摘要:
A substitute for amino and phenolic resins is disclosed. It is used in the polycondensation of such resins based on formaldehyde for bonding water penetrable cellulosic particles. The substitute comprises an aqueous solution of(a) either at least one aldehyde together with at least one amide and/or together with at least one phenol, or a non-resinous condensation product of formaldehyde and urea, and(b) a sugar or a sugar derivative or their byproducts or a starch or its degradation products or a mixture thereof, and/or(c) a raw and/or treated lignosulfonate.This substitute also reduces the free formaldehyde of the resulting board without impairing the other properties thereof.
摘要:
A process for preparing a urea-formaldehyde base resin having a F/U molar ratio of 1.0:1-1.2:1, that is hydrolytically stable, which comprises adjusting a formaldehyde solution to a pH of 0.5-2.5, slowly charging urea to said formaldehyde solution while maintaining the temperature at 40.degree.-70.degree. C., neutralizing the reaction mixture after obtaining a Gardner viscosity in the range of T+-V+, then adding the final charge of urea and permitting equilibration.
摘要:
A cationic adsorption agent which is obtained by reaction of(a) an amino compound which contains at least one amino group and at least one free or methylolated carboxamide group, with(b) an aminoplast precondensate which does not contain amino groups.The novel adsorption agent is suitable in particular for removing anionic substances, such as acid dyes or reactive dyes, from aqueous solutions, especially from wastewaters.
摘要:
Polymer compositions comprising hemiacetals of acrolein-isocyanuric acid adducts and polyfunctional compounds containing hemiacetal-reactive groups such as amines, amides, alcohols, thiols and oxiranes. The compositions are useful in molding, laminating, coating and adhesive applications.
摘要:
A textile finishing composition comprises a water dispersible urethane prepolymer and a water soluble methylol compound, a glyoxalamide adduct, or bis(.beta.-hydroxyethyl) sulfone.
摘要:
An aldehyde condensation copolymer is disclosed which is formed by co-condensingA. 90% - 10% by weight of an essentially linear non-crosslinkable aldehyde condensation prepolymer withB. 10% - 90% by weight of a highly thermosettable and crosslinkable aldehyde condensation prepolymer.
摘要:
Described herein are resin products having particular utility as rapid curing adhesives for wood and other materials, and processes for making the resin compositions. The products are made by reacting aldehude condensation polymer containing reactive alkylol groups, such as a phenol-formaldehyde condensation polymer, with di-substitued bis-aryl amine having the formula:
WHERE R and R'' are alkoxy, amino, hydrogen, hydroxyl, nitro, carboxyl or C1 to C4 alkyl AND X is
to obtain an amine-modified polymer. When the resulting reaction product is blended with an appropriate curing agent, such as an aldehyde, the compositions cure very rapidly at ambient temperature. When pieces of wood or other materials are spread with the preferred adhesives employing the resin compositions of this invention and brought into contact with another wood surface the bond strength develops within minutes. The durability, strength and flexibility of the adhesives of this invention under adverse weathering conditions are excellent.
摘要:
METHOD OF PRODUCING TRANSPARENT AND COLORED RESINOUS FILM BY DIFFERENTIAL POLYMERIZATION OF COMPOITIONS OF POLYMERIZABLE MONOMERS AND POLYMERS FROM WATER-SOLUBLE AND SOLVENT SOULUBLE MATERIALS PROVIDING POLYMERS DERIVED FROM THE CONDENSATION OR COMBINED ADDITION AND CONDENSATION REACTION OF (A) A FORMALDEHYDE MATERIAL, (B) A PHOTOSENSITVE AMIDE OF AN OLEFINIC CARBOXYLIC ACID OR THE PHOTOSENSITVE DERIVATIVES THEREOF, AND (C) A CYANAMIDE DERIVATIVE AS A MEMBER OF THE GOUP CONSISTING OF THIOUREA, UREA, GUANIDINE AND MELAMINE, DERIVATIVES, AND MIXTURES THEREOF, WITH OR WITHOUT (D) THE SOLUBLE MONO AND POLYVALENT SALTS AND SALT REAGENTS USEFUL IN PHOTOSENSITIVITY, WHICH COMPOSITIONS AND POLYMERS ARE PHOTOPOLYMERIZABLE IN THE PRESENCE OF A LIGHT ACTIVATED CATALYST TO PRODUCE PHOTOPOLYMER MASSES BY ADDITION POLYMERIZATION AND SIMULTANEOUSLY THEREWITH OR BEFORE OR AFTER CONDENSATION POLYMERS ARE FORMED.
摘要:
A PROCESS FOR MANUFACTURING AMINOPLAST RESIN-MODIFIED STARCH PASTE, WHICH COMPRISES HOMOGNEEOUSLY MIXING STARCH, AN AMINO COMPOUND AND FORMALDELYDE IN THE PRESENCE OF WATER UNDER A PH OF 4 TO 7 AT 15 TO 95*C. FOR 0.5 TO 3 HOURS, ADDING ALKALI TO THE SYSTEM TO TURN THE PH THEREOF TO 8.0 TO 10.0, AND THEN HEATING THE SYSTEM AT 50 TO 90*C. TO EFFECT THE CONDEENSATION REACTION OF THE STARCH, AMINO COMPOUND AND FORMALDEHYDE.