ichiro Saito ,  Hiroaki Kato

发明人： Nobuo Yamagami ,  Kunikazu Tomita ,  Yasuyuki Takada ,  Yoshihiko Oda ,  Chohachi Sato ,  Teruo Takeuchi ,  Ichiro Saito ,  Hiroaki Kato

IPC分类号： C22C3802

CPC分类号： H01F1/14775 ,  C21D8/0226 ,  C21D8/0236 ,  C21D8/0273 ,  C21D8/12 ,  C22C38/002 ,  C22C38/004 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  H01J29/867 ,  H01J2229/003

摘要： A steel sheet for preparing a heat shrink band effective for preventing the color drift is provided by a steel sheet having 24 kg/mm2 or higher of yield stress and 400 or higher of the product between the permeability &mgr; under a magnetic field of 0.3 Oe and the sheet thickness.

摘要翻译： 用于制备有效防止颜色漂移的热收缩带的钢板是由在0.3Oe的磁场和渗透率μμ之间的产品在屈服应力为24kg / mm2的钢板和400或更高的产品之间提供的， 片材厚度。

公开(公告)号：US6139650A

公开(公告)日：2000-10-31

申请号：US41335

申请日：1998-03-12

申请人： Yoshihiko Oda ,  Nobuo Yamagami ,  Akira Hiura ,  Yasushi Tanaka ,  Noritaka Takahashi ,  Hideki Matsuoka ,  Atsushi Chino ,  Katsumi Yamada ,  Shunji Iizuka

发明人： Yoshihiko Oda ,  Nobuo Yamagami ,  Akira Hiura ,  Yasushi Tanaka ,  Noritaka Takahashi ,  Hideki Matsuoka ,  Atsushi Chino ,  Katsumi Yamada ,  Shunji Iizuka

IPC分类号： C21D8/12 ,  C22C38/02 ,  H01F1/047

CPC分类号： C21D8/1272 ,  C22C38/02 ,  C21D8/1261

摘要： A non-oriented electromagnetic steel sheet contains 0.005 wt. % or less C, 0.2 wt. % or less P, 0.005 wt. % or less N, 4.5 wt. % or less Si, 0.05 to 1.5 wt. % Mn, 1.5 wt. % or less Al and 0.001 wt. % or less S, at least one element selected from the group of 0.001 to 0.05 wt. % Sb, 0.002 to 0.1 wt. % Sn, 0.0005 to 0.01 wt. % Se and 0.0005 to 0.01 wt. % Te; and the balance being Fe and inevitable impurities. The non-oriented electromagnetic steel sheet is produced by the steps of: hot-rolling a slab to form a hot-rolled steel sheet, cold-rolling the hot-rolled steel sheet to form a cold-rolled steel sheet; and finish annealing the cold-rolled steel sheet.

摘要翻译： 无取向电磁钢板含有0.005重量％ ％以下C，0.2重量％ ％以下P，0.005重量％ ％以下N，4.5重量％ ％以下的Si，0.05〜1.5重量％ ％Mn，1.5wt。 ％以下Al和0.001重量％ ％以下的S，选自0.001〜0.05重量％的至少一种元素。 ％Sb，0.002〜0.1wt。 ％Sn，0.0005〜0.01重量％ ％Se和0.0005〜0.01wt。 ％Te 余量为Fe和不可避免的杂质。 无取向电磁钢板是通过以下工序制造的：热轧板坯以形成热轧钢板，冷轧该热轧钢板以形成冷轧钢板; 并对冷轧钢板进行最终退火。

公开(公告)号：US20150213928A1

公开(公告)日：2015-07-30

申请号：US14413658

申请日：2012-08-08

申请人： Hiroaki Toda ,  Tadashi Nakanishi ,  Masaaki Kohno ,  Yoshihiko Oda

发明人： Hiroaki Toda ,  Tadashi Nakanishi ,  Masaaki Kohno ,  Yoshihiko Oda

IPC分类号： H01F1/16 ,  C21D8/02 ,  C21D6/00 ,  C22C38/34 ,  C22C38/60 ,  C22C38/06 ,  C22C38/04 ,  C22C38/02 ,  C22C38/00 ,  C22C38/32 ,  C21D9/46 ,  C22C38/12

CPC分类号： H01F1/16 ,  C21D1/76 ,  C21D6/002 ,  C21D6/005 ,  C21D6/008 ,  C21D8/0236 ,  C21D8/0263 ,  C21D8/1222 ,  C21D8/1233 ,  C21D8/1261 ,  C21D8/1272 ,  C21D8/1283 ,  C21D9/46 ,  C22C38/001 ,  C22C38/002 ,  C22C38/004 ,  C22C38/008 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/12 ,  C22C38/32 ,  C22C38/34 ,  C22C38/60

