摘要:
Continuous gas-phase polymerization process for preparing ethylene and propene homopolymers and copolymers, in which ethylene, propene or mixtures comprising ethylene or propene and C3-C8-α-monoolefins are polymerized in the polymerization zone of a gas-phase polymerization reactor at from 30 to 125° C. and pressures of from 1 to 100 bar in the gas phase in a bed comprising finely divided polymer in the presence of a catalyst. To remove the heat of polymerization, the reactor gas is circulated and firstly passes through a cyclone after leaving the reactor. To prevent polymer deposits in the circulating gas system, a catalyst poison having a boiling point above the maximum temperature within the circulating gas system is fed into this circulating gas system at a position between the reactor and the cyclone.
摘要:
In a continuous gas-phase polymerization process for preparing ethylene and propene homopolymers and copolymers, in which ethylene, propene or a mixture of ethylene or propene and C3-C8-&agr;-monoolefins is polymerized in the polymerization zone of a gas-phase polymerization reactor at from 30 to 125° C. and a pressure of from 1 to 100 bar in the gas phase in a bed of finely divided polymer in the presence of a catalyst, where the reactor gas is circulated to remove the heat of polymerization, polymer deposits in the circulating gas line are prevented by metering a catalyst poison having a boiling point above the maximum temperature within the circulating gas line into this circulating gas line in at most such an amount that it does not significantly impair the productivity of the catalyst in the reactor.
摘要:
A continuous vapor-phase fluidized-bed process for the preparation of ethylene homopolymers and copolymers having a density of from 0.87 to 0.97 g/cm3 in which ethylene or mixtures of ethylene and C3-C8 a-monoolefins are (co)polymerized in the presence of a supported chromium catalyst in the polymerization zone of a vapor-phase fluidized-bed reactor under pressures ranging from 1 to 100 bar and at temperatures ranging from 30° to 125° C. in the vapor phase in an agitated bed of bulk material comprising particulate polymer, the resultant heat of polymerization is removed by cooling the recirculated reactor gas and the resulting (co)polymer is removed from the vapor-phase fluidized-bed reactor, wherein, for the preparation of a (co)polymer of a specific density d, the (co)polymerization is carried out at a temperature which is in a range restricted by an upper envelope defined by equation I T H = 171 + 6 d ′ 0.84 - d ′ ( I ) and a lower envelope defined by equation II T L = 173 + 7.3 d ′ 0.837 - d ′ , ( II ) in which the variables have the following meanings: TH is the highest reaction temperature in ° C.; TL is the lowest reaction temperature in ° C.; d′ is the numerical value of the density d of the (co)polymer to be synthesized.
摘要:
A continuous vapor-phase fluidized-bed process for the preparation of ethylene homopolymers and copolymers having a density of from 0.87 to 0.97 g/cm3 in which ethylene or mixtures of ethylene and C3-C8 a-monoolefins are (co)polymerized in the presence of a supported chromium catalyst in the polymerization zone of a vapor-phase fluidized-bed reactor under pressures ranging from 1 to 100 bar and at temperatures ranging from 30° to 125° C. in the vapor phase in an agitated bed of bulk material comprising particulate polymer, the resultant heat of polymerization is removed by cooling the recirculated reactor gas and the resulting (co)polymer is removed from the vapor-phase fluidized-bed reactor, wherein, for the preparation of a (co)polymer of a specific density d, the (co)polymerization is carried out at a temperature which is in a range restricted by an upper envelope defined by equation I T H = 171 + 6 d ′ 0.84 - d ′ ( I ) and a lower envelope defined by equation II T L = 173 + 7.3 d ′ 0.837 - d ′ , ( II ) in which the variables have the following meanings: TH is the highest reaction temperature in ° C.; TL is the lowest reaction temperature in ° C.; d′ is the numerical value of the density d of the (co)polymer to be synthesized.
摘要:
A polyethylene composition, in particular suitable for the preparation of films, and a process for preparing the same are described. The polyethylene composition of the invention comprises from 50 to 89% by weight of a first polyethylene component comprising at least one multimodal polyethylene including a plurality of ethylene polymer fractions having distinct molecular weights and comonomer contents, at least one of said plurality of ethylene polymer fractions being prepared by the use of a single site catalyst, and from 50 to 11% by weight of a second polyethylene component comprising a low or medium density polyethylene.
摘要:
Method for metering polar, antistatically acting process auxiliaries into a polymerization reactor in which the process auxiliaries are present in solution in a nonpolar solvent, wherein the electrical conductivity of the solution is measured and the amount of the process auxiliary metered in is determined from the electrical conductivity.
摘要:
A polyethylene composition, in particular suitable for the preparation of films, and a process for preparing the same are described. The polyethylene composition of the invention comprises from 50 to 89% by weight of a first polyethylene component comprising at least one multimodal polyethylene including a plurality of ethylene polymer fractions having distinct molecular weights and comonomer contents, at least one of said plurality of ethylene polymer fractions being prepared by the use of a single site catalyst, and from 50 to 11% by weight of a second polyethylene component comprising a low or medium density polyethylene.
摘要:
A polyethylene composition, in particular suitable for the preparation of films, and a process for preparing the same are described. The polyethylene composition of the invention comprises from 50 to 89% by weight of a first polyethylene component comprising at least one multimodal polyethylene including a plurality of ethylene polymer fractions having distinct molecular weights and comonomer contents, at least one of said plurality of ethylene polymer fractions being prepared by the use of a single site catalyst, and from 50 to 11% by weight of a second polyethylene component comprising a low or medium density polyethylene.