摘要:
Provided is a film for a film capacitor in which electrical insulation, and especially electrical properties at high temperatures are improved while a high dielectric constant of a vinylidene fluoride resin is maintained. The film for a film capacitor includes a tetrafluoroethylene resin (a1) that includes a vinylidene fluoride unit and a tetrafluoroethylene unit in the vinylidene fluoride unit/tetrafluoroethylene unit ratio (mol %) of 0/100 to 49/51 as a film-forming resin (A).
摘要:
The present invention provides an organosol composition that is stable even in the case that the PTFE particle content is high. The present invention relates to an organosol composition of PTFE particles, comprising PTFE particles (A), a polymer (B), and an organic solvent (S), wherein (1) the polymer (B) is soluble in the organic solvent (S), (2) the amount of the PTFE particles (A) is not lower than 50% by mass of the total amount of the PTFE particles (A) and the polymer (B), and (3) the precipitation ratio of the PTFE particles after 48 hours is not higher than 60% when the total solids concentration of the PTFE particles (A) and the polymer (B) is 5% by mass.
摘要:
The present invention provides a fluoropolymer capable of giving fluorine-containing molded materials and laminates excellent in moldability, productivity, interlaminar bonding and stress cracking resistance, in particular stress cracking resistance upon contacting with various liquid chemicals, without impairing such characteristics intrinsic in fluororesins as chemical resistance, solvent resistance, weathering resistance, antifouling properties, liquid chemical impermeability and nonstickiness. The present invention provides a fluoropolymer which is an oligomer-containing or oligomer-free fluoropolymer, wherein said oligomer has a molecular weight not higher than 10,000 and amounts to not more than 0.05% by mass relative to the fluoropolymer.
摘要:
It is an object of the present invention to provide a fluororesin composition which hardly causes molding defects even when high-speed molding is performed in covering extrusion molding within a relatively broad molding temperature range and which can give covered electric wires, in particular foamed electric wires, excellent in surface smoothness.A fluororesin composition comprising a polytetrafluoroethylene [PTFE] having a standard specific gravity of 2.15 to 2.30 and a tetrafluoroethylene/hexafluoropropylene-based copolymer [FEP], the content of said PTFE being 0.01 to 3 parts by mass per 100 parts by mass of said FEP and the alkali metal content being not higher than 5 ppm on the resin composition solid matter basis, wherein said composition is obtained by a method comprising the step (1) of obtaining a cocoagulated fluororesin powder by mixing an aqueous dispersion containing said FEP and an aqueous dispersion containing said PTFE together, followed by coagulation, the step (2) of melt extruding the cocoagulated powder and the step (3) of subjecting the extrusion product to treatment for stabilizing unstable terminal groups in said PTFE and FEP.
摘要:
A layer of a tetrafluoroethylene copolymer having 30 to 81% by mole of tetrafluoroethylene and 70 to 19% by mole of at least one other monomer and having a carbonate group in a polymer chain or at a polymer chain terminal, which has a melt flow rate of 0.1 to 100 g/10 minutes (230° C., 5 kg-load) and a melting point of 90 to 230° C. and a layer of a polyolefin resin are adhered with a layer of an ethylene-vinyl acetate copolymer, which satisfies the following relationship: X×Y/100≧7.0, wherein X is a vinyl acetate content (% by mole) and Y is a saponification degree of a methyl ester (%). The resulting laminate has high resistance to fuels, and the layer of the tetrafluoroethylene copolymer having a carbonate group and the layer of the polyolefin resin are firmly adhered.
摘要:
A tetrafluoroethylene copolymer comprising 30 to 81 mole % of tetrafluoroethylene and a 70 to 19 mole % of at least one other monomer, and having terminal carbonate groups at polymer chain ends, which has a melt flow rate of 0.1 to 100 g/10 min. at 200° C. under a load of 5 kg, and a melting point of 90 to 200° C. This copolymer can be firmly adhered directly to other materials such as general-purpose resins while maintaining the good properties of fluororesins such as chemical resistance, weather resistance, solvent resistance, non-tackiness, electrical insulation, stain-proofing properties, and flame retardance, molded at a lower temperature than conventional fluororesins, and heat bonded or co-extruded with general-purpose resins having low heat resistance.
摘要:
The resin composition of the present invention comprises (a) a fluorine-free resin, (b) a fluorine-containing resin, and (c) a polyfluoroalkyl group-containing polymer, has excellent impact strength, and repels a flux.
摘要:
The present invention provides a carrier comprising a core and a coating for developing electrostatic images, the core being formed from a specific polymer composition.
摘要:
This invention provides (i) novel hexafluoroneopentyl alcohol, (ii) its derivatives, i.e., hexafluoroneopentyl (meth)acrylate, (iii) fluorinated polymers comprising said acrylate as the monomer component, and (iv) optical materials comprising said fluorinated polymers.
摘要:
This invention provides a carrier for developing electrostatic images comprising a core and a coating on the core, the coating being formed from a copolymer comprising a fluoralkyl acrylate and a monomer copolymerizable therewith.