公开(公告)号：US20090253852A1

公开(公告)日：2009-10-08

申请号：US12327396

申请日：2008-12-03

申请人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Akira MAGARIO ,  Shigeki INUKAI ,  Masaei ITO ,  Takashi WANIBUCHI ,  Takushi MATSUSHITA ,  Tsuyoshi WATANABE

发明人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Akira MAGARIO ,  Shigeki INUKAI ,  Masaei ITO ,  Takashi WANIBUCHI ,  Takushi MATSUSHITA ,  Tsuyoshi WATANABE

IPC分类号： C08K3/04

CPC分类号： C09K3/1009 ,  B82Y30/00 ,  E21B33/1208

摘要： A heat-resistant seal material includes 100 parts by weight of a ternary fluoroelastomer, 1 to 30 parts by weight of vapor-grown carbon fibers having an average diameter of more than 30 nm and 200 nm or less, and carbon black having an average particle diameter of 25 to 500 nm. The heat-resistant seal material contains the vapor-grown carbon fibers and the carbon black in an amount of 20 to 40 parts by weight in total. The heat-resistant seal material has a compression set when subjected to a compression set test at a compression rate of 25% and a temperature of 200° C. for 70 hours of 0 to 15% and a dynamic modulus of elasticity at 200° C. (E′/200° C.) of 30 to 100 MPa.

摘要翻译： 耐热密封材料包括100重量份的三元含氟弹性体，1至30重量份的平均直径大于30nm和200nm或更小的气相生长碳纤维，以及具有平均颗粒的炭黑 直径为25〜500nm。 耐热密封材料总共包含20至40重量份的气相生长碳纤维和炭黑。 当以25％的压缩率和200℃的温度进行压缩变形试验时，耐热密封材料具有0至15％的70小时和200℃的动态弹性模量的压缩永久变形 （E'/ 200℃）为30〜100MPa。

公开(公告)号：US20110156355A1

公开(公告)日：2011-06-30

申请号：US12647898

申请日：2009-12-28

申请人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Masaei ITO ,  Raghu MADHAVAN ,  Morinobu ENDO ,  Satoshi IINOU

发明人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Masaei ITO ,  Raghu MADHAVAN ,  Morinobu ENDO ,  Satoshi IINOU

IPC分类号： E21B33/10 ,  E21B33/00 ,  C08K3/04 ,  C08K3/36 ,  C08K3/34

CPC分类号： C08K7/06 ,  C08K2201/011 ,  C08L15/005

摘要： A seal member includes a hydrogenated acrylonitrile-butadiene rubber (HNBR) and carbon nanofibers. The seal member has a number of cycles to fracture of 7000 or more when subjected to a tensile fatigue test at a temperature of 70° C., a maximum tensile stress of 4 N/mm, and a frequency of 1 Hz. The seal member exhibits excellent abrasion resistance.

摘要翻译： 密封件包括氢化丙烯腈 - 丁二烯橡胶（HNBR）和碳纳米纤维。 当在70℃的温度，4N / mm的最大拉伸应力和1Hz的频率下进行拉伸疲劳试验时，密封构件具有7000以上的断裂的循环次数。 密封件表现出优异的耐磨性。

公开(公告)号：US20110156357A1

公开(公告)日：2011-06-30

申请号：US12647948

申请日：2009-12-28

申请人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Masaei ITO ,  Raghu MADHAVAN ,  Morinobu ENDO ,  Satoshi IINOU

发明人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Masaei ITO ,  Raghu MADHAVAN ,  Morinobu ENDO ,  Satoshi IINOU

IPC分类号： E21B33/10 ,  E21B33/00 ,  B32B5/00 ,  B32B5/16

CPC分类号： F16J15/3284 ,  C09K3/1009 ,  C09K2200/0208 ,  C09K2200/0282 ,  F04C2/1075 ,  F04C13/008 ,  F05C2225/00 ,  F05C2253/04 ,  Y10T428/249921 ,  Y10T428/25 ,  Y10T428/256 ,  Y10T428/259

