摘要:
A steel composition and method from making a dual phase steel therefrom. The dual phase steel may have carbon of about 0.05% by weight to about 0.12 wt %; niobium of about 0.005 wt % to about 0.03 wt %; titanium of about 0.005 wt % to about 0.02 wt %; nitrogen of about 0.001 wt % to about 0.01 wt %; silicon of about 0.01 wt % to about 0.5 wt %; manganese of about 0.5 wt % to about 2.0 wt %; and a total of molybdenum, chromium, vanadium and copper less than about 0.15 wt %. The steel may have a first phase consisting of ferrite and a second phase having one or more of carbide, pearlite, martensite, lower bainite, granular bainite, upper bainite, and degenerate upper bainite. A solute carbon content in the first phase may be about 0.01 wt % or less.
摘要:
A steel composition and method from making a dual phase steel therefrom. The dual phase steel may have carbon of about 0.05% by weight to about 0.12 wt %; niobium of about 0.005 wt % to about 0.03 wt %; titanium of about 0.005 wt % to about 0.02 wt %; nitrogen of about 0.001 wt % to about 0.01 wt %; silicon of about 0.01 wt % to about 0.5 wt %; manganese of about 0.5 wt % to about 2.0 wt %; and a total of molybdenum, chromium, vanadium and copper less than about 0.15 wt %. The steel may have a first phase consisting of ferrite and a second phase having one or more of carbide, pearlite, martensite, lower bainite, granular bainite, upper bainite, and degenerate upper bainite. A solute carbon content in the first phase may be about 0.01 wt % or less.
摘要:
A steel composition and method from making a dual phase steel therefrom. The dual phase steel may have carbon of about 0.05% by weight to about 0.12 wt %; niobium of about 0.005 wt % to about 0.03 wt %; titanium of about 0.005 wt % to about 0.02 wt %; nitrogen of about 0.001 wt % to about 0.01 wt %; silicon of about 0.01 wt % to about 0.5 wt %; manganese of about 0.5 wt % to about 2.0 wt %; and a total of molybdenum, chromium, vanadium and copper less than about 0.15 wt %. The steel may have a first phase consisting of ferrite and a second phase having one or more of carbide, pearlite, martensite, lower bainite, granular bainite, upper bainite, and degenerate upper bainite. A solute carbon content in the first phase may be about 0.01 wt % or less.
摘要:
Weld metals and methods for welding ferritic steels are provided. The weld metals have high strength and high ductile tearing resistance and are suitable for use in strain based pipelines. The weld metal contains retained austenite and has a cellular microstructure with cell walls containing lath martensite and cell interiors containing degenerate upper bainite. The weld metals are comprised of between 0.02 and 0.12 wt % carbon, between 7.50 and 14.50 wt % nickel, not greater than about 1.00 wt % manganese, not greater than about 0.30 wt % silicon, not greater than about 150 ppm oxygen, not greater than about 100 ppm sulfur, not greater than about 75 ppm phosphorus, and the balance essentially iron. Other elements may be added to enhance the properties of the weld metal. The weld metals are applied using a power source with current waveform control which produces a smooth, controlled welding arc and weld pool in the absence of CO2 or oxygen in the shielding gas.
摘要:
Weld metals and methods for welding ferritic steels are provided. The weld metals have high strength and high ductile tearing resistance and are suitable for use in strain based pipelines. The weld metals are comprised of between 0.03 and 0.08 wt % carbon, between 2.0 and 3.5 wt % nickel, not greater than about 2.0 wt % manganese, not greater than about 0.80 wt % molybdenum, not greater than about 0.70 wt % silicon, not greater than about 0.03 wt % aluminum, not greater than 0.02 wt % titanium, not greater than 0.04 wt % zirconium, between 100 and 225 ppm oxygen, not greater than about 100 ppm nitrogen, not greater than about 100 ppm sulfur, not greater than about 100 ppm phosphorus, and the balance essentially iron. The weld metals are applied using a power source with pulsed current waveform control with
摘要:
Weld metals and methods for welding ferritic steels are provided. The weld metals have high strength and high ductile tearing resistance and are suitable for use in strain based pipelines. The weld metal contains retained austenite and has a cellular microstructure with cell walls containing lath martensite and cell interiors containing degenerate upper bainite. The weld metals are comprised of between 0.02 and 0.12 wt % carbon, between 7.50 and 14.50 wt % nickel, not greater than about 1.00 wt % manganese, not greater than about 0.30 wt % silicon, not greater than about 150 ppm oxygen, not greater than about 100 ppm sulfur, not greater than about 75 ppm phosphorus, and the balance essentially iron. Other elements may be added to enhance the properties of the weld metal. The weld metals are applied using a power source with current waveform control which produces a smooth, controlled welding arc and weld pool in the absence of CO2 or oxygen in the shielding gas.
