    METHOD OF WELDING ALLOY ARTICLES
    8.
    发明申请
    METHOD OF WELDING ALLOY ARTICLES 有权
    焊接合金文章的方法

    公开(公告)号：US20140014628A1

    公开(公告)日：2014-01-16

    申请号：US13549891

    申请日：2012-07-16

    申请人： Yan Cui ,  Daniel Anthony Nowak ,  Srikanth Chandrudu Kottilingam ,  Brian Lee Tollison ,  Dechao Lin

    发明人： Yan Cui ,  Daniel Anthony Nowak ,  Srikanth Chandrudu Kottilingam ,  Brian Lee Tollison ,  Dechao Lin

    IPC分类号： B23K31/02 ,  B23K10/02 ,  B23K26/32 ,  B23K9/167

    CPC分类号： B23K9/23 ,  B23K26/32 ,  B23K2103/05 ,  B23K2103/08 ,  B23K2103/10 ,  B23K2103/26 ,  C22C1/02

    摘要： A method of welding alloys having a ductility drop temperature range to limit strain-age cracking. The method involves the use of a welding device to weld a weld area of an article while maintaining temperatures throughout the weld area and a heat affected zone adjacent the weld area within a non-crack sensitive temperature range that is above a ductility drop temperature range of the alloy being welded. During welding, the temperatures of the weld area and the heat affected zone are predominantly controlled with heat input from the welding device. Once the welding has been terminated, the weld area and the heat affected zone are cooled from the non-crack sensitive temperature range through the ductility drop temperature range to a temperature below the ductility drop temperature range of the alloy.

    摘要翻译： 一种焊接合金的方法，其具有延展性降温温度范围以限制应变时效开裂。 该方法包括使用焊接装置来焊接制品的焊接区域，同时保持在整个焊接区域内的温度和邻近焊接区域的热影响区域在非裂纹敏感的温度范围内，该非裂纹敏感温度范围高于延展性下降温度范围 该合金被焊接。 在焊接过程中，焊接区域和热影响区域的温度主要由焊接设备的热量输入控制。 一旦焊接已经终止，焊接区域和热影响区域将从非裂纹敏感温度范围通过延性降低温度范围冷却至低于合金的延展性温度范围的温度。

    FILLER METAL CHEMISTRY FOR IMPROVED WELDABILITY OF SUPER ALLOYS
    9.
    发明申请
    FILLER METAL CHEMISTRY FOR IMPROVED WELDABILITY OF SUPER ALLOYS 审中-公开
    用于改善超合金焊接性的填充金属化学

    公开(公告)号：US20130048700A1

    公开(公告)日：2013-02-28

    申请号：US13219993

    申请日：2011-08-29

    申请人： Yan Cui ,  Srikanth Chandrudu Kottilingam ,  Dechao Lin ,  Brian Lee Tollison

    发明人： Yan Cui ,  Srikanth Chandrudu Kottilingam ,  Dechao Lin ,  Brian Lee Tollison

    IPC分类号： B23K31/00 ,  C22C30/00 ,  C22C19/05

    CPC分类号： C22C19/057 ,  B23K35/3033 ,  B23K35/304 ,  C22C19/056

    摘要： A filler metal chemistry includes an amount of chromium weight of between about 9.0% and about 16% by weight, an amount of cobalt of between about 7.0% and about 14% by weight, an amount of molybdenum of between about 10% and about 20% by weight, an amount of iron of between about 1.0% and about 5.0% by weight, an amount of aluminum of between about 0.05% and about 0.75% by weight, an amount of titanium of between about 0.5% and about 2.0% by weight, an amount of manganese not to exceed 0.8% by weight, an amount of carbon of between 0.02% and about 0.10% by weight, an amount of titanium+aluminum of between about 0.55% and 2.75% by weight, and an amount of nickel.

    摘要翻译： 填料金属化学性质包括约9.0％至约16％重量的铬重量，约7.0％至约14％重量的钴的量，约10％至约20％的钼量 重量％，铁的量为约1.0％至约5.0％重量，铝的量为约0.05％至约0.75％重量，钛的量为约0.5％至约2.0％之间，通过 重量，锰的量不超过0.8重量％，碳量在0.02重量％至约0.10重量％之间，钛+铝的量在约0.55重量％至2.75重量％之间， 镍。

    PROCESS AND APPARATUS FOR OVERLAY WELDING
    10.
    发明申请
    PROCESS AND APPARATUS FOR OVERLAY WELDING 审中-公开
    焊接过程和装置

    公开(公告)号：US20130086911A1

    公开(公告)日：2013-04-11

    申请号：US13253189

    申请日：2011-10-05

    申请人： Dechao Lin ,  Srikanth Chandrudu Kottilingam ,  Yan Cui ,  Ibrahim Ucok ,  Brian Lee Tollison

    发明人： Dechao Lin ,  Srikanth Chandrudu Kottilingam ,  Yan Cui ,  Ibrahim Ucok ,  Brian Lee Tollison

    IPC分类号： F02C7/22 ,  B23K9/04

    CPC分类号： B23K9/042 ,  F02C7/222 ,  F05D2230/232 ,  F05D2230/31 ,  F05D2230/80

    摘要： An apparatus and process for depositing an overlay weld on a substrate in a manner that reduces dilution of the substrate material. A consumable electrode is positioned in proximity to the surface of the substrate, and an electrical potential is applied between the electrode and substrate to generate an electrical arc therebetween. The arc melts the electrode and forms a molten spray that deposits on the substrate surface. Energy of the electric arc is absorbed to reduce the temperature at the substrate surface by feeding an additional filler material into the electric arc toward its center axis. The filler material continuously melts prior to reaching the center axis of the electric arc, and the electrode and filler materials are simultaneously deposited to form the overlay weld on the substrate. Sufficient energy is absorbed by the filler material to reduce intermixing between the overlay weld and the substrate.

    摘要翻译： 一种用于以减少衬底材料的稀释的方式在衬底上沉积覆盖焊缝的装置和工艺。 消耗性电极位于基板的表面附近，并且在电极和基板之间施加电势以在它们之间产生电弧。 电弧熔化电极并形成沉积在基板表面上的熔融喷雾。 吸收电弧的能量，以通过向其中心轴线向电弧供给附加的填充材料来降低衬底表面的温度。 填充材料在到达电弧的中心轴线之前连续熔融，同时沉积电极和填充材料，以在衬底上形成覆盖焊缝。 足够的能量被填充材料吸收，以减少覆盖焊缝和衬底之间的混合。