摘要:
Disclosed is a method for preparing aqueous negatively charged tin oxide sols having substantially uniform particle size no greater than about 50 nm and preferably from about 5 to about 20 nm, the sols being characterized as being substantially free of any other reagents which may adversely affect contemplated usage as a catalyst.
摘要:
A process for preparing sols of urania composed of particles in the 60 to 1900 angstrom size range which comprises electrodialysizing a solution of a tetravalent salt of uranium in a multi-compartment cell wherein the compartments are separated by an ion exchange resin membrane.
摘要:
A METHOD FOR PREPARING STABLE URANIA-PLUTONIA SOLS WHICH EXHIBIT MINIMAL OXIDATION-REDUCTION BETWEEN THE TETRAVALENT IONIC SPECIES IS PROVIDED BY PREPARING A NITRATESTABILIZED POLYMERIC TETRAVALENT PLUTONIUM SOL BY ALCOHOL EXTRACTION OF A PLUTONIUM NITRATE SOLUTION, MIXING THE TETRAVALENT PLUTONIUM SOL WITH A CRYSTALLINE, NITRATESTABILIZED, TETRAVALENT URANIUM SOL AND THEREAFTER REMOVING NITRATE BY SOLVENT EXTRACTION.
摘要:
The present invention relates to a method for preparing an aqueous or hydro-alcoholic colloidal solution of metal chalcogenide amorphous nanoparticles notably of the Cu2ZnSnS4 (CZTS) type and to the obtained colloidal solution.The present invention also relates to a method for manufacturing a film of large-grain crystallized semi-conducting metal chalcogenide film notably of CZTS obtained from an aqueous or hydro-alcoholic colloidal solution according to the invention, said film being useful as an absorption layer deposited on a substrate applied in a solid photovoltaic device.
摘要:
The present invention relates to a method for preparing an aqueous or hydro-alcoholic colloidal solution of metal chalcogenide amorphous nanoparticles notably of the Cu2ZnSnS4 (CZTS) type and to the obtained colloidal solution.The present invention also relates to a method for manufacturing a film of large-grain crystallized semi-conducting metal chalcogenide film notably of CZTS obtained from an aqueous or hydro-alcoholic colloidal solution according to the invention, said film being useful as an absorption layer deposited on a substrate applied in a solid photovoltaic device.
摘要:
THE PRESENT INVENTION RELATES TO A METHOD FOR FORMING A STABLE, PREDOMINANTLY CRYSTALLINE SOL FROM AN ACID-DEFICIENT SOLUTION OF A HYDROUS METAL OXIDE IN WHICH THE METAL IS IN THE +4 OXIDATION STATE WHICH COMPRISES HEATING SAID SOLUTION TO A CRYSTALLIZING TEMPERATURE TO CAUSE AN INCREASE IN CONDUCTIVITY OF SAID SOLUTION, REMOVING ANION AT THE CRYSTALLIZING TEMPERATURE TO A CONDITION OF FURTHER ACID DIFICIENCY AT A RATE WHICH APPROXIMATES THE RATE OF RELEASE OF FREE ACID TO THE AQUEOUS PHASE OF THE RESULTANT SOL, AND THEN ADJUSTING THE ANION-TO-METAL RATIO OF THE SOL TO A DESIRED ANION-TO-METAL RATIO.