摘要： A dynamic seal member includes a ternary fluoroelastomer (FKM) and carbon nanofibers. The carbon nanofibers are carbon nanofibers having an average diameter of 10 to 20 nm, or carbon nanofibers having an average diameter of 60 to 110 nm and subjected to a low-temperature heat treatment. The carbon nanofibers having an average diameter of 60 to 110 nm and subjected to the low-temperature heat treatment have a ratio (D/G) of a peak intensity D at around 1300 cm−1 to a peak intensity G at around 1600 cm−1 measured by Raman scattering spectroscopy of more than 0.9 and less than 1.6. The dynamic seal member has a number of cycles to fracture of 10 or more when subjected to a tension fatigue test at a temperature of 200° C., a maximum tensile stress of 2.5 N/mm, and a frequency of 1 Hz. The dynamic seal member exhibits excellent heat resistance and abrasion resistance.

摘要翻译： 动态密封件包括三元含氟弹性体（FKM）和碳纳米纤维。 碳纳米纤维是平均直径为10〜20nm的碳纳米纤维，平均直径为60〜110nm的碳纳米纤维，进行低温热处理。 平均直径为60〜110nm并进行低温热处理的碳纳米纤维具有1300cm -1左右的峰强度D与1600cm -1附近的峰值强度G的比（D / G） 1通过拉曼散射光谱测量，大于0.9且小于1.6。 当在200℃的温度，2.5N / mm的最大拉伸应力和1Hz的频率下进行拉伸疲劳试验时，动态密封构件具有10个以上的断裂的循环次数。 动态密封件表现出优异的耐热性和耐磨性。

公开(公告)号：US20110156356A1

公开(公告)日：2011-06-30

申请号：US12647943

申请日：2009-12-28

申请人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Masaei ITO ,  Raghu MADHAVAN ,  Morinobu ENDO ,  Satoshi IINOU

发明人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Masaei ITO ,  Raghu MADHAVAN ,  Morinobu ENDO ,  Satoshi IINOU

IPC分类号： E21B33/10 ,  E21B33/00 ,  C08K3/04

CPC分类号： E21B33/10 ,  B82Y30/00 ,  C08J5/005 ,  C08J2327/18 ,  C09K3/1009 ,  F01C1/107 ,  F01C13/00 ,  F01C19/005 ,  F01C19/125 ,  F04C2/1075 ,  F04C13/008

摘要： The seal member includes a tetrafluoroethylene-propylene copolymer (FEPM) and carbon nanofibers. The seal member has a number of cycles to fracture of 10 or more when subjected to a tension fatigue test at a temperature of 150° C., a maximum tensile stress of 2 N/mm, and a frequency of 1 Hz. The seal member exhibits excellent heat resistance and abrasion resistance.

摘要翻译： 密封件包括四氟乙烯 - 丙烯共聚物（FEPM）和碳纳米纤维。 当在150℃的温度，2N / mm的最大拉伸应力和1Hz的频率下进行拉伸疲劳试验时，密封构件具有10个以上的断裂的循环次数。 密封件表现出优异的耐热性和耐磨性。

公开(公告)号：US20110160375A1

公开(公告)日：2011-06-30

申请号：US12648040

申请日：2009-12-28

申请人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Satoshi IINOU ,  Masaei ITO

发明人： Toru NOGUCHI ,  Hiroyuki UEKI ,  Shigeki INUKAI ,  Satoshi IINOU ,  Masaei ITO

IPC分类号： C08K3/04

CPC分类号： H01B3/47 ,  C08K3/04 ,  C08K2201/011

摘要： A carbon fiber composite material comprising 100 parts by mass of an elastomer, and 20 to 100 parts by mass of carbon nanofibers that have been oxidized and reduced in number of branch points. The carbon fiber composite material has a dynamic modulus of elasticity (E′) at 200° C. and 10 Hz of 10 to 1000 MPa, and a volume resistivity of 106 to 1018 ohms·cm.

摘要翻译： 一种碳纤维复合材料，其包含100质量份的弹性体，和20〜100质量份已经被氧化并且分支点数减少的碳纳米纤维。 碳纤维复合材料在200℃下的动态弹性模量（E'）和10〜1000MPa的10Hz，体积电阻率为106〜1018欧姆·厘米。