Halogen-free flameproofed thermoplastic molding material
    2.
    发明授权
    Halogen-free flameproofed thermoplastic molding material 失效
    无卤阻燃热塑性成型材料

    公开(公告)号:US4632946A

    公开(公告)日:1986-12-30

    申请号:US692620

    申请日:1985-01-18

    CPC分类号: C08K5/0066 C08L101/00

    摘要: A halogen-free flameproofed thermoplastic molding material consists of a halogen-free thermoplastic resin (A) and one or more further halogen-free components.The thermoplastic resin (A) is present in an amount of from 30 to 90% by weight, based on the molding material. The latter contains, as further components, from 1 to 50% by weight of a phenol/aldehyde resin (B), from 1 to 50% by weight of a nitrogen-containing organic compound (C) and from 3 to 50% by weight of a phosphorus-containing organic compound (D), the percentages in each case being based on the molding material.The molding material is used for the production of flameproofed moldings.

    摘要翻译: 无卤阻燃热塑性成型材料由无卤素热塑性树脂(A)和一种或多种其它无卤素组分组成。 基于成型材料,热塑性树脂(A)的存在量为30〜90重量%。 后者含有1至50重量%的酚/醛树脂(B),1至50重量%的含氮有机化合物(C)和3至50重量% 的含磷有机化合物(D),每种情况下的百分比基于成型材料。 成型材料用于生产防火模制品。

    Flameproofed thermoplastic molding material comprising a novolak resin
    3.
    发明授权
    Flameproofed thermoplastic molding material comprising a novolak resin 失效
    包含酚醛清漆树脂的防火热塑性成型材料

    公开(公告)号:US4618636A

    公开(公告)日:1986-10-21

    申请号:US692621

    申请日:1985-01-18

    CPC分类号: C08K13/02 C08L25/00 C08L61/04

    摘要: A flameproofed thermoplastic molding material consists ofA. a thermoplastic resin containing a vinylaromatic monomerand furthermore containsB. from 0 to 100 parts by weight of an elastomer having a glass transition temperature Tg 0.degree. C., as an impact modifier,C. from 2 to 50 parts by weight of a halogen-containing organic compound (flameproofing agent),D. from 0.5 to 20 parts by weight of a compound containing a metal or non-metal (synergistic agent) andE. from 5 to 50 parts by weight of a novolak (phenol/aldehyde resin).The novolak is obtained from an aldehyde of the formula (I)R.sup.1 --CHO (I)where R.sup.1 is H, C.sub.1 -C.sub.10 -alkyl, cycloalkyl, C.sub.6 -C.sub.12 -aryl or .omega.-aryl-C.sub.1 -C.sub.3 -alkyl, and a mixture of phenols, and this mixture contains two or more monosubstituted phenols and the substituents can be alkyl of 1 to 8 carbon atoms or CN.The molding material is used for the production of flameproofed moldings.

    摘要翻译: 一种防火热塑性成型材料由A.含有乙烯基芳族单体的热塑性树脂组成,并且还含有0-100重量份玻璃化转变温度Tg 0℃的弹性体,作为抗冲改性剂的C.来自 2至50重量份的含卤素的有机化合物(防火剂),D。0.5至20重量份的含有金属或非金属的化合物(增效剂)和E。5至50份 酚醛清漆(苯酚/醛树脂)的重量。 酚醛清漆得自式(Ⅰ)R1-CHO(Ⅰ)的醛,其中R1是H,C1-C10-烷基,环烷基,C6-C12-芳基或ω-芳基-C1-C3-烷基,和 酚的混合物,并且该混合物含有两个或更多个单取代的酚,并且取代基可以是1至8个碳原子的烷基或CN。 成型材料用于生产防火模制品。

    Process for the preparation of noncellular polyurethane elastomers based
on 4,4-diisocyanato-1,2-diphenylethane
    7.
    发明授权
    Process for the preparation of noncellular polyurethane elastomers based on 4,4-diisocyanato-1,2-diphenylethane 失效
    用于制备基于4,4-二异氰酸根合-1,2-二苯基乙烷的非细胞聚氨酯弹性体的方法

    公开(公告)号:US4448946A

    公开(公告)日:1984-05-15

    申请号:US418717

    申请日:1982-09-16

    IPC分类号: C08G18/76

    CPC分类号: C08G18/7671

    摘要: The invention relates to a process for the manufacture of noncellular polyurethane elastomers by reacting 4,4'-diisocyanato-1,2-diphenylethane or diisocyanato-1,2-diphenylethane isomer mixtures with a 4,4'-diisocyanato-1,2-diphenylethane content in excess of 95 percent by weight, higher molecular weight polyhydroxyl compounds and low molecular weight chain extenders optionally in the presence of auxiliaries and additives.The polyurethane elastomers produced in accordance with this invention excel by a greater hardness and improved mechanical properties compared with polyurethane elastomers based on 4,4'-diphenylmethane diisocyanate with otherwise comparable composition.

