摘要:
A photopolymerizable recording material for the preparation of relief plates comprises a base and a photopolymerizable layer, which layer contains, as the binder, a substantially linear, high molecular weight, thermoplastic diisocyanate-modified nylon which is solid at room temperature and which possesses quaternary and/or quaternizable nitrogen atoms and also possesses photopolymerizable double bonds in side branches.
摘要:
A photopolymerizable recording material for the production of relief plates comprises a photopolymerizable layer which can be developed in an alcoholic solution and contains a mixture of a photoinitiator, a photopolymerizable monomer and a linear, high molecular weight polyurethane which possesses activated double bonds in side branches, and is prepared using a polyether-diol from the group comprising the polyethylene glycols, propylene glycols and ethylene glycol/propylene glycol co-condensates.
摘要:
Described are tape-type magnetic recording media (I) including a non-magnetic substrate (III), at least one film applied to the substrate and, in at least one of these films, an inorganic acicular pigment (II) suitable for use as a supporting pigment, the ratio of the mean length to the mean diameter of the pigment (II) being at least 3 and the mean modulus of elasticity of the films being not less than 15 GPa in the longitudinal direction of the tape-type recording medium (I).
摘要:
Magnetic recording media consist of a nonmagnetic base and at least one matnetizable layer which is firmly applied thereon and is based on a magnetic material finely dispersed in a binder, consisting of not less than 50% by weight of a polyurethane, and further conventional additives, wherein the magnetizable layer also contains a saturated, branched hydrocarbon.
摘要:
Magnetic recording media consist of a nonmagnetic substrate and at least one magnetizable layer bonded thereon and based on a magnetic material dispersed in at least one polyurethane and one polyurethaneurea (meth)acrylate, the polyurethaneurea (meth)acrylate being obtained by reacting a hydroxyl-containing poly(meth)acrylate with a mixture of di- and polyisocyanates and converting the remaining NCO groups with ammonia or primary or secondary amines into urea groups.
摘要:
Magnetic recording media are obtained by preparing a dispersion of anisotropic magnetic material and additives in a solution of a polymeric binder in an organic solvent, applying the dispersion as a layer to a nonmagnetizable substrate, then orienting the anisotropic magnetic material in a magnetic field and solidifying the applied magnetic layer, and the magnetic layer contains water-repellent polysilica and, if required, a highly viscous polysiloxane.
摘要:
Magnetic recording media consist of a nonmagnetic substrate and at least one magnetizable layer which is firmly applied thereon and is based on a polyurethane binder, not less than 50% by weight of the binder consisting of a high molecular weight branched polyurethane elastomer having OH-containing urea groups at the chain ends, and the frictional properties of the binder being improved and its coefficient of friction reduced by incorporation of perfluoro groups.
摘要:
Magnetic recording media consist of a nonmagnetic substrate and at least one magnetizable layer which is applied firmly thereon and is based on a polyurethane binder, not less than 50% by weight of binder consisting of a branched polyurethane elastomer having urea groups at the chain ends.
摘要:
Magnetic recording media consist of a nonmagnetic substrate and at least one magnetizable layer which is firmly applied thereon and is based on a polyurethane binder which may be crosslinked with polyisocyanate, not less than 50% by weight of the binder consisting of a low molecular weight branched polyureaurethane having OH-containing urea groups at the chain ends, and the sliding properties of the said binder being improved and its coefficient of friction reduced by incorporation of siloxane groups.
摘要:
Magnetic recording media consist of a nonmagnetic substrate and one or more magnetizable layers which are firmly applied thereon and are based on a magnetic material which is finely dispersed in a polymer binder and further conventional additives and essentially consists of ferromagnetic chromium dioxide, and the said recording media are particularly stable to the chemical decomposition due to moisture and oxidizable compounds and hence to deterioration in the magnetic properties, owing to the addition of from 0.1 to 8% by weight of an organic compound from the group consisting of the antioxidants, based on the amount of chromium dioxide, to the magnetic layer.