摘要:
Weld metals and methods for welding ferritic steels are provided. The weld metals have high strength and high ductile tearing resistance and are suitable for use in strain based pipelines. The weld metals are comprised of between 0.03 and 0.08 wt % carbon, between 2.0 and 3.5 wt % nickel, not greater than about 2.0 wt % manganese, not greater than about 0.80 wt % molybdenum, not greater than about 0.70 wt % silicon, not greater than about 0.03 wt % aluminum, not greater than 0.02 wt % titanium, not greater than 0.04 wt % zirconium, between 100 and 225 ppm oxygen, not greater than about 100 ppm nitrogen, not greater than about 100 ppm sulfur, not greater than about 100 ppm phosphorus, and the balance essentially iron. The weld metals are applied using a power source with pulsed current waveform control with
摘要:
Weld metals suitable for joining high strength, low alloy steels are provided. These weld metals have microstructures of acicular ferrite interspersed in a hard constituent, such as lath martensite, yield strengths of at least about 690 MPa (100 ksi), and DBTTs lower than about −50° C. (−58° F.) as measured by a Charpy energy versus temperature curve. These weld metals include about 0.04 wt % to about 0.08 wt % carbon; about 1.0 wt % to about 2.0 wt % manganese; about 0.2 wt % to about 0.7 wt % silicon; about 0.30 wt % to 0.80 wt % molybdenum; about 2.3 wt % to about 3.5 wt % nickel; about 0.0175 wt % to about 0.0400 wt % oxygen, and at least one additive selected from the group consisting of (i) up to about 0.04 wt % zirconium, and (ii) up to about 0.02 wt % titanium.
摘要:
Provided are coated sleeved oil and gas well production devices and methods of making and using such coated sleeved devices. In one form, the coated sleeved oil and gas well production device includes an oil and gas well production device including one or more bodies and one or more sleeves proximal to the outer or inner surface of the one or more bodies, and a coating on at least a portion of the inner sleeve surface, outer sleeve surface, or a combination thereof, wherein the coating is chosen from an amorphous alloy, a heat-treated electroless or electro plated based nickel-phosphorous composite with a phosphorous content greater than 12 wt %, graphite, MoS2, WS2, a fullerene based composite, a boride based cermet, a quasicrystalline material, a diamond based material, diamond-like-carbon (DLC), boron nitride, and combinations thereof. The coated sleeved oil and gas well production devices may provide for reduced friction, wear, erosion, corrosion, and deposits for well construction, completion and production of oil and gas.
摘要:
Provided are coated sleeved oil and gas well production devices and methods of making and using such coated sleeved devices. In one form, the coated sleeved oil and gas well production device includes an oil and gas well production device including one or more bodies and one or more sleeves proximal to the outer or inner surface of the one or more bodies, and a coating on at least a portion of the inner sleeve surface, outer sleeve surface, or a combination thereof, wherein the coating is chosen from an amorphous alloy, a heat-treated electroless or electro plated based nickel-phosphorous composite with a phosphorous content greater than 12 wt %, graphite, MoS2, WS2, a fullerene based composite, a boride based cermet, a quasicrystalline material, a diamond based material, diamond-like-carbon (DLC), boron nitride, and combinations thereof. The coated sleeved oil and gas well production devices may provide for reduced friction, wear, erosion, corrosion, and deposits for well construction, completion and production of oil and gas.