摘要:
A material composition for producing a fireproof material having a fine-grain fraction with grain sizes of less than 100 μm and a coarse-grain fraction with grain sizes of more than 100 μm is provided. The fine-grain fraction includes aluminum oxide having a weight proportion of at least 90% by wt. in relation to the total weight of the fine-grain fraction, zirconium oxide having a weight proportion of up to 5% by wt. in relation to the total weight of the fine-grain fraction, a stabilizer for the zirconium oxide as well as titanium oxide powder having a weight proportion of up to 5% by wt. in relation to the total weight of the fine-grain fractional. The coarse-grain fraction represents a weight fraction of more than 30% by wt. of the material composition.
摘要:
A pressure casting slip for producing a refractory ceramic for use as a heat shield, e.g. in the hot gas path of gas turbine units, includes a particulate mixture of at least two materials having different coefficients of thermal expansion and also organic and/or inorganic binders and floating agents. The particulate mixture has a multimodal particle size distribution divided into 10-20 percent by weight of coarse particles in the size range 1-5 mm in diameter, 10-20 percent by weight of medium particles in the size range 0.5-1 mm in diameter and 60-80 percent by weight of fine particles in the size range up to 0.5 mm in diameter which together make up 100 percent by weight of the particle mixture.
摘要:
A method for producing a refractory molded boy using a material composition having a fine-grain fraction with grain sizes of less than 100 μm and a coarse-grain fraction with grain sizes of more than 100 μm. The method includes the steps of adding a dispersing agent and/or a liquefier to the material composition unless the material compositing already includes the dispersing agent and/or liquefier, forming the material composition into a molded body, and sintering the molded body at a temperature above 1300 degrees Celsius.
摘要:
A method for producing a refractory molded boy using a material composition having a fine-grain fraction with grain sizes of less than 100 μm and a coarse-grain fraction with grain sizes of more than 100 μm. The method includes the steps of adding a dispersing agent and/or a liquefier to the material composition unless the material compositing already includes the dispersing agent and/or liquefier, forming the material composition into a molded body, and sintering the molded body at a temperature above 1300 degrees Celsius.
摘要:
A pressure casting slip for producing a refractory ceramic for use as a heat shield, e.g. in the hot gas path of gas turbine units, includes a particulate mixture of at least two materials having different coefficients of thermal expansion and also organic and/or inorganic binders and floating agents. The particulate mixture has a multimodal particle size distribution divided into 10-20 percent by weight of coarse particles in the size range 1-5 mm in diameter, 10-20 percent by weight of medium particles in the size range 0.5-1 mm in diameter and 60-80 percent by weight of fine particles in the size range up to 0.5 mm in diameter which together make up 100 percent by weight of the particle mixture.
摘要:
A material composition for producing a fireproof material having a fine-grain fraction with grain sizes of less than 100 μm and a coarse-grain fraction with grain sizes of more than 100 μm is provided. The fine-grain fraction includes aluminum oxide having a weight proportion of at least 90% by wt. in relation to the total weight of the fine-grain fraction, zirconium oxide having a weight proportion of up to 5% by wt. in relation to the total weight of the fine-grain fraction, a stabilizer for the zirconium oxide as well as titanium oxide powder having a weight proportion of up to 5% by wt. in relation to the total weight of the fine-grain fractional. The coarse-grain fraction represents a weight fraction of more than 30% by wt. of the material composition.