摘要:
The invention relates to a fire-resistant ceramic product, a batch for manufacturing a product of said type, and a process for manufacturing a product of said type.
摘要:
Provided is a dielectric ceramic composition including a first component and a second component, wherein the first component comprises an oxide of Ca of 0.00 mol % to 35.85 mol % an oxide of Sr of 0.00 mol % to 47.12 mol %, an oxide of Ba of 0.00 mol % to 51.22 mol %, an oxide of Ti of 0.00 mol % to 17.36 mol %, an oxide of Zr of 0.00 mol % to 17.36 mol %, an oxide of Sn of 0.00 mol % to 2.60 mol %, an oxide of Nb of 0.00 mol % to 35.32 mol %, an oxide of Ta of 0.00 mol % to 35.32 mol %, and an oxide of V of 0.00 mol % to 2.65 mol %, and the second component includes at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass and (b) an oxide of Cu and/or an oxide of Ru.
摘要:
A ceramic composition which can be used as a sintering aid includes 1-2 mol % of magnesium oxide (MgO), 5-15 mol % of aluminum oxide (Al2O3), 25-40 mol % of silicon dioxide (SiO2), 40-55 mol % of calcium oxide (CaO), 0.1-8 mol % of ferric oxide (Fe2O3), 0.1-2 mol % of sulfur trioxide (SO3) and 0.1-2 mol % of titanium oxide (TiO2). Alternatively, the ceramic composition includes 1-8 mol % of MgO, 5-15 mol % of Al2O3, 25-40 mol % of SiO2, 40-55 mol % of CaO, 0.1-8 mol % of Fe2O3, 0.1-2 mol % of SO3 and 0.9-2 mol % of TiO2.
摘要:
The present invention provides for a solid body composition that is able to withstand penetration and/or reaction with salts or salt compositions in one or more states of matter (solid, liquid, gas). The composition comprises at least one aggregate and at least one binder. The aggregate may be chosen based on its thermodynamic stability compared to a salt composition. The binder comprises a resol resin or a novolac resin, or a combination of one or more of a resol resin and one or more of a novolac resin. The resin binder sets to provide initial strength then is pyrolized to form a glassy carbon which acts as a barrier to a salt phase or phases of an industrial process.
摘要:
The invention relates to a process for making a ceramic body that comprises providing particles of a metal salt precursor material wetted by a liquid medium. The particles are characterized by a grain size of below 600 nm, and the precursor material has a solubility in the liquid medium of at least 10−5 mol/L. A pressure of ≥100 MPa is applied at a temperature of below 100° C., rendering a material of high theoretical density values previously unattainable at low temperatures. The invention further relates to a calcium carbonate ceramic material of the vaterite isomorph having a density of the material ≥1.76 g/cm3 and a Modulus of rupture ≥30 MPa, and to a calcium phosphate ceramic material consisting of the monetite isomorph with ≥2.5 g/cm3 density and a Modulus of rupture ≥18 MPa.
摘要:
A ceramic substrate is formed of a polycrystalline ceramic and has a supporting main surface. The supporting main surface has a roughness of 0.01 nm or more and 3.0 nm or less in terms of Sa. The number of projections and depressions with a height of 1 nm or more in a square region with 50 μm sides on the supporting main surface is less than 5 on average, and the number of projections and depressions with a height of 2 nm or more in the square region is less than 1 on average.