摘要:
A method of applying particles to a backing having a make layer on one of the backing's opposed major surfaces. The method including the steps of: supporting the particles on a feeding member having a feeding surface such that the particles settle into one or more layers on the feeding surface; the feeding surface and the backing being arranged in a non-parallel manner; and translating the particles from the feeding surface to the backing and attaching the particles to the make layer by an electrostatic force.
摘要:
Abrasive particles comprising shaped abrasive particles each having a sidewall, each of the shaped abrasive particles comprising alpha alumina and having a first face and a second face separated by a sidewall and having a maximum thickness, T; and the shaped abrasive particles further comprising a plurality of grooves on the second face.
摘要:
Abrasive particles comprising dish-shaped abrasive particles each having a sidewall; each of the shaped abrasive particles comprising alpha alumina and having a first face and a second face separated by a thickness, t; and wherein either the first face or the second face is recessed or concave.
摘要:
Precursor alpha alumina abrasive particles in a mold are subjected to a drying process that cracks or fractures at least a majority of the precursor abrasive particles into at least two pieces thereby producing abrasive shards having a smaller size than the mold cavity from which they were made. The smaller abrasive shards, once formed, could be reassembled like jigsaw puzzle pieces to reproduce the original cavity shape of the mold from which they were made. The cracking or fracturing of the precursor abrasive particles is believed to occur by ensuring that the surface tension of the abrasive dispersion to the walls of the mold is greater than the internal attractive forces of the abrasive dispersion as the abrasive dispersion is dried within the mold cavity.
摘要:
A method of making an abrasive article including the steps of treating a plurality of cavities in a contacting surface of a production tool by plasma deposition of a thin film thereby forming a plurality of plasma treated cavities. Filling the plurality of plasma treated cavities in the production tool with an abrasive slurry, and at least partially curing the abrasive slurry while residing in the plurality of cavities.
摘要:
An abrasive comprising shaped abrasive particles each with an opening. The shaped abrasive particles are formed from alpha alumina and have a first face and a second face separated by a thickness t. The opening in each of the shaped abrasive particles can improve grinding performance by reducing the size of a resulting wear flat, can provide a reservoir for grinding aid, and can improve adhesion to a backing in a coated abrasive article.
摘要:
Abrasive particles comprising dish-shaped abrasive particles each having a sidewall; each of the shaped abrasive particles comprising alpha alumina and having a first face and a second face separated by a thickness, t; and wherein either the first face or the second face is recessed or concave.
摘要:
A method for forming agglomerated powder particles whereby powder particles absorb energy pulses emanating from a high intensity light source, which causes particles to soften to produce agglomerated powder particles by inter-particle contact, reducing the amount of fines, and producing agglomerated powder particles of increased average particle size, having smooth surfaces and improved flow characteristics for bulk powders.
摘要:
A thermosettable resin composition is prepared by admixing a liquid mixture of thermosettable resins such as a polyepoxide and amorphous thermoplastic polymer particles such as a polyetherimide to form a homogeneous cured resin composition. The particles have an average diameter of from 0.5-50 micrometers, a surface area of at least 1.0 m.sup.2 /g, a dissolution temperature of at least 50.degree. C., and are essentially insoluble in the thermosettable resin at temperatures of up to 15.degree. C. below the dissolution temperature but are completely dissolved at a temperature of at least 20.degree. C. below the cure temperature of the resin.
摘要:
A method of making an abrasive article including the steps of treating a plurality of cavities in a contacting surface of a production tool by plasma deposition of a thin film thereby forming a plurality of plasma treated cavities. Filling the plurality of plasma treated cavities in the production tool with an abrasive slurry, and at least partially curing the abrasive slurry while residing in the plurality of cavities.