摘要:
The invention according to the present application provides a high strength solidification body by solidifying a starting metallic powder of iron and the like by means of plastic working using hydrostatic pressing, which is, for instance, a high strength high toughness steel material and the like having a superfine texture comprising a crystalline texture consisting of grains 5 &mgr;m or less in average diameter, or preferably, 3 &mgr;m or less in average diameter. Furthermore, the present invention provides a steel material included in the high strength solidification body, which contains oxide grain 0.2 &mgr;m or less in diameter at a volume ratio of from 0.5 to 60%.
摘要:
A high strength phosphorus-containing steel having fine texture free from the problem of embrittlement by positively using the presence of P, which is a carbon steel having an average ferritic grain diameter of 3 &mgr;m or less and containing from 0.04 to 0.1% by mass of P, wherein the volume fraction of P segregated in the grain boundary accounts for 0.3 or less in case the grain boundary is covered by a P layer 1 nm in thickness.
摘要:
A fine ferrite-based steel is disclosed, wherein at least 60% of the ferrite grain boundary is a large angle grain boundary of at least 15°, and the mean ferrite grain size is not more than 2.5 &mgr;m. The fine ferrite-based steel of the invention has a high strength and a long fatigue life.
摘要:
A method of producing a ultra fine grain steel made of ferrite having a mean grain size of not larger that 3 &mgr;m as the base phase, after ingoting raw materials, by austenitizing the ingot by heating it to a temperature of at least an Ac 3 point, then, applying compression working of a reduction ratio of at least 50% at a temperature of from an Ae 3 point or lower to an Ar 3 point −150° C., or at a temperature of at least 550° C., and thereafter, cooling, wherein the strain rate as compression working is in the range of from 0.001 to 10/second.
摘要:
The invention provides an ultra-fine grain steel comprising fine ferrite grains as oriented at random and surrounded by large angle grain boundaries. The steel comprises fine ferrite grains having a mean grain size of not larger and 3.0 &mgr;m and surrounded by large angle grain boundaries having an misorientation not smaller than 15°.
摘要:
There are provided a steel for warm working, to be subjected to warm working as various structures, components of cars, and the like, a warm working method thereof, and a steel material and a steel component obtainable from the warm working method.[Solving Means] A steel is to have a particle dispersion type fiber structure formed in the matrix by warm working. The steel is characterized in that the total amount of the dispersed second-phase particles at room temperature is 7×10−3 or more in terms of volume fraction, and the Vickers hardness (HV) is equal to or larger than the hardness H of the following equation (2): H=(5.2−1.2×10−4λ)×102 (2) when the steel is subjected to any of annealing, tempering, and aging treatments in the as-unworked state under conditions such that a parameter λ expressed by the following equation (1): λ=T(log t+20)(T; temperature(K), t; time(hr)) (1) is 1.4×104 or more in a prescribed temperature range of 350° C. or more and Ac1 point or less. This steel is taken as the steel for warm working.
摘要:
A tough high strength heavy wall steel material having superior weldability is provided, said steel material has a diameter or a side 5 mm or more in length, and comprises oxides 1 μm or less in particle diameter homogeneously dispersed at a dispersion density in a range of from 10,000 to 100,000 particles/mm2 and uniform ferrite grains 2 μm or less in grain diameter formed over the entire plane making a right angle with respect to the rolling direction.
摘要:
A tough high strength heavy wall steel material having superior weldability is provided, said steel material has a diameter or a side 5 mm or more in length, and comprises oxides 1 μm or less in particle diameter homogeneously dispersed at a dispersion density in a range of from 10,000 to 100,000 particles/mm2 and uniform ferrite grains 2 μm or less in grain diameter formed over the entire plane making a right angle with respect to the rolling direction.
摘要翻译:提供具有优良焊接性的坚韧的高强度重壁钢材料,所述钢材具有长度为5mm以上的直径或侧面,并且包括以分散密度均匀分散的1μm以下的氧化物,其分散密度范围为 10,000〜100,000个/ mm 2,在整个平面上形成的晶粒直径为2μm以下的均匀的铁素体相对于轧制方向成直角。
摘要:
A tough high strength heavy wall steel material having superior weldability is provided, said steel material has a diameter or a side 5 mm or more in length, and comprises oxides 1 μm or less in particle diameter homogeneously dispersed at a dispersion density in a range of from 10,000 to 100,000 particles/mm2 and uniform ferrite grains 2 μm or less in grain diameter formed over the entire plane making a right angle with respect to the rolling direction.
摘要:
In carbon steel, oxides with grain diameter of 1 .mu.m or less and with grain spacing of 6 .mu.m or less are dispersed to suppress growth of .gamma. grains by heating at .gamma. region temperature.