    摘要翻译: 本发明涉及一种通过使4,4'-二异氰酸酯基-1,2-二苯基乙烷或二异氰酸酯基-1,2-二苯基乙烷异构体混合物与4,4'-二异氰酸酯基-1,2-二苯基乙烷异构体混合物反应制备非细胞聚氨酯弹性体的方法, 二苯基乙烷含量超过95重量%,较高分子量的多羟基化合物和低分子量扩链剂,任选在助剂和添加剂的存在下。 与基于4,4'-二苯基甲烷二异氰酸酯的聚氨酯弹性体相比,根据本发明生产的聚氨酯弹性体具有更大的硬度和更好的机械性能。

    Process for the preparation of cellular polyurethane elastomers based on
4,4'-diisocyanato-1,2-diphenylethane
    8.
    发明授权
    Process for the preparation of cellular polyurethane elastomers based on 4,4'-diisocyanato-1,2-diphenylethane 失效
    基于4,4'-二异氰酸根合-1,2-二苯基乙烷制备细胞聚氨酯弹性体的方法

    公开(公告)号:US4421870A

    公开(公告)日:1983-12-20

    申请号:US419755

    申请日:1982-09-20

    IPC分类号: C08G18/00 C08G18/76 C12P7/16

    摘要: The invention relates to a method for the preparation of cellular polyurethane elastomers with densities of approximately 250 to 800 grams per liter by reacting 4,4'-diisocyanato-1,2-diphenylethane or a diisocyanato-1,2-diphenylethane isomer mixture with a 4,4'-diisocyanato-1,2-diphenylethane content of more than 95 percent by weight with higher molecular weight polyhydroxyl compounds and water, as well as optionally chain extenders in the presence of auxiliaries and/or additives according to the one-shot or preferably the prepolymer method in closed molds.Compared with products based on 4,4'-diisocyanatodiphenylmethane, the polyurethane elastomer molded parts have improved physical and thermal properties.

    摘要翻译: 本发明涉及一种通过使4,4'-二异氰酸根合-1,2-二苯基乙烷或二异氰酸酯-1,2-二苯基乙烷异构体混合物与一种二异氰酸酯基-1,2-二苯基乙烷异构体混合物的混合物制备密度为约250至800克/升的多孔聚氨酯弹性体的方法, 与较高分子量的多羟基化合物和水相比,4,4'-二异氰酸酯基-1,2-二苯基乙烷含量大于95重量%,以及根据一次性助剂和/或添加剂存在下任选的增链剂 或优选在封闭模具中的预聚物方法。 与基于4,4'-二异氰酸基二苯基甲烷的产品相比,聚氨酯弹性体模塑部件具有改善的物理和热性能。

    Polyurethane-urea elastomers and their production
    9.
    发明授权
    Polyurethane-urea elastomers and their production 失效
    聚氨酯 - 尿素弹性体及其生产

    公开(公告)号:US4208507A

    公开(公告)日:1980-06-17

    申请号:US922317

    申请日:1978-07-06

    IPC分类号: C08G18/10 C08G18/75 C08G18/32

    CPC分类号: C08G18/75 C08G18/10

    摘要: Polyurethane-urea elastomers with improved temperature characteristics, in particular improved low temperature properties, good mechanical properties over a large temperature range and excellent resistance to hydrolysis, are obtained by reacting(A) a prepolymer, possessing cycloaliphatic NCO groups, which has been prepared from essentially difunctional polyhydroxy compounds and organic diisocyanates possessing at least one NCO group bonded to a cycloaliphatic structure, these reactants being used so as to give a ratio of total hydroxyl: NCO groups of from 1:1.2 to 1:10, with(B) 3,3',5,5'-tetramethyl-4,4'-diamino-diphenylmethane, A and B being reacted in the molar ratio of from 1:0.8 to 1:1.2.

    摘要翻译: 通过使(A)具有环脂族NCO基团的预聚物(其由以下制备)制备的具有改进的温度特性,特别是改进的低温性能,在大温度范围内的良好机械性能和优异的抗水解性的聚氨酯 - 脲弹性体 基本上是双官能多羟基化合物和具有至少一个与脂环族结构键合的NCO基团的有机二异氰酸酯,使用这些反应物,以使总羟基:NCO基团的比例为1:1.2至1:10,与(B)3 ,3',5,5'-四甲基-4,4'-二氨基 - 二苯基甲烷,A和B的摩尔比为1:0.8至1:1.2。

    Process for producing photo-cured printing plates possessing a defined
hardness
    10.
    发明授权
    Process for producing photo-cured printing plates possessing a defined hardness 失效
    制造具有规定硬度的光固化印版的方法

    公开(公告)号:US4606994A

    公开(公告)日:1986-08-19

    申请号:US726286

    申请日:1985-04-23

    IPC分类号: G03F7/16 G03C7/00

    CPC分类号: G03F7/168

    摘要: Photocured layers possessing a defined controllable hardness are produced by exposing a layer of a photopolymerizable or photocrosslinkable mixture, which contains a partially crystalline polymeric binder possessing olefinic double bonds capable of undergoing polymerization, to actinic light, by a method in which the photocurable layer, prior to exposure to actinic light, is subjected to a heat treatment in which the partially crystalline parts of the polymeric binder are partially or completely fused.

    摘要翻译: 具有确定的可控硬度的光固化层通过将可光聚合或可光交联的混合物层(其含有具有能够进行聚合的具有烯属双键的部分结晶聚合物粘合剂)暴露于光化学光,通过以下方法曝光:光可固化层,先前 曝光于光化性光,经受热处理,其中聚合物粘合剂的部分结晶部分部分或完全熔合。