公开(公告)号：US5759951A

公开(公告)日：1998-06-02

申请号：US696387

申请日：1995-11-21

申请人： Yusheng Zhao ,  Jiahuan Wang ,  Zhiwu Wang ,  Xilai Liu ,  Jingchun Shao ,  Xiaojing Chen ,  Wei Li ,  Shaowu Wang

发明人： Yusheng Zhao ,  Jiahuan Wang ,  Zhiwu Wang ,  Xilai Liu ,  Jingchun Shao ,  Xiaojing Chen ,  Wei Li ,  Shaowu Wang

IPC分类号： B01J23/04 ,  B01J21/02 ,  B01J23/24 ,  B01J23/74 ,  B01J23/85 ,  B01J27/055 ,  B01J27/12 ,  B01J27/14 ,  B01J27/16 ,  B01J27/18 ,  B01J27/185 ,  B01J27/19 ,  B01J35/10 ,  C10G45/04 ,  C10G45/06 ,  C10G45/08

CPC分类号： B01J21/02 ,  B01J23/24 ,  B01J23/74 ,  B01J23/85 ,  B01J27/16 ,  C10G45/08 ,  B01J35/1019 ,  B01J35/1038 ,  B01J35/1042 ,  B01J35/1047

摘要： Disclosed is a hydrogenation demetalization catalyst with a stabilized alkali metal, having a). an alumina carrier, b). 0.01-10.2% by weight of an alkali metal, c). 0-3.0% by weight of a Group VIB element, and d). 0-3.0% by weight of a Group VIII element of the periodic table of elements, with a pore volume of 0.4-1.3 ml/g, a surface area of 100-230 m.sup.2 /g, comprising a nonmetallic element selected from the group consisting of P, Si, B and F with the atomic ratio of said nonmetallic element to said alkali metal being 0.5-40.0. Also disclosed is a process for preparing the same.

摘要翻译： 公开了具有稳定的碱金属的氢化脱金属催化剂，其具有a）。 氧化铝载体，b）。 0.01-10.2重量％的碱金属，c）。 0-3.0重量％的VIB族元素，和d）。 0-3.0重量％的元素周期表第Ⅷ族元素，孔体积为0.4-1.3ml / g，表面积为100-230m2 / g，包含选自以下的非金属元素： 的P，Si，B和F，其中所述非金属元素与所述碱金属的原子比为0.5-40.0。 还公开了其制备方法。

公开(公告)号：US07060641B2

公开(公告)日：2006-06-13

申请号：US11110252

申请日：2005-04-19

申请人： Jiang Qian ,  Yusheng Zhao

发明人： Jiang Qian ,  Yusheng Zhao

IPC分类号： C04B35/577

CPC分类号： C04B35/645 ,  C04B35/52 ,  C04B35/6316 ,  C04B2235/3826 ,  C04B2235/427 ,  C04B2235/428 ,  C04B2235/5436 ,  C04B2235/6567 ,  C04B2235/77 ,  C04B2235/80 ,  C04B2235/96 ,  Y10T428/30

摘要： Fully dense, diamond-silicon carbide composites are prepared from ball-milled microcrystalline diamond/amorphous silicon powder mixture. The ball-milled powder is sintered (P=5–8 GPa, T=1400K–2300K) to form composites having high fracture toughness. A composite made at 5 GPa/1673K had a measured fracture toughness of 12 MPa·m1/2. By contrast, liquid infiltration of silicon into diamond powder at 5 GPa/1673K produces a composite with higher hardness but lower fracture toughness. X-ray diffraction patterns and Raman spectra indicate that amorphous silicon is partially transformed into nanocrystalline silicon at 5 GPa/873K, and nanocrystalline silicon carbide forms at higher temperatures.

摘要翻译： 由球磨微晶金刚石/非晶硅粉末混合物制备全密度的金刚石碳化硅复合材料。 将球磨粉末烧结（P = 5-8GPa，T = 1400K-2300K）以形成具有高断裂韧性的复合材料。 以5GPa / 1673K制成的复合材料具有12MPa.m 1/2的测得的断裂韧性。 相比之下，以5GPa / 1673K将硅浸入金刚石粉末中产生具有较高硬度但较低断裂韧性的复合材料。 X射线衍射图和拉曼光谱表明，非晶硅在5GPa / 873K下部分转变为纳米晶硅，在较高温度下形成纳米晶碳化硅。

