公开(公告)号：US5317051A
公开(公告)日：1994-05-31
申请号：US890360
申请日：1992-05-22
申请人： Masahiro Harashige , Tsutomu Kawamura , Satoru Kaneko , Takashi Inoue , Atsuo Tokutake , Toshitsune Yoshikawa
发明人： Masahiro Harashige , Tsutomu Kawamura , Satoru Kaneko , Takashi Inoue , Atsuo Tokutake , Toshitsune Yoshikawa
CPC分类号： C08L23/0815 , C08K3/22 , C08K5/20 , C08L23/02 , C08L23/06 , C08L23/08 , C08L23/0853 , C08L23/0869 , C08L2201/02 , C08L2205/03 , C08L2205/035 , C08L2310/00 , C08L27/16 , C08L27/20 , C08L51/06 , C08L83/04 , C08L91/00 , C08L91/06
摘要： A flame-retardant olefin polymer composition superior in surface whitening preventing property is obtained by blending 100 parts by weight of a resin component consisting principally of:a) 99-60% by weight of a polyolefin resin andb) 1-40% by weight of an olefin polymer modified with an unsaturated carboxylic acid or a derivative thereof: withc) 5-200 parts by weight of a flame retardant: andd) at least one component selected from the group consisting of:1 a mineral oil, a wax, or a paraffin.2 a higher fatty acid or an ester, amide or metallic salt thereof,3 a silicone4 a partial fatty ester of a polyhydric alcohol or aliphatic alcohol-, fatty acid-, aliphatic amino-, fatty acid amide-, alkylphenol- or alkylnaphthol-ethylene oxide adduct, and5 a fluoric elastomer.
摘要翻译： PCT No.PCT / JP89 / 00853 Sec。 371日期1990年04月9日 102（e）1990年4月9日PCT PCT 1989年8月22日提交PCT公布。 WO90 / 02153 PCT出版物 日本1990年3月8日。具有优异的表面增白防止性能的阻燃烯烃聚合物组合物通过混合100重量份的树脂组分获得，该组分主要包括：a）99-60重量％的聚烯烃树脂和b ）1-40重量％的用不饱和羧酸或其衍生物改性的烯烃聚合物：c）5-200重量份的阻燃剂：和d）至少一种选自以下的组分： + E，crc / 1 / a矿物油，蜡或石蜡。 + E，crc / 2 / a高级脂肪酸或其酯，酰胺或金属盐，+ E，crc / 3 / a硅酮+ E，crc / 4 / a多元醇或脂族醇的部分脂肪酸酯， 脂肪酸 - 脂肪族氨基 - ，脂肪酸酰胺 - ，烷基酚 - 或烷基萘酚 - 环氧乙烷加合物和+ E，crc / 5 / a氟弹性体。
-
公开(公告)号：US5248729A
公开(公告)日：1993-09-28
申请号：US934184
申请日：1992-08-21
IPC分类号： C08F291/00 , C08K5/00 , C08K5/01 , C08L9/00 , C08L23/02
CPC分类号： C08L23/02 , C08F291/00 , C08K5/0025 , C08K5/01 , C08L23/06 , C08L23/12 , C08L25/06 , C08L23/16 , C08L53/02 , C08L9/00 , Y10S525/941
摘要： A thermoplastic resin composition is prepared by heat-treating a mixture of a thermoplastic resin substantially containing no olefinic unsaturated carbon-carbon bond and an elastomer having an olefinic unsaturated carbon-carbon bond, dynamically in the presence of a crosslinking agent, characterized in that as said elastomer there is used at least one member selected from the group consisting of styrene-butadiene-styrene block copolymer (SBS), styrene-isoprene-styrene block copolymer (SIS), 1,2-polybutadiene rubber and ethylene-propylene-diene random copolymer (EPDM), and that as said crosslinking agent there is used a dihydroaromatic compound or a polymer thereof.
