摘要:
Disclosed are architectural compositions, including aqueous paint and stain compositions, that utilized copolymers including bio-based cross-linking monomers and their synthetic analogues that are comparable to copolymers including DAAM cross-linking monomers. The bio-based cross-linking monomers are preferably synthetic version of the bio-based cross-linking monomers.
摘要:
The architectural compositions, such as paints and stains, include an additive comprising a plurality of latex particles added to an existing mixture of opacifying pigments and a film-forming binder as an admixture. Each latex particle is made from a latex polymer copolymerized with a polymerizable surfactant. The latex polymer is a non-film forming polymer at ambient temperatures.
摘要:
The present invention relates to storage stable film forming latex particles that crosslink under ambient conditions during or after drying. Monomers for the formation of the crosslinkable moieties in the latex particles include diacetone acrylamide (DAAM) or the likes and methacrylamide (MAM) or the likes with or without styrene. A paint composition comprising the storage stable latex particles that may include a small amount or crosslinking agent such as adipic acid dihydrazide (ADH) in the aqueous phase is also described.
摘要:
The present invention relates to storage stable film forming latex particles substantially free of adipic acid dihydrazide (ADH) that crosslink under ambient conditions during or after drying. Monomers for the formation of the crosslinkable moieties in the latex particles include diacetone acrylamide (DAAM) or the likes and methacrylamide (MAM) or the likes with or without styrene. A paint composition comprising the storage stable latex particles was described.
摘要:
The present invention relates to a grafted pigment dispersing polymeric additive for opacifying pigments, prepared by polymerizing monomers in the presence of a polymeric pigment dispersant. The polymeric pigment dispersant has low molecular weight, high acid number and is dissolvable in alkali solution. When incorporated into paint compositions, hiding is improved with less opacifying pigments.
摘要:
Disclosed herein is an aqueous architectural composition forming a paint film on a substrate capable of resisting hydrophobic and hydrophilic stains. The architectural composition includes a film forming latex resin, a high molecular weight silicone resin, and a wax microsphere. The stain resistant architectural composition may also include at least one organic extender pigment, a fluorosurfactant and a phosphate monomer.
摘要:
The present invention relates to latex compositions comprising hydroxyethyl cellulose grafted acrylic polymer emulsions and methods for preparing same without gelling or coagulation. The latex composition comprises at least about 0.2% of HEC by weight relative to the monomer weight, contains at least about 45% solid, and the average mean volume (mV) latex particle size is in the range of about 320-about 850 nm. Paint compositions incorporating the HEC grafted acrylic latex show high viscosity at static conditions and have no color flow and no syneresis compared paints containing a latex without HEC grafting. The present invention also relates to a cross-linking mechanism that cross-links latex particles at ambient conditions. This cross-linking mechanism comprises diacetone acrylamide (DAAM) and methacrylamide (MAM) with or without styrene.
摘要:
The present invention relates to storage stable film forming latex particles substantially free of adipic acid dihydrazide (ADH) that crosslink under ambient conditions during or after drying. Monomers for the formation of the crosslinkable moieties in the latex particles include diacetone acrylamide (DAAM) or the likes and methacrylamide (MAM) or the likes with or without styrene. A paint composition comprising the storage stable latex particles was described.
摘要:
The present invention relates to latex compositions comprising hydroxyethyl cellulose grafted acrylic polymer emulsions and methods for preparing same without gelling or coagulation. The latex composition comprises at least about 0.2% of HEC by weight relative to the monomer weight, contains at least about 45% solid, and the average mean volume (mV) latex particle size is in the range of about 320-about 850 nm. Paint compositions incorporating the HEC grafted acrylic latex show high viscosity at static conditions and have no color flow and no syneresis compared paints containing a latex without HEC grafting. The present invention also relates to a cross-linking mechanism that cross-links latex particles at ambient conditions. This cross-linking mechanism comprises diacetone acrylamide (DAAM) and methacrylamide (MAM) with or without styrene.
摘要:
Disclosed herein is a frambinone methacrylate (FMA) or raspberry ketone methacrylate (RKMA) monomer having the following structure:
and
a zingerone methacrylate (ZMA) having the following structure
Also disclosed are homopolymers and co-polymers utilizing same monomer. Also disclosed is a class of methacrylate monomers comprising a bio-based moiety and a reactive ketone moiety. Also disclosed are paint compositions made with a copolymer including FMA and/or ZMA.