公开(公告)号：US06759128B1

公开(公告)日：2004-07-06

申请号：US10190156

申请日：2002-07-05

申请人： Yusheng Zhao ,  Duanwei He

发明人： Yusheng Zhao ,  Duanwei He

IPC分类号： B32B900

CPC分类号： C04B35/645 ,  B82Y30/00 ,  C04B35/583 ,  C04B35/6261 ,  C04B35/62625 ,  C04B2235/386 ,  C04B2235/422 ,  C04B2235/425 ,  C04B2235/5454 ,  C04B2235/549 ,  C04B2235/656 ,  C04B2235/6567 ,  C04B2235/767 ,  C04B2235/781 ,  C04B2235/80 ,  C04B2235/85 ,  C04B2235/96 ,  C04B2235/9661 ,  Y10T428/30

摘要： Bulk, superhard, B-C-N nanocomposite compact and method for preparing thereof. The bulk, superhard, nanocomposite compact is a well-sintered compact and includes nanocrystalline grains of at least one high-pressure phase of B-C-N surrounded by amorphous diamond-like carbon grain boundaries. The bulk compact has a Vicker's hardness of about 41-68 GPa. It is prepared by ball milling a mixture of graphite and hexagonal boron nitride, encapsulating the ball-milled mixture, and sintering the encapsulated ball-milled mixture at a pressure of about 5-25 GPa and at a temperature of about 1000-2500 K.

摘要翻译： 散装，超硬，B-C-N纳米复合材料及其制备方法。 体积超硬的纳米复合材料是一种良好烧结的压块，包括由无定形类金刚石碳晶界包围的B-C-N的至少一个高压相的纳晶晶粒。 该批量紧凑件具有约41-68GPa的维氏硬度。 通过球磨研磨石墨和六方氮化硼的混合物，包封球磨的混合物，并在约5-25GPa的压力和约1000-2500K的温度下烧结封装的球磨混合物制备。

公开(公告)号：US20100237547A1

公开(公告)日：2010-09-23

申请号：US11529657

申请日：2006-09-27

申请人： Yusheng Zhao ,  Duanwei He

发明人： Yusheng Zhao ,  Duanwei He

IPC分类号： C04B35/563

CPC分类号： C04B35/583 ,  B82Y30/00 ,  C04B35/6261 ,  C04B35/62625 ,  C04B35/645 ,  C04B2235/386 ,  C04B2235/422 ,  C04B2235/425 ,  C04B2235/5454 ,  C04B2235/549 ,  C04B2235/656 ,  C04B2235/6567 ,  C04B2235/767 ,  C04B2235/781 ,  C04B2235/80 ,  C04B2235/85 ,  C04B2235/96 ,  C04B2235/9661

摘要： Bulk, superhard, B—C—N nanocomposite compacts were prepared by ball milling a mixture of graphite and hexagonal boron nitride, encapsulating the ball-milled mixture at a pressure in a range of from about 15 GPa to about 25 GPa, and sintering the pressurized encapsulated ball-milled mixture at a temperature in a range of from about 1800-2500 K. The product bulk, superhard, nanocomposite compacts were well sintered compacts with nanocrystalline grains of at least one high-pressure phase of B—C—N surrounded by amorphous diamond-like carbon grain boundaries. The bulk compacts had a measured Vicker's hardness in a range of from about 41 GPa to about 68 GPa.

摘要翻译： 通过球磨石墨和六方氮化硼的混合物制备块状，超硬，B-C-N纳米复合材料，将球磨的混合物在约15GPa至约25GPa的压力下包封，并烧结 加压密封的球磨混合物在约1800-2500K的温度范围内。产品本体，超硬纳米复合体是具有至少一个B-C-N高压相的纳晶晶粒的良好烧结体 通过无定形菱形碳晶界。 该批量压块具有在约41GPa至约68GPa范围内的测得的维氏硬度。

公开(公告)号：US06939506B2

公开(公告)日：2005-09-06

申请号：US10448672

申请日：2003-05-30

申请人： Jiang Qian ,  Yusheng Zhao

发明人： Jiang Qian ,  Yusheng Zhao

IPC分类号： B28B1/00 ,  B28B3/00 ,  B28B5/00 ,  C04B33/32 ,  C04B33/36 ,  C04B35/52 ,  C04B35/565 ,  C04B35/573 ,  C04B35/575 ,  C04B35/577 ,  C04B35/64 ,  C04B35/645

CPC分类号： C04B35/645 ,  C04B35/52 ,  C04B35/6316 ,  C04B2235/3826 ,  C04B2235/427 ,  C04B2235/428 ,  C04B2235/5436 ,  C04B2235/6567 ,  C04B2235/77 ,  C04B2235/80 ,  C04B2235/96 ,  Y10T428/30