摘要翻译： 通过在交联剂的存在下动态地热处理基本不含烯属不饱和碳 - 碳键的热塑性树脂和具有烯属不饱和碳 - 碳键的弹性体的混合物来制备热塑性树脂组合物，其特征在于，作为 所述弹性体使用选自苯乙烯 - 丁二烯 - 苯乙烯嵌段共聚物（SBS），苯乙烯 - 异戊二烯 - 苯乙烯嵌段共聚物（SIS），1,2-聚丁二烯橡胶和乙烯 - 丙烯 - 二烯烃随机的至少一种 共聚物（EPDM），作为所述交联剂使用二氢芳族化合物或其聚合物。
-
公开(公告)号：US4793956A
公开(公告)日：1988-12-27
申请号：US946074
申请日：1986-12-24
IPC分类号： C08J9/00 , B29C55/02 , B29K23/00 , B29K105/04 , B29L7/00 , C08J5/18 , C08K3/00 , C08L23/08 , B29C67/20
CPC分类号： C08J5/18 , C08K3/0033 , C08L23/0815 , C08J2323/04 , C08L2205/02
摘要： A process for preparing a porous film or sheet, which process comprises melt-forming a composition into a film or sheet and then stretching the thus-formed film or sheet at a temperature in the range of 30.degree. to 110.degree. C., said composition containing:(a) 30-90% by weight of a linear low-density polyethylene having a density not smaller than 0.910 g/cm.sup.3 and smaller than 0.940 g/cm.sup.3 ;(b) 10-70% by weight of an ethylene/.alpha.-olefin copolymer having a density not smaller than 0.860 g/cm.sup.3 and smaller than 0.910 g/cm.sup.3, a boiling n-hexane insolubles content not less than 10% by weight and a maximum peak temperature not lower than 100.degree. C. as measured according to a differential scanning calorimetry; and(c) 20-500 parts by weight of a filler based on 100 parts by weight of said resin components.
摘要翻译： 一种制备多孔膜或片的方法，该方法包括将组合物熔融成膜或片，然后在30℃至110℃的温度范围内拉伸如此形成的膜或片，所述组合物 含有：（a）30-90重量％的密度不小于0.910g / cm 3且小于0.940g / cm 3的线性低密度聚乙烯; （b）10-70重量％的密度不小于0.860g / cm 3且小于0.910g / cm 3的乙烯/α-烯烃共聚物，沸点正己烷不溶物含量不小于10重量％，和 根据差示扫描量热法测定的最高峰值温度不低于100℃; 和（c）基于100重量份所述树脂组分20-500重量份的填料。
-
公开(公告)号：US5159016A
公开(公告)日：1992-10-27
申请号：US290362
申请日：1988-12-27
IPC分类号： C08F291/00 , C08K5/00 , C08K5/01 , C08L9/00 , C08L23/02 , C08L23/06 , C08L23/08 , C08L23/10 , C08L23/16 , C08L53/02
CPC分类号： C08L25/06 , C08F291/00 , C08K5/0025 , C08K5/01 , C08L23/02 , C08L23/06 , C08L23/0815 , C08L23/10 , C08L23/12 , C08L23/16 , C08L9/00 , C08L53/02
摘要： A thermoplastic resin composition is prepared by heat-treating a mixture of a thermoplastic resin substantially containing no olefinic unsaturated carbon-carbon bond and an elastomer having an olefinic unsaturated carbon-carbon bond, dynamically in the presence of a crosslinking agent, characterized in that as said elastomer there is used at least one member selected from the group consisting of styrene-butadiene-styrene block copolymer (SBS), styrene-iosprene-styrene block copolymer (SIS), 1,2-polybutadiene rubber and ethylene-propylene-diene random copolymer (EPDM), and that as said crosslinking agent there is used a dihydroaromatic compound or a polymer thereof.
-
公开(公告)号：US5100937A
公开(公告)日：1992-03-31
申请号：US575554
申请日：1990-08-30
申请人： Junichi Kubo , Atsuo Tokutake , Toshitsune Yoshikawa , Osamu Kato
发明人： Junichi Kubo , Atsuo Tokutake , Toshitsune Yoshikawa , Osamu Kato
IPC分类号： C08K5/01
CPC分类号： C08K5/01
摘要： A thermoplastic resin composition comprising a thermoplastic resin (A) and a hydrogen donative material or Component (B) added in an amount of 0.01-40 weight parts per 100 weight parts resin (A), the hydrogen donative material having a transfer of hydrogen or at least 0.1 (hydrogen atoms/molecules anthracene). The composition further incorporates metal salts of aliphatic acid and/or hydrotalcites and a selected class of oxidation inhibitors.
-
-
-
-