摘要:
An aqueous adhesive composition includes: a phenol/aldehyde resin; and an unsaturated elastomer latex. The phenol/aldehyde resin is based on at least: an aromatic polyaldehyde bearing at least two aldehyde functional groups and including at least one aromatic nucleus; and 2,2′,4,4′-tetrahydroxydiphenyl sulphide. The adhesive composition is useable to make a textile material adhere to a crosslinkable rubber composition, and may be used as an advantageous alternative to a formaldehyde-based RFL adhesive.
摘要:
The present invention provides a hot melt adhesive suitable for use in disposable products, which can be applied at a high speed and provides excellent in adhesion in a wet state and low-temperature coating, with little odor. The hot melt adhesive for disposable products comprises: (A) a propylene homopolymer having a melting point of 100° C. or lower obtained by polymerizing propylene using a metallocene catalyst; and (B) a wax modified with carboxylic acid and/or carboxylic acid anhydride. The wet adhesion of the hot melt adhesive is improved when the wax is modified with maleic acid and/or maleic anhydride.
摘要:
Adhesive tape consisting of a textile carrier and of an adhesive layer applied to at least one side of the carrier, the carrier being colored with a mixture of dyes and/or pigments,characterized in thatat least one of the dyes and/or one of the pigments is based on anthraquinone.
摘要:
An elastic laminate is made by first coextruding a film having an elastic outer film layer formed of a styrene-block copolymer and an inner film layer of lesser elasticity than the outer layer. An outer fleece web with an outer adhesive layer is then adhered to the outer film layer, and an inner fleece web with an inner adhesive layer is adhered to the inner film layer so as to form between the inner fleece web and the inner film layer a bond that is weaker than a bond formed by the outer adhesive layer between the outer fleece web and the outer film layer. Thereafter the coextruded film bonded by the inner and outer adhesive layers to the outer and inner fleece webs is prestretched such that the weak bond formed by the inner adhesive layer separates only locally from the inner film layer but the bond formed by the outer adhesive layer remains intact.
摘要:
The invention is directed to a joint tape for finishing a joint between boards comprising a nonwoven substrate that does not swell substantially in the presence of water. The invention further provides a method of finishing a joint between boards comprising (i) applying a joint tape of the invention to a joint between boards by embedding the joint tape in a first coat of joint compound, (ii) applying a second coat of joint compound over the tape, wherein step (ii) is carried out before the joint tape and joint compound applied in step (i) have substantially dried, and optionally (iii) applying a third fill or finish coat of joint compound over the tape, wherein step (iii) is carried out before the joint tape and second coat have substantially dried.
摘要:
The present invention relates to aqueous dispersions containing hydrophilized polycarbodiimides, methods for producing the aqueous dispersions according to the invention, their use as a constituent of binders in adhesives, lacquers, paints, paper coating compounds or in fiber nonwovens and articles made of wood, metal, textile, leather or plastic, which are treated with the aqueous dispersion according to the invention.
摘要:
An adhesive preparation comprising a stretchable support and an adhesive layer laminated on at least one side of the support, wherein the stretchable support comprises a interlock woven fabric subjected to crimping processing, the adhesive layer contains 10% by mass or more of methyl salicylate with respect to the total mass of the layer, the whole adhesive preparation has moisture permeability of 1 to 350 g/m2·24 hr measured at a temperature of 40° C. and a relative humidity of 90%, and the methyl salicylate has a plasma AUC0-24 ranging from 3.0 to 60.0 ng·hr/mL in terms of a mean±standard deviation, and salicylic acid as a metabolite of the methyl salicylate has a plasma AUC0-24 ranging from 5000 to 13000 ng·hr/mL in terms of a mean±standard deviation, when the adhesive preparation is applied to a human skin for 8 hours such that an application amount of the adhesive layer applied is 50 to 300 g/m2 and a contact area is 280 cm2.
摘要:
A cloth backing for an abrasive article is treated by combining a phenolic resin, a latex and a colloidal silicon oxide composition to prepare a colloidal formulation, which is then applied to the cloth backing and cured. Coated abrasive articles are formed by applying a make coat formulation to the treated cloth backing, applying an abrasive and then curing the make coat formulation.
摘要:
An adhesive preparation comprising a stretchable support and an adhesive layer laminated on at least one side of the support, wherein the stretchable support comprises a interlock woven fabric subjected to crimping processing, the adhesive layer contains 10% by mass or more of methyl salicylate with respect to the total mass of the layer, the whole adhesive preparation has moisture permeability of 1 to 350 g/m2·24 hr measured at a temperature of 40° C. and a relative humidity of 90%, and the methyl salicylate has a plasma AUC0-24 ranging from 3.0 to 60.0 ng·hr/mL in terms of a mean±standard deviation, and salicylic acid as a metabolite of the methyl salicylate has a plasma AUC0-24 ranging from 5000 to 13000 ng·hr/mL in terms of a mean±standard deviation, when the adhesive preparation is applied to a human skin for 8 hours such that an application amount of the adhesive layer applied is 50 to 300 g/m2 and a contact area is 280 cm2.
摘要翻译:一种粘合剂制剂,其包含层压在所述载体的至少一侧的可拉伸载体和粘合剂层,其中所述可拉伸载体包括进行压接加工的互锁织物,所述粘合剂层包含10质量%以上的水杨酸甲酯, 相对于该层的总质量,整个粘合剂在40℃,相对湿度90%的温度下测得的透湿度为1〜350g / m 2·24小时,水杨酸甲酯的血浆AUC 0 -24的范围为3.0〜60.0ng·hr / mL,以水杨酸甲酯为代表的水杨酸的血浆AUC 0-24为5000〜13000ng·hr / mL,以 当将粘合剂制剂施用于人类皮肤8小时,使得施加的粘合剂层的施用量为50至300g / m 2,接触面积为280cm 2时,其平均值为±标准偏差。
摘要:
The present invention provides a hot melt adhesive suitable for use in disposable products, which can be applied at a high speed and provides excellent in adhesion in a wet state and low-temperature coating, with little odor. The hot melt adhesive for disposable products comprises: (A) a propylene homopolymer having a melting point of 100° C. or lower obtained by polymerizing propylene using a metallocene catalyst; and (B) a wax modified with carboxylic acid and/or carboxylic acid anhydride. The wet adhesion of the hot melt adhesive is improved when the wax is modified with maleic acid and/or maleic anhydride.