摘要： Fully dense, diamond-silicon carbide composites are prepared from ball-milled microcrystalline diamond/amorphous silicon powder mixture. The ball-milled powder is sintered (P=5-8 GPa, T=1400K-2300K) to form composites having high fracture toughness. A composite made at 5 GPa/1673K had a measured fracture toughness of 12 MPa·m1/2. By contrast, liquid infiltration of silicon into diamond powder at 5 GPa/1673K produces a composite with higher hardness but lower fracture toughness. X-ray diffraction patterns and Raman spectra indicate that amorphous silicon is partially transformed into nanocrystalline silicon at 5 GPa/873K, and nanocrystalline silicon carbide forms at higher temperatures.

摘要翻译： 由球磨微晶金刚石/非晶硅粉末混合物制备全密度的金刚石碳化硅复合材料。 将球磨粉末烧结（P = 5-8GPa，T = 1400K-2300K）以形成具有高断裂韧性的复合材料。 以5GPa / 1673K制成的复合材料具有12MPa.m 1/2的测得的断裂韧性。 相比之下，以5GPa / 1673K将硅浸入金刚石粉末中产生具有较高硬度但较低断裂韧性的复合材料。 X射线衍射图和拉曼光谱表明，非晶硅在5GPa / 873K下部分转变为纳米晶硅，在较高温度下形成纳米晶碳化硅。

公开(公告)号：US20050209089A1

公开(公告)日：2005-09-22

申请号：US11110252

申请日：2005-04-19

申请人： Jiang Qian ,  Yusheng Zhao

发明人： Jiang Qian ,  Yusheng Zhao

IPC分类号： B28B1/00 ,  B28B3/00 ,  B28B5/00 ,  C04B33/32 ,  C04B33/36 ,  C04B35/52 ,  C04B35/565 ,  C04B35/573 ,  C04B35/575 ,  C04B35/577 ,  C04B35/64 ,  C04B35/645

CPC分类号： C04B35/645 ,  C04B35/52 ,  C04B35/6316 ,  C04B2235/3826 ,  C04B2235/427 ,  C04B2235/428 ,  C04B2235/5436 ,  C04B2235/6567 ,  C04B2235/77 ,  C04B2235/80 ,  C04B2235/96 ,  Y10T428/30

摘要： Fully dense, diamond-silicon carbide composites are prepared from ball-milled microcrystalline diamond/amorphous silicon powder mixture. The ball-milled powder is sintered (P=5-8 GPa, T=1400K-2300K) to form composites having high fracture toughness. A composite made at 5 GPa/1673K had a measured fracture toughness of 12 MPa.m1/2. By contrast, liquid infiltration of silicon into diamond powder at 5 GPa/1673K produces a composite with higher hardness but lower fracture toughness. X-ray diffraction patterns and Raman spectra indicate that amorphous silicon is partially transformed into nanocrystalline silicon at 5 GPa/873K, and nanocrystalline silicon carbide forms at higher temperatures.

摘要翻译： 由球磨微晶金刚石/非晶硅粉末混合物制备全密度的金刚石碳化硅复合材料。 将球磨粉末烧结（P = 5-8GPa，T = 1400K-2300K）以形成具有高断裂韧性的复合材料。 以5GPa / 1673K制成的复合材料具有12MPa.m 1/2的测得的断裂韧性。 相比之下，以5GPa / 1673K将硅浸入金刚石粉末中产生具有较高硬度但较低断裂韧性的复合材料。 X射线衍射图和拉曼光谱表明，非晶硅在5GPa / 873K下部分转变为纳米晶硅，在较高温度下形成纳米晶碳化硅。

公开(公告)号：US07371907B2

公开(公告)日：2008-05-13

申请号：US10886229

申请日：2004-07-07

申请人： Konstantin Lokshin ,  Yusheng Zhao

发明人： Konstantin Lokshin ,  Yusheng Zhao

IPC分类号： F17C11/00 ,  C07C9/00

CPC分类号： C01B3/001 ,  Y02E60/324

摘要： The present invention includes a method for hydrogen clathrate hydrate synthesis. First, ice and hydrogen gas are supplied to a containment volume at a first temperature and a first pressure. Next, the containment volume is pressurized with hydrogen gas to a second higher pressure, where hydrogen clathrate hydrates are formed in the process.

