摘要:
Continuous gas-phase polymerization process for preparing ethylene and propene homopolymers and copolymers, in which ethylene, propene or mixtures comprising ethylene or propene and C3-C8-α-monoolefins are polymerized in the polymerization zone of a gas-phase polymerization reactor at from 30 to 125° C. and pressures of from 1 to 100 bar in the gas phase in a bed comprising finely divided polymer in the presence of a catalyst. To remove the heat of polymerization, the reactor gas is circulated and firstly passes through a cyclone after leaving the reactor. To prevent polymer deposits in the circulating gas system, a catalyst poison having a boiling point above the maximum temperature within the circulating gas system is fed into this circulating gas system at a position between the reactor and the cyclone.
摘要:
Gas-phase fluidized-bed reactor for polymerizing ethylenically unsaturated monomers, comprising a reactor chamber (1) in the form of a vertical tube, if desired a calming zone (2) following the upper section of the reactor chamber, a circulation gas line (3), a circulation gas compressor (4) and a cooling device (5), where, in the region of transition of the reaction gas from the circulation gas line into the reactor chamber and in the lower section of the reactor chamber itself, there is either no gas distributor plate at all or only a gas distributor plate the total surface area of whose gas orifices is more than 20% of the total surface area of said gas distributor plate.
摘要:
A process for preparing polyethylene which comprises ethylene homopolymers and/or copolymers of ethylene with 1-alkenes and has a molar mass distribution width Mw/Mn of from 5 to 30, a density of from 0.92 to 0.955 g/cm3, a weight average molar mass Mw of from 50000 g/mol to 500 000 g/mol and has from 0.01 to 20 branches/1000 carbon atoms and a z-average molar mass Mz of less than 1 million g/mol.
摘要:
Catalysts suitable for preparation of a polyethylene which comprises ethylene homopolymers and/or copolymers of ethylene with 1-alkenes and has a molar mass distribution width Mw/Mn of from 5 to 30, a density of from 0.92 to 0.955 g/cm3, a weight average molar mass Mw of from 50000 g/mol to 500 000 g/mol and has from 0.01 to 20 branches/1000 carbon atoms and a z-average molar mass Mz of less than 1 million g/mol.
摘要:
Polyethylene which comprises ethylene homopolymers and/or copolymers of ethylene with 1-alkenes and has a molar mass distribution width Mw/Mn of from 3 to 30, a density of from 0.945 to 0.965 g/cm3, a weight average molar mass Mw of from 50 000 g/mol to 200 000 g/mol, a HLMI of from 10 to 300 g/10 min and has from 0.1 to 15 branches/1000 carbon atoms, wherein the 1 to 15% by weight of the polyethylene having the highest molar masses have a degree of branching of more than 1 branch of side chains larger than CH3/1000 carbon atoms, a process for its preparation, catalysts suitable for its preparation and also injection moldings in which this polyethylene is present.
摘要翻译:聚乙烯,其包含乙烯均聚物和/或乙烯与1-烯烃的共聚物,其摩尔质量分布宽度Mw / Mn为3至30,密度为0.945至0.965g / cm 3,重均摩尔质量Mw为 50 000 g / mol至200 000 g / mol,HLMI为10至300 g / 10 min,具有0.1至15个支链/ 1000个碳原子,其中1至15重量%的具有最高摩尔数的聚乙烯 质量具有大于1分支的大于CH 3/1000碳原子的侧链的分支程度,其制备方法,适用于其制备的催化剂以及其中存在该聚乙烯的注射成型品。
摘要:
Method of preparing olefin polymers, which comprises the polymerization of at least one α-olefin in the presence of a hybrid catalyst to produce a polymer comprising at least a higher molecular weight polymer component and a lower molecular weight polymer component in the presence of water in an amount of from 2 to 100 mol ppm and/or carbon dioxide in an amount of from 2 to 100 mol ppm, in each case based on the total reaction mixture, in order to alter the ratio of the higher molecular weight polymer component to the lower molecular weight polymer component. This enables the ratio of the higher molecular weight component to the lower molecular weight component to be controlled selectively.
摘要:
Method of preparing olefin polymers, which comprises the polymerization of at least one α-olefin in the presence of a hybrid catalyst to produce a polymer comprising at least a higher molecular weight polymer component and a lower molecular weight polymer component in the presence of water in an amount of from 2 to 100 mol ppm and/or carbon dioxide in an amount of from 2 to 100 mol ppm, in each case based on the total reaction mixture, in order to alter the ratio of the higher molecular weight polymer component to the lower molecular weight polymer component. This enables the ratio of the higher molecular weight component to the lower molecular weight component to be controlled selectively.
摘要:
Catalysts suitable for preparation of a polyethylene which comprises ethylene homopolymers and/or copolymers of ethylene with 1-alkenes and has a molar mass distribution width Mw/Mn of from 5 to 30, a density of from 0.92 to 0.955 g/cm3, a weight average molar mass Mw of from 50000 g/mol to 500 000 g/mol and has from 0.01 to 20 branches/1000 carbon atoms and a z-average molar mass Mz of less than 1 million g/mol.
摘要:
A polyethylene which comprises ethylene homopolymers and/or copolymers of ethylene with 1-alkenes and has a molar mass distribution width Mw/Mn of from 5 to 30, a density of from 0.92 to 0.955 g/cm3, a weight average molar mass Mw of from 50000 g/mol to 500 000 g/mol and has from 0.01 to 20 branches/1000 carbon atoms and a z-average molar mass Mz of less than 1 million g/mol, a process for its preparation, catalysts suitable for its preparation and also films in which this polyethylene is present.
摘要:
Molding composition comprising polyethylene and having a density in the range from 0.915 to 0.955 g/cm, an MI in the range from 0 to 3.5 g/10 min, an MFR in the range from 5 to 50, a polydispersity Mw/Mn in the range from 5 to 20, and a z-average moiar mass Mz of less than 1 million g/mol, a process for preparing such a composition, a catalyst suitable for the preparation of the same, as well as films comprising this molding composition.