摘要:
This disclosure involves a new spinel and glass micro-composite material and process for making such. The composite has excellent transmission in the 0.5-5.0 μm wavelength region suitable for various visible and mid IR applications utilizing windows, domes and other geometric shapes. The composite can be made at a temperature about 40% lower than the glass melting temperature and about 50% lower than the spinel sintering temperature. The composite material has high modulus and fracture toughness which are important for impact resistance in armor and other practical applications.
摘要:
A method for synthesizing Cu(InxGa1-x)S2 and Cu(InxGa1-x)Se2 nanopowders using flame spray pyrolysis to form solar cell absorber materials. The flame spray product is the oxide nanoparticles of the absorber materials (copper indium gallium oxide). The oxide nanoparticles may be deposited directly onto glass substrates. The oxide nanoparticles are then sulfurdized or selenized with a post deposition anneal directly on the substrate to form the absorber layer for a solar cell device.
摘要翻译:使用火焰喷雾热解合成Cu(In x Ga 1-x)S2和Cu(In x Ga 1-x)Se 2纳米粉末以形成太阳能电池吸收材料的方法。 火焰喷涂产品是吸收材料(铜铟镓氧化物)的氧化物纳米颗粒。 氧化物纳米颗粒可以直接沉积到玻璃基底上。 然后将氧化物纳米颗粒直接在基板上进行后沉积退火硫化或硒化,形成太阳能电池器件的吸收层。
摘要:
A spinel ceramic made from the process comprising the steps of polishing one edge of a first spinel part to a surface roughness of less than 1 nm, polishing one edge of a second spinel part to a surface roughness of less than 1 nm, joining the polished edge of the first spinel part to the polished edge of the second spinel part, heating the first and second spinel parts to about 1000-1200° C., and maintaining said heating for about 3-6 hours resulting in bonded spinel parts.
摘要:
A laser apparatus uses a dysprosium doped chalcogenide glass fiber. The glass fiber has a laser pump operatively connected to it. The chalcogenide glass fiber is located in a laser cavity including one or more reflective elements such as a Bragg grating, a Bragg minor, a grating, and a non-doped fiber end face. The apparatus provides laser light output at a wavelength of about 4.3 μm to about 5.0 μm at a useful power level using laser light input at a wavelength of from about 1.7 μm to about 1.8 μm. Also disclosed is a method for providing laser light output at a wavelength of about 4.3 μm to about 5.0 μm using the apparatus of the invention.
摘要:
This invention pertains to a composite of AlON and a germanate glass, and to a process for bonding AlON to the glass. The composite includes AlON and glass bonded together and having transmission in the visible and mid-infrared wavelength region. The process includes the step of heating them together above the softening temperature of the glass, the composite having excellent, i.e., typically in excess of about 60%, transmission in the 0.4-5 wavelength region.
摘要:
A glass-ceramic article or composition which has better thermal and physical properties than the competing materials of zinc sulfide, spinel, or magnesium fluoride comprising 2-30 mole percent yttrium oxide and/or rare earth oxide, 25-80 mole percent germanium oxide, and 5-30 mole percent gallium oxide, based on the total moles of yttrium oxide and/or the rare earth oxide, germanium oxide, and gallium oxide; which article is over 80% by volume crystalline.
摘要:
A method for making a smooth ceramic including loading ceramic powder to be densified into a hot press die, placing one or more spacers with a polished surface between a hot press punch and the ceramic powder, placing the die and punch into a hot press and hot pressing the ceramic powder, and removing a smooth ceramic shape that requires no subsequent polishing or processing and has a surface roughness of 5 nm RMS or better. The smooth ceramic shape may be transparent, and it may be spinel, magnesia, yttria, lutetia, scandia, YAG, any composites thereof, or any of their rare earth doped compounds. Also disclosed is the related smooth ceramic made by this process.
摘要:
A transparent polycrystalline ceramic having scattering and absorption loss less than 0.2/cm over a region comprising more than 95% of the originally densified shape and a process for fabricating the same by hot pressing. The ceramic can be any suitable ceramic such as yttria (Y2O3) or scandia (Sc2O3) and can have a doping level of from 0 to 20% and a grain size of greater than 30 μm, although the grains can also be smaller than 30 μm. Ceramic nanoparticles can be coated with a sintering aid to minimize direct contact of adjacent ceramic powder particles and then baked at high temperatures to remove impurities from the coated particles. The thus-coated particles can then be densified by hot pressing into the final ceramic product. The invention further provides a transparent polycrystalline ceramic solid-state laser material and a laser using the hot pressed polycrystalline ceramic.
摘要:
This invention pertains to a process of bonding a magnesium aluminate spinel article or articles and a germanate glass article or articles including the step of heating them together above the softening temperature of the glass.