摘要翻译： 本发明包括氢包合水合物合成方法。 首先，在第一温度和第一压力下将冰和氢气供应到容纳体积。 接下来，将容纳体积用氢气加压至第二较高压力，其中在该过程中形成氢包合物水合物。

公开(公告)号：US20060217258A1

公开(公告)日：2006-09-28

申请号：US11444649

申请日：2006-05-31

申请人： Yusheng Zhao

发明人： Yusheng Zhao

IPC分类号： C04B35/577

CPC分类号： C04B35/645 ,  C04B35/52 ,  C04B35/6316 ,  C04B2235/3826 ,  C04B2235/427 ,  C04B2235/428 ,  C04B2235/5436 ,  C04B2235/616 ,  C04B2235/656 ,  C04B2235/6567 ,  C04B2235/77 ,  C04B2235/80 ,  C04B2235/96

摘要： Uniformly dense, diamond-silicon carbide composites having high hardness, high fracture toughness, and high thermal stability are prepared by consolidating a powder mixture of diamond and amorphous silicon. A composite made at 5 GPa/1673K had a measured fracture toughness of 12 MPa·m1/2. By contrast, liquid infiltration of silicon into diamond powder at 5 GPa/1673K produces a composite with higher hardness but lower fracture toughness.

摘要翻译： 通过固结金刚石和非晶硅的粉末混合物制备具有高硬度，高断裂韧性和高热稳定性的均匀致密的金刚石 - 碳化硅复合材料。 以5GPa / 1673K制成的复合材料具有12MPa.m 1/2的测得的断裂韧性。 相比之下，以5GPa / 1673K将硅浸入金刚石粉末中产生具有较高硬度但较低断裂韧性的复合材料。

公开(公告)号：US20130202971A1

公开(公告)日：2013-08-08

申请号：US13833124

申请日：2013-03-15

申请人： Yusheng Zhao ,  Luc Lous Daemen

发明人： Yusheng Zhao ,  Luc Lous Daemen

IPC分类号： H01M10/0562 ,  H01G9/025

CPC分类号： H01M10/0562 ,  C01D15/00 ,  C01D15/04 ,  C01P2002/34 ,  C01P2002/72 ,  C01P2006/40 ,  H01G9/025 ,  H01G11/56 ,  H01M6/185 ,  H01M6/186 ,  H01M2300/0071 ,  Y02E60/13

摘要： Solid electrolyte antiperovskite compositions for batteries, capacitors, and other electrochemical devices have chemical formula Li3OA, Li(3-x)Mx/2OA, Li(3-x)Nx/3OA, or LiCOXzY(1-z), wherein M and N are divalent and trivalent metals respectively and wherein A is a halide or mixture of halides, and X and Y are halides.

摘要翻译： 用于电池，电容器和其他电化学装置的固体电解质抗钙钛矿组合物具有化学式Li 3 O，Li（3-x）Mx / 20A，Li（3-x）Nx / 30A或LiCOXzY（1-z），其中M和N 分别为二价和三价金属，其中A为卤化物或卤化物混合物，X和Y为卤化物。

公开(公告)号：US07959841B2

公开(公告)日：2011-06-14

申请号：US11444649

申请日：2006-05-31

申请人： Yusheng Zhao

发明人： Yusheng Zhao

IPC分类号： C04B35/577 ,  B28B1/00

CPC分类号： C04B35/645 ,  C04B35/52 ,  C04B35/6316 ,  C04B2235/3826 ,  C04B2235/427 ,  C04B2235/428 ,  C04B2235/5436 ,  C04B2235/616 ,  C04B2235/656 ,  C04B2235/6567 ,  C04B2235/77 ,  C04B2235/80 ,  C04B2235/96

摘要： Uniformly dense, diamond-silicon carbide composites having high hardness, high fracture toughness, and high thermal stability are prepared by consolidating a powder mixture of diamond and amorphous silicon. A composite made at 5 GPa/1673K had a measured fracture toughness of 12 MPa·m1/2. By contrast, liquid infiltration of silicon into diamond powder at 5 GPa/1673K produces a composite with higher hardness but lower fracture toughness.

摘要翻译： 通过固结金刚石和非晶硅的粉末混合物制备具有高硬度，高断裂韧性和高热稳定性的均匀致密的金刚石 - 碳化硅复合材料。 以5GPa / 1673K制成的复合材料的断裂韧性测定值为12MPa·m1 / 2。 相比之下，以5GPa / 1673K将硅浸入金刚石粉末中产生具有较高硬度但较低断裂韧性的复合材料。