摘要:
A pneumatic tire having an air permeation prevention layer composed of a thin film of a resin composition including at least 20% by weight of a thermoplastic polyester elastomer comprised of a block copolymer of polybutylene terephthalate and polyoxyalkylene diimide diacid at a weight ratio of polybutylene terephthalate/polyoxyalkylene diimide diacid of 85/15 or less.
摘要:
A polymer composition for a tire having an air permeation coefficient of 25.times.10.sup.-12 cc.multidot.cm/cm.sup.2 .multidot.sec.multidot.cmHg (at 30.degree. C.) or less and a Young's modulus of 1 to 500 MPa, including (A) at least 10% by weight, based on the weight of the total polymer component, of at least one thermoplastic resin having an air permeation coefficient of not more than 25.times.10.sup.-12 cc.multidot.cm/cm.sup.2 .multidot.sec.multidot.cmHg (at 30.degree. C.) and a Young's modulus of more than 500 MPa and (B) at least 10% by weight, based on the total weight of the polymer component, of at least one elastomer component having an air permeation coefficient of more than 25.times.10.sup.-12 cc.multidot.cm/cm.sup.2 .multidot.sec.multidot.cmHg (at 30.degree. C.) and a Young's modulus of not more than 500 MPa, wherein the total amount (A)+(B) of the component (A) and the component (B) is not less than 30% by weight based on the weight of the total polymer component, and a pneumatic tire obtained therefrom.
摘要翻译:一种轮胎用聚合物组合物,其透气系数为25×10 12 cc×cm 2 / cm 2×sec×cm 3(30℃)以下,杨氏模量为1〜500MPa,包括(A)至少10重量% 至少一种热塑性树脂的透气系数不超过25×10-12 ccxcm / cm2×secxcmHg(30℃)和杨氏模量大于500MPa的聚合物组分的重量,(B) 至少10重量%,基于聚合物组分的总重量,至少一种具有大于25×10 12 cc×cm / cm 2·sec·x·cmHg(30℃)的透气系数的弹性体成分,杨氏模量不大 其中,组分(A)和组分(B)的总量(A)+(B)相对于总聚合物组分的重量为30重量%,得到的充气轮胎 由此。
摘要:
A polymer composition for a tire having an air permeation coefficient of 25×10−12 cc·cm/cm2·sec ·cmHg (at 30° C.) or less and a Young's modulus of 1 to 500 MPa, including (A) at least 10% by weight, based on the weight of the total polymer component, of at least one thermoplastic resin having an air permeation coefficient of not more than 25×10−12 cc·cm/cm2·sec·cmHg (at 30° C.) and a Young's modulus of more than 500 MPa and (B) at least 10% by weight, based on the total weight of the polymer component, of at least one elastomer component having an air permeation coefficient of more than 25×10−12 cc·cm/cm2·sec·cmHg (at 30° C.) and a Young's modulus of not more than 500 MPa, wherein the total amount (A)+(B) of the component (A) and the component (B) is not less than 30% by weight based on the weight of the total polymer component, and a pneumatic tire obtained therefrom.
摘要:
A thermoplastic polymer having a carbonyl-containing group and a nitrogen-containing 5-membered heterocycle-containing group in side chains, and a composition thereof. The thermoplastic polymer and composition thereof have excellent recycle property in that physical properties do not deteriorate even though formation of crosslinking and dissociation of crosslinking are repeatedly conducted with altering temperature. The thermoplastic polymer and composition thereof are that its crosslinked structure is considerably stable at room temperature, and therefore have considerably high tensile strength. In particular, in the case of bonding to a main chain at 3-position or 4-position of a nitrogen-containing 5-membered heterocycle, intermolecular hydrogen bond is caused, so that a cured product has high mechanical properties.
摘要:
A thermoplastic resin elastomer/rubber laminate comprising a rubber layer containing 100 parts by weight of a rubber and 0.1-20 parts by weight of an antioxidant preblended thereto and a thermoplastic resin elastomer composition layer, obtained by laminating at least two layers of the rubber layer and the thermoplastic resin elastomer composition layer followed by heating and pressing, whereby the antioxidant migrates from the rubber layer to the thermoplastic resin elastomer composition layer to improve the weathering resistance as well as a pneumatic tire using the same as an inner liner.
摘要:
A thermo-reversible, crosslinkable elastomer, a composition containing the same, a rubber-bonded body and a rubber structure containing the rubber-bonded body are disclosed. The thermo-reversible, crosslinkable elastomer has an elastomer main-chain and a crosslinkable portion having at least one group selected from the group consisting of acid anhydride group and hydroxyl group. The thermo-reversible, crosslinkable elastomer can form stable crosslinked structure at room temperature, thereby having rubber plasticity, show sufficient melt flowability at molding temperature of general thermoplastic resin, and repeatedly reproduce crosslinking formation and crosslinking dissociation.
摘要:
A thermoplastic resin elastomer/rubber laminate comprising a rubber layer containing 100 parts by weight of a rubber and 0.1-20 parts by weight of an antioxidant preblended thereto and a thermoplastic resin elastomer composition layer, obtained by laminating at least two layers of the rubber layer and the thermoplastic resin elastomer composition layer followed by heating and pressing, whereby the antioxidant migrates from the rubber layer to the thermoplastic resin elastomer composition layer to improve the weathering resistance as well as a pneumatic tire using the same as an inner liner.
摘要:
A composition useful as a sealant, coating, a potting agent for a printed circuit board, a prepreg or an adhesive comprises a compound (A) wherein all or a part of the oxirane rings in an epoxy compound is replaced with thiirane rings represented by the following formula (1): or compound (A) and compound (B) which contains oxirane rings and no thiirane ring in the molecule, wherein the ratio of oxirane ring/thiirane ring is from 90/10 to 10/90.
摘要:
An elastomer composition including an elastomer having a functional group, and a compound having a functional group, in which corresponding functional groups form a cross-link by at least one of an ionic bond, a hydrogen bond, and Diels-Alder reaction with temperatures, i.e., by heating, while the cross-link is cleaved at around room temperature, forming and cleaving of the cross-link being reversible.
摘要:
An organically modified layered clay ionically bonded with an organic compound having an ammonium group and an amino group, an organic polymer composition containing the same and an organic polymer capable of reacting with the amino group, and an inner liner using the same.