摘要:
Methods are provided for producing epoxidation catalysts. The present methods are able to produce catalysts having the desired loading levels of catalytic species at a lower vacuum level (having a higher minimum residual pressure) than previously appreciated by the art, thereby providing equipment cost and time savings.
摘要:
A plant and process for producing alkylene oxides to control the production of silver chloride on a high efficiency silver catalyst is disclosed and described. The process involves reacting an alkylene and an organic chloride gas phase promoter with oxygen over the high efficiency silver catalyst. The sulfur concentration in the alkylene oxide reactor feed is controlled to reduce the production of silver chloride which acts as a catalyst poison.
摘要:
The present invention provides rhenium-promoted epoxidation catalysts based upon shaped porous bodies comprising a minimized percentage of their total pore volume being present in pores having diameters of less than one micron, and a surface area of at least about 1.0 m2/g. Processes of making the catalysts and using them in epoxidation processes are also provided.
摘要:
A catalyst for the manufacture of alkylene oxide, for example ethylene oxide, by the vapor-phase epoxidation of alkene containing impregnated silver and at least one efficiency-enhancing promoter on an inert, refractory solid support, said support incorporating a sufficient amount of zirconium component (present and remaining substantially as zirconium silicate) as to enhance at least one of catalyst activity, efficiency and stability as compared to a similar catalyst which does not contain the zirconium component.
摘要:
A catalyst for the manufacture of alkylene oxide, for example ethylene oxide, by the vapor-phase epoxidation of alkene containing impregnated silver and at least one efficiency-enhancing promoter on an inert, refractory solid support, said support incorporating a sufficient amount of zirconium component (present and remaining substantially as zirconium silicate) as to enhance at least one of catalyst activity, efficiency and stability as compared to a similar catalyst which does not contain the zirconium component.
摘要:
A supported silver catalyst and use thereof in a process for producing an alkylene oxide, such as ethylene oxide, by the direct oxidation of an alkylene with oxygen or an oxygen-containing gas, wherein the catalyst provides improved stability and improved resilience to reactor upsets and timely recovery to substantially pre-upset levels of catalyst activity and/or efficiency. In some embodiments, the catalyst also exhibits improved activity. A catalyst capable of producing ethylene oxide at a selectivity of at least 87 percent while achieving a work rate of at least 184 kg/h/m3 at a temperature of no greater than 235° C. when operated in a process where the inlet feed to a reactor containing the catalyst comprises ethylene, oxygen, and carbon dioxide, wherein the concentration of carbon dioxide in the inlet feed is greater than or equal to 2 mole percent.
摘要:
A supported silver catalyst and use thereof in a process for producing an alkylene oxide, such as ethylene oxide, by the direct oxidation of an alkylene with oxygen or an oxygen-containing gas, wherein the catalyst provides improved stability and improved resilience to reactor upsets and timely recovery to substantially pre-upset levels of catalyst activity and/or efficiency. In some embodiments, the catalyst also exhibits improved activity. A catalyst capable of producing ethylene oxide at a selectivity of at least 87 percent while achieving a work rate of at least 184 kg/h/m3 at a temperature of no greater than 235° C. when operated in a process where the inlet feed to a reactor containing the catalyst comprises ethylene, oxygen, and carbon dioxide, wherein the concentration of carbon dioxide in the inlet feed is greater than or equal to 2 mole percent.
摘要:
A catalyst for the manufacture of alkylene oxide, for example ethylene oxide, by the vapor-phase epoxidation of alkene containing impregnated silver and at least one efficiency-enhancing promoter on an inert, refractory solid support, said support incorporating a sufficient amount of zirconium component (present and remaining substantially as zirconium silicate) as to enhance at least one of catalyst activity, efficiency and stability as compared to a similar catalyst which does not contain the zirconium component.
摘要:
A supported silver catalyst and use thereof in a process for producing an alkylene oxide, such as ethylene oxide, by the direct oxidation of an alkylene with oxygen or an oxygen-containing gas, wherein the catalyst provides improved stability and improved resilience to reactor upsets and timely recovery to substantially pre-upset levels of catalyst activity and/or efficiency. In some embodiments, the catalyst also exhibits improved activity. A catalyst capable of producing ethylene oxide at a selectivity of at least 87 percent while achieving a work rate of at least 184 kg/h/m3 at a temperature of no greater than 235° C. when operated in a process where the inlet feed to a reactor containing the catalyst comprises ethylene, oxygen, and carbon dioxide, wherein the concentration of carbon dioxide in the inlet feed is greater than or equal to 2 mole percent.
摘要翻译:负载型银催化剂及其在通过氧气或含氧气体直接氧化亚烷基的环氧乙烷生产方法中的用途,其中催化剂提供改进的稳定性和改善对反应器不稳定性的回弹性, 及时恢复,以大大预测催化剂活性和/或效率的水平。 在一些实施方案中,催化剂还表现出改进的活性。 能够以至少87%的选择性生产环氧乙烷的催化剂,同时在不高于235℃的温度下实现至少184kg / h / m3的工作速率,当在进料进料至 含有催化剂的反应器包括乙烯,氧气和二氧化碳,其中入口进料中二氧化碳的浓度大于或等于2摩尔%。
摘要:
A method of producing an alkylene oxide includes passing a reaction mixture comprising alkylene, oxygen and a gaseous chlorine-containing promoter species over a supported catalyst containing silver and a promoting amount of rhenium to undergo an epoxidation reaction at a first operating condition. The method further includes subsequently performing the epoxidation reaction at a preferred operating condition. The preferred operating condition is characterized by an efficiency of the epoxidation reaction toward the alkylene oxide where the efficiency is lower than that of a maximum efficiency achievable at an operating temperature corresponding to the preferred operating condition.