摘要： According to the present invention, a high-strength electrical steel sheet that is suitable as rotor material for a high speed motor, steadily has high strength, and also has excellent magnetic properties can be obtained by setting the chemical composition thereof to include, by mass %, C: 0.005% or less, Si: more than 3.5% and 4.5% or less, Mn: 0.01% or more and 0.10% or less, Al: 0.005% or less, Ca: 0.0010% or more and 0.0050% or less, S: 0.0030% or less, and N: 0.0030% or less, Ca/S being 0.80 or more, the balance being Fe and incidental impurities, and by setting the sheet thickness to 0.40 mm or less, the non-recrystallized deformed microstructure to 10% or more and 70% or less, tensile strength (TS) to 600 MPa or more, and iron loss W10/400 to 30 W/kg or less.

摘要翻译： 根据本发明，适用于高速电动机的转子材料的高强度电工钢板稳定地具有高的强度，并且通过将其化学组成设定为包括质量 ％，C：0.005％以下，Si：超过3.5％，4.5％以下，Mn：0.01％以上且0.10％以下，Al：0.005％以下，Ca：0.0010％以上且0.0050％以下 S：0.0030％以下，N：0.0030％以下，Ca / S为0.80以上，余量为Fe和附带杂质，通过将片材厚度设定为0.40mm以下，未再结晶变形 微观结构为10％以上且70％以下，拉伸强度（TS）为600MPa以上，铁损W10 / 400〜30W / kg以下。

公开(公告)号：US20130263981A1

公开(公告)日：2013-10-10

申请号：US13992011

申请日：2011-12-16

申请人： Yoshiaki Zaizen ,  Yoshihiko Oda ,  Hiroaki Toda

发明人： Yoshiaki Zaizen ,  Yoshihiko Oda ,  Hiroaki Toda

IPC分类号： C21D8/02

CPC分类号： C21D8/0263 ,  C21D8/1255 ,  C21D8/1261 ,  C21D8/1272 ,  C22C38/00 ,  C22C38/001 ,  C22C38/008 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/60 ,  H01F1/16

摘要： A non-oriented electrical steel sheet having a high magnetic flux density in a rolling direction of the steel sheet is produced by hot rolling a raw steel material including C: not more than 0.03 mass %, Si: not more than 4 mass %, Mn: 0.03˜3 mass %, Al: not more than 3 mass %, S: not more than 0.005 mass %, N: not more than 0.005 mass % and the balance being Fe and inevitable impurities, and then cold rolling and finishing annealing to produce a non-oriented electrical steel sheet, characterized in that a crystal grain size before the cold rolling is rendered into not more than 100 μM and the finishing annealing is conducted by rapidly heating up to a temperature exceeding recrystallization temperature at an average temperature rising rate of not less than 100° C./sec.

摘要翻译： 通过将包含C：0.03质量％以下的原料钢，Si：4质量％以下的原料钢热轧，制造钢板的轧制方向的磁通密度高的无方向性电磁钢板 ：0.03〜3质量％，Al：3质量％以下S：0.005质量％以下N：0.005质量％以下，余量为Fe和不可避免的杂质，然后冷轧终轧退火至 制造无取向电工钢板，其特征在于，冷轧前的结晶粒径为100μm以下，通过以平均升温速度快速升温至超过再结晶温度的温度进行精加工退火 不低于100℃/秒。

公开(公告)号：US20130306200A1

公开(公告)日：2013-11-21

申请号：US13981955

申请日：2011-02-24

申请人： Masaaki Kohno ,  Yoshiaki Zaizen ,  Yoshihiko Oda ,  Akira Fujita

发明人： Masaaki Kohno ,  Yoshiaki Zaizen ,  Yoshihiko Oda ,  Akira Fujita

IPC分类号： C22C38/60 ,  C22C38/16 ,  C22C38/14 ,  C22C38/00 ,  C22C38/08 ,  C22C38/06 ,  C22C38/04 ,  C22C38/02 ,  C21D8/12 ,  C22C38/10

CPC分类号： C22C38/10 ,  C21D8/12 ,  C21D8/1227 ,  C21D8/1266 ,  C21D8/1272 ,  C22C38/001 ,  C22C38/002 ,  C22C38/004 ,  C22C38/005 ,  C22C38/008 ,  C22C38/02 ,  C22C38/04 ,  C22C38/06 ,  C22C38/08 ,  C22C38/14 ,  C22C38/16 ,  C22C38/60 ,  H01F1/16

