摘要:
The invention relates to a fireproof coating which forms an insulating layer and is based on carbon-forming substances forming a foam layer in the case of a fire, film-forming binders, blowing agents and conventional assistants and additives, wherein said coating contains, as blowing agents, a melamine salt and/or guanidine salts and/or microencapsulated melamine.The fireproof coating forming an insulating layer and according to the invention is stable in particular under tropical conditions (up to 100% rel. humidity, about 75.degree. C.), i.e. it releases only very little NH.sub.3.
摘要:
The invention relates to a flame-retardant coating which forms an insulating layer and is based on substances which carbonize and which form a foam layer in the event of a fire, on film-forming binders, on blowing agents and on customary auxiliaries and additives, wherein the blowing agent and foam layer forming substance present comprises melamine polyphosphate. The novel flame-retardant coating which forms an insulating layer is particularly stable under tropical conditions (at up to 100% rel. humidity, about 75° C.), i.e. it releases only an extremely small amount of NH3.
摘要:
The invention relates to a flame-retardant coating which forms an insulating layer and is based on substances which carbonize and form a foam layer in the event of a fire, on film-forming binders, on blowing agents and on customary auxiliaries and additives, wherein the blowing agent present comprises melamine polyphosphate. The novel flame-retardant coating which forms an insulating layer is particularly stable under tropical conditions (up to 100% rel. humidity, about 75° C.), i.e. it releases only an extremely small amount of NH3.
摘要:
The invention relates to a flame-retardant coating for fiber materials comprising at least one film-forming binder and one flame retardant, wherein this comprises melamine polyphosphate as flame retardant. The invention also relates to the use of the novel flame-retardant coating for producing flame-retardant fiber materials.
摘要:
The invention relates to a fire-protection coating which forms an insulating layer, which comprises a flame retardant mixture which comprises a phosphorus/nitrogen flame retardant and comprises a phosphinic salt of the formula (I) and/or comprises a diphosphinic salt of the formula (II) and/or comprises polymers of these, where R1, R2 are identical or different and are C1-C6-alkyl, linear or branched, and/or aryl; R3 is C1-C10-alkylene, linear or branched, C6-C10-arylene, -alkylarylene or -arylalkylene; M is Mg, Ca, Al, Sb, Sn, Ge, Ti, Zn, Fe, Zr, Ce, Bi, Sr, Mn, Li, Na, K and/or a protonated nitrogen base; m is from 1 to 4; n is from 1 to 4 and x is from 1 to 4.
摘要:
The invention relates to a phosphorus-containing flame retardant formulation for cellulose-containing moldings, comprising from 0.1 to 99.9% by weight of a resin of an organic nitrogen compound and from 0.1 to 99.9% by weight of a phosphorus-containing flame retardant.
摘要:
The invention relates to a granular detergent builder in the form of cogranules of a mixture of sodium bicarbonate and crystalline sheet silicates of the formula NaMSi.sub.x O.sub.2x+1 *yH.sub.2 O, where M is sodium or hydrogen, x is a number from 1.9 to 4, and y is a number from 0 to 20, whereina) the granular detergent builder contains 5 to 50% by weight of crystalline sheet silicate and 50 to 95% by weight of sodium bicarbonate;b) has a pH of .ltoreq.10 in 1% strength solution in distilled water;c) has a calcium-binding capacity of .gtoreq.150 mg Ca/g (30.degree. German hardness) and a magnesium-binding capacity of .gtoreq.4 mg Mg/g (3.degree. German hardness), andd) has an apparent density of .gtoreq.850 g/l.The invention likewise relates to a process for the production of such a granular detergent builder, and to its use in detergents and cleaners.
摘要:
The invention relates to a flame retardant combination comprising, as component A, a phosphinate of the formula (I) and/or a diphosphinate of the formula (II) and/or polymers of these where R1 and R2 are identical or different and are C1–C6-alkyl, linear or branched, and/or aryl; R3 is C1–C10-alkylene, linear or branched, C6–C10-arylene, -alkylarylene or -arylalkylene; M is calcium ions, magnesium ions, aluminum ions and/or zinc ions, m is 2 or 3; n is 1 or 3; x is 1 or 2; and comprising a component B1, B2 and/or B3 wherein B1 is a salt of 1,3,5-triazine compound with polyphosphoric acid, and wherein B2 is a melamine polymetaphosphate, and wherein B3 is a composite salt of polyphosphoric acid with melamine, melam and/or melem.
摘要:
The invention relates to a process for the preparation of crystalline sodium silicates having a sheet structure and high .delta. phase content from water glass, which has been prepared predominantly hydrothermally, by dehydration of the water glass and subsequent crystallization at elevated temperature, wherein the water glass is a mixture of water glass prepared hydrothermally and tank furnace water glass, and also to its use.