摘要:
Pipe systems having at least one layer comprising a semi-crystalline random polymer of propylene and 0.2 to 5 wt % 1-hexen and optionally a recurring unit selected from ethylene and a C4-C10 α-olefin in an amount from more than 0 to 9% by moles. The polymer exhibits broad molecular weight distribution, in terms of the ratio of weight average molecular weight to numeric average molecular weight formula (I), ranging from 5 to 11, molecular weight distribution of monomodal type and hexen-1 content in the fraction with an intrinsic viscosity of equal to or higher than 3.3 dl/g lower than the hexen-1 content in the fraction with an intrinsic viscosity of less than 3.3 dl/g. ( Mw/ Mn) (I)
摘要:
Pipe systems having at least one layer comprising a semi-crystalline random polymer of propylene and 0.2 to 5 wt % 1-hexen and optionally a recurring unit selected from ethylene and a C4-C10 α-olefin in an amount from more than 0 to 9% by moles. The polymer exhibits broad molecular weight distribution, in terms of the ratio of weight average molecular weight to numeric aver-age molecular weight formula (1), ranging from 5 to 11, molecular weight distribution of monomodal type and hexen-1 content in the fraction with an intrinsic viscosity of equal to or higher than 3.3 dl/g lower than the hexen-1 content in the fraction with an intrinsic viscosity of less than 3.3 dl/g. ( Mw/ Mn) (I)
摘要:
A fiber for thermal bonding comprising semicrystalline random copolymers of propylene, 1-hexene and optionally another α-olefin, the amount of 1-hexene being from 0.75 to less 1.52 mol % (i.e. 1.5 to less than 3 wt %) with respect to the total weight of the copolymer. The said copolymers possess a value of melt flow rate (MFR) ranging from 4 to 35 g/10 min and a molecular weight distribution, in terms of the ratio between weight average molecular weight and numeric average molecular weight ( Mw/ Mn), ranging from 4 to 12.
摘要:
A polypropylene composition for injection-molded drainage systems comprising 78-84 wt % of a crystalline propylene polymer, 8 to less than 13 wt % of an elastomeric copolymer and 8 to less than 13 wt % of polyethylene. The said composition exhibits a flexural modulus value higher than 1400 MPa, a melt flow rate (MFR), determined according to ISO method 1133 (230° C. and 2.16 kg), of from 1.5 to 5.0 g/10 min, and a value of Izod impact resistance at 0° C. of more than 6 kJ/m2 according to ISO method 180/1A.
摘要翻译:一种用于注射成型的排水系统的聚丙烯组合物,其包含78-84重量%的结晶丙烯聚合物,8至小于13重量%的弹性体共聚物和8至小于13重量%的聚乙烯。 所述组合物显示高于1400MPa的挠曲模量值,根据ISO方法1133(230℃和2.16kg)测定的熔体流动速率(MFR)为1.5至5.0g / 10min,值为 根据ISO方法180 / 1A,0℃下的Izod抗冲击强度大于6kJ / m 2。
摘要:
A propylene polymer composition having a Flexural modulus lower than 500 MPa, a total ethylene content from 9 to 30% by weight, a xylene soluble fraction at room temperature higher than 25% by weight, a melting temperature measured by DSC (Tm° C.) from 130 to 150° C. and a ratio between the weight of xylene soluble fraction at 25° C. and the hexane soluble fraction determined on plaque (100 μm) of higher than 4.
摘要:
Multilayer heat-shrinkable films in which the skin layers A consist of a polyolefin selected from: A1) a composition containing 25-45% b.w. of a random copolymer of propylene with ethylene and 55-75% b.w. of a random terpolymer of propylene, ethylene and one or more C4-C10 alpha-olefins; and A2) random copolymer(s) of propylene and one or more C4-C10 alpha-olefins. Core layer B comprises a heterophasic composition comprising: a) 20-60% b.w. of a propylene homopolymer with an isotacticity index higher than 80 or of a propylene crystalline copolymer with ethylene and/or C4-C10 alpha-olefins containing at least 85% b.w. of propylene units and having an isotacticity index of at least 80 or of mixtures thereof and b) 40-80% b.w. of an ethylene copolymer with propylene and/or 1-butene and possibly a diene, containing 20-60% b.w. of ethylene units and completely soluble in xylene at 25° C.
摘要:
Articles, particularly pressure pipes, having high strength as well as high stiffness and very good impact resistance even at low temperatures can be obtained by using a heterophasic polyolefin composition comprising (percent by weight) 70-90% of a random copolymer of propylene with 0.5-6% of 1-hexene, and 10-30% of a polymer of ethylene with a C3-C10 α-olefin and optionally a diene, wherein the polymer of ethylene has an ethylene content higher than 45% and an intrinsic viscosity [η] value from 3 to 5 dl/g.A particular advantage of the present invention is that articles comprising the above heterophasic polyolefin composition show a low ductile to brittle transition temperature (DBTT).
摘要:
A propylene polymer composition having a Flexural modulus lower than 500 MPa, a total ethylene content from 9 to 30% by weight, a xylene soluble fraction at room temperature higher than 25% by weight, a melting temperature measured by DSC (Tm° C.) from 130 to 150° C. and a ratio between the weight of xylene soluble fraction at 25° C. and the hexane soluble fraction determined on plaque (100 μm) of higher than 4.
摘要:
Cast laminates produced from highly crystalline propylene polymers having a MFR ranging from 5 to 15 g/10 min, a ratio between the weight average molecular weight and the number average molecular weight ranging from 4.5 to 9, a density equal to or greater than 0.9020 g/cm3, and solubility in xylene at ambient temperature not greater than 2.5% by weight.
摘要:
Propylene polymers having specific values of total comonomer content and melting temperature, articles obtained therefrom, in particular extrusion blow molded articles, and gas-phase process for obtaining said propylene polymers.