摘要： The present invention provides a non-oriented electrical steel sheet at low cost that has excellent magnetic properties and mechanical properties as well as excellent quality of steel sheet. The non-oriented electrical steel sheet has a chemical composition containing, by mass %, Si: 5.0% or less, Mn: 2.0% or less, Al: 2.0% or less, and P: 0.05% or less, in a range satisfying formula (1), and furthermore, C: 0.008% or more and 0.040% or less; N: 0.003% or less, and Ti: 0.04% or less, in a range satisfying formula (2), with the balance composed of Fe and incidental impurities: 300≦85[Si %]+16[Mn %]+40[Al %]+490[P %]≦430  (1) 0.008≦Ti*

摘要翻译： 本发明以低成本提供了具有优异的磁性能和机械性能以及优异的钢板质量的无取向电工钢板。 无方向性电磁钢板的化学组成为：以质量％计含有Si：5.0％以下，Mn：2.0％以下，Al：2.0％以下，P：0.05％以下，满足 式（1），并且C：0.008％以上且0.040％以下; N：0.003％以下，Ti：0.04％以下，余量由Fe和杂质构成：300〜85 [Si％] +16 [Mn％] + 40 [ Al％] + 490 [P％] @ 430（1）0.008 @ Ti * <1.2 [C％]（2），其中Ti * = Ti-3.4 [N％]。

公开(公告)号：US20130146187A1

公开(公告)日：2013-06-13

申请号：US13812430

申请日：2011-08-25

申请人： Yoshiaki Zaizen ,  Yoshihiko Oda ,  Masaaki Kohno

发明人： Yoshiaki Zaizen ,  Yoshihiko Oda ,  Masaaki Kohno

IPC分类号： C21D8/02

CPC分类号： C21D8/0205 ,  C21D8/12 ,  C21D8/1244 ,  C21D8/1255 ,  C21D8/1272 ,  C21D2201/05 ,  C22C1/02 ,  C22C38/00

摘要： Disclosed is a method for producing a non-oriented magnetic steel sheet, wherein a steel slab that consists of 0.01-0.1 mass % of C, 4 mass % or less of Si, 0.05-3 mass % of Mn, 3 mass % or less of Al, 0.005 mass % or less of S, 0.005 mass % or less of N and the balance made up of Fe and unavoidable impurities is subjected to hot rolling, cold rolling and final annealing. By carrying out the final annealing, while setting the average heating rate during the heating to 100° C./sec or more and setting the soaking temperature within the temperature range of 750-1100° C., a non-oriented magnetic steel sheet that has extremely increased magnetic flux density in the rolling direction of the steel sheet is advantageously produced.

摘要翻译： 本发明提供一种无取向磁钢板的制造方法，其特征在于，钢板由C：0.01-0.1质量％，Si 4质量％以下，Mn：0.05〜3质量％，3质量％以下 的Al，0.005质量％以下的S，0.005质量％以下的N，余量由Fe和不可避免的杂质构成，进行热轧，冷轧，最终退火。 通过进行最终退火，在将加热时的平均加热速度设定为100℃/秒以上，将均热温度设定在750〜1100℃的温度范围内的非取向磁钢板 钢板的轧制方向的磁通密度极大地提高。

公开(公告)号：US10242782B2

公开(公告)日：2019-03-26

申请号：US14413658

申请日：2012-08-08

申请人： Hiroaki Toda ,  Tadashi Nakanishi ,  Masaaki Kohno ,  Yoshihiko Oda

发明人： Hiroaki Toda ,  Tadashi Nakanishi ,  Masaaki Kohno ,  Yoshihiko Oda

IPC分类号： H01F1/16 ,  C22C38/06 ,  C22C38/60 ,  C21D1/76 ,  C21D8/12 ,  C22C38/00 ,  C22C38/02 ,  C22C38/04 ,  C21D6/00 ,  C21D8/02 ,  C21D9/46 ,  C22C38/12 ,  C22C38/32 ,  C22C38/34

摘要： According to the present invention, a high-strength electrical steel sheet that is suitable as rotor material for a high speed motor, steadily has high strength, and also has excellent magnetic properties can be obtained by setting the chemical composition thereof to include, by mass %, C: 0.005% or less, Si: more than 3.5% and 4.5% or less, Mn: 0.01% or more and 0.10% or less, Al: 0.005% or less, Ca: 0.0010% or more and 0.0050% or less, S: 0.0030% or less, and N: 0.0030% or less, Ca/S being 0.80 or more, the balance being Fe and incidental impurities, and by setting the sheet thickness to 0.40 mm or less, the non-recrystallized deformed microstructure to 10% or more and 70% or less, tensile strength (TS) to 600 MPa or more, and iron loss W10/400 to 30 W/kg or less.