Disclosed are coating compositions comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having free and/or blocked isocyanate groups, and (c) at least one catalyst (D) for the crosslinking of silane groups, where (i) one or more constituents of the coating composition contain hydrolyzable silane groups and (iii) the coating composition can be finally cured to a coating which has statistically distributed regions of an Si—O—Si network. The finally cured coating obtained from the coating composition has a post-crosslinking index (PCI) of less than 2, wherein (PCI) is defined as the ratio of the storage modulus E′(200) at 200° C. to the minimum of the storage modulus E′(min) at a temperature above the measured glass transition temperature Tg.
摘要:
Disclosed are coating compositions comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having isocyanate groups, and (c) at least one catalyst (D) for the crosslinking of silane groups, said catalyst (D) comprising phosphorus. It is an aspect of the disclosed coating compositions that (i) one or more constituents of the coating composition contain hydrolyzable silane groups and (ii) the coating composition can be finally cured to a coating which has statistically distributed regions of an Si—O—Si network.
摘要:
Transparent coatings with a thickness of at least 30 μm, a relative elastic resilience to DIN 55676 of at least 70%, and a scratch resistance corresponding to a score of not more than 2 in the steel wool scratch test to DIN 1041 after 10 double strokes; process for producing them, and their use.
摘要:
Disclosed are coating compositions comprising (a) at least one hydroxyl-containing compound (A), (b) at least one compound (B) having isocyanate groups, and (c) at least one catalyst (D) for the crosslinking of silane groups, said catalyst (D) comprising phosphorus. It is an aspect of the disclosed coating compositions that (i) one or more constituents of the coating composition contain hydrolyzable silane groups and (ii) the coating composition can be finally cured to a coating which has statistically distributed regions of an Si—O—Si network.
摘要:
Disclosed herein is a silane-functional mixture, comprising at least one phosphonic diester (A), at least one diphosphonic diester (A), or at least one phosphonic diester and one diphosphonic diester (A), and at least one compound (B) comprising at least two condensable silane groups.
摘要:
Disclosed are coating compositions comprising at least one hydroxyl-containing compound (A) and at least one isocyanato-containing compound (B), wherein one or more of the constituents of the coating composition comprise between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (I) —N(X—SiR″x(OR′)3-x)n(X′—SiR″y(OR′)3-y)m (I) and between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (II) —Z—(X—SiR″x(OR′)3-x) (II).
摘要:
Autocatalyzed, thermally curable compositions free from external catalysts and comprising condensates of silanes which contain at least one of hydrolyzable atoms and hydrolyzable groups and processes for preparing them, and their use for producing thermally cured compositions.
摘要:
An aqueous dispersion with a pH of from 2 to 7, comprising (A) at least one swellable polymer or oligomer containing anionic and/or potentially anionic functional groups, (B) surface-modified, cationically stabilized, inorganic nanoparticles of at least one kind, and (C) at least one amphiphile; and its use for producing highly scratch-resistant coatings, moldings, and self-supporting films.
摘要:
Disclosed are coating compositions comprising at least one hydroxyl-containing compound (A) and at least one isocyanato-containing compound (B), wherein one or more of the constituents of the coating composition comprise between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (I) —N(X—SiR″x(OR′)3-x)n(X′—SiR″y(OR′)3-y)m (I) and between 2.5 and 97.5 mol %, based on the entirety of structural units (I) and (II), of at least one structural unit of the formula (II) —Z—(X—SiR″x(OR′)3-x) (II).
摘要:
Disclosed herein is a silane-functional mixture, comprising at least one phosphonic diester (A), at least one diphosphonic diester (A), or at least one phosphonic diester and one diphosphonic diester (A), and at least one compound (B) comprising at least two condensable silane groups.