摘要:
The Ni-based single crystal alloy disclosed here is a single crystal and has a chemical composition containing, as % by mass, Co: 8 to 12%, Cr: 5 to 7.5%, Mo: 0.2 to 1.2%, W: 5 to 7%, Al: 5 to 6.5%, Ta: 8 to 12%. Hf: 0.01 to 0.2%, Re: 2 to 4%, Si: 0.005 to 0.1%, with the balance of Ni and inevitable impurities.
摘要:
The Ni-based single crystal alloy disclosed here is a single crystal and has a chemical composition containing, as % by mass, Co: 8 to 12%, Cr: 5 to 7.5%, Mo: 0.2 to 1.2%, W: 5 to 7%, Al: 5 to 6.5%, Ta: 8 to 12%. Hf: 0.01 to 0.2%, Re: 2 to 4%, Si: 0.005 to 0.1%, with the balance of Ni and inevitable impurities.
摘要:
A thermal barrier coating material that exhibits superior high-temperature crystal stability to YSZ, as well as a high degree of toughness and an excellent thermal barrier effect. Also provided are a thermal barrier coating, which has a ceramic layer formed using the thermal barrier coating material and exhibits excellent durability to heat cycling, and a turbine member and a gas turbine which are each provided with the thermal barrier coating. The thermal barrier coating material comprises mainly ZrO2 which contains Yb2O3 and Sm2O3 as stabilizers, wherein the amount of the stabilizers is not less than 2 mol % and not more than 7 mol %, and the amount of the Sm2O3 is not less than 0.1 mol % and not more than 2.5 mol %.
摘要:
A process for producing a thermal barrier coating having an excellent thermal barrier effect and superior durability to thermal cycling. Also, a turbine member having a thermal barrier coating that has been formed using the production process, and a gas turbine. The process for producing a thermal barrier coating includes: forming a metal bonding layer (12) on a heat-resistant alloy substrate (11), and forming a ceramic layer (13) on the metal bonding layer (12) by thermal spraying of thermal spray particles having a particle size distribution in which the 10% cumulative particle size is not less than 30 μm and not more than 100 μm.
摘要:
In a specimen collecting method according to the present invention, a specimen is collected from a surface (114a) of a blade. An ultrasonic cutter having a cylindrical cutting blade is fed from the surface (114a) of the blade to a surface (110a) of a base material (100), and thus, a cylindrical incision is formed. After performing cutting to expand the incision outwardly, a rotating cutter (220) having a disc-shaped cutting blade (222) performs cutting inwardly from the cylindrical incision. Thus, a part (20a) situated inside the incision is cut away. The part (20a) becomes the specimen.
摘要:
A process for producing a thermal barrier coating having an excellent thermal barrier effect and superior durability to thermal cycling. Also, a turbine member having a thermal barrier coating that has been formed using the production process, and a gas turbine. The process for producing a thermal barrier coating includes: forming a metal bonding layer (12) on a heat-resistant alloy substrate (11), and forming a ceramic layer (13) on the metal bonding layer (12) by thermal spraying of thermal spray particles having a particle size distribution in which the 10% cumulative particle size is not less than 30 μm and not more than 100 μm.
摘要:
In a specimen collecting method according to the present invention, a specimen is collected from a surface (114a) of a blade. An ultrasonic cutter having a cylindrical cutting blade is fed from the surface (114a) of the blade to a surface (110a) of a base material (100), and thus, a cylindrical incision is formed. After performing cutting to expand the incision outwardly, a rotating cutter (220) having a disc-shaped cutting blade (222) performs cutting inwardly from the cylindrical incision. Thus, a part (20a) situated inside the incision is cut away. The part (20a) becomes the specimen.
摘要:
A method by which physical properties, including the Young's modulus and thermal conductivity of a ceramic layer of a thermal barrier coating formed on a high-temperature member, are quickly and accurately estimated. A method for estimating a physical property of a ceramic includes a step of calculating the Larson-Miller parameter from the time for which and the temperature at which the ceramic is heated; a step of acquiring the porosity of the ceramic corresponding to the calculated Larson-Miller parameter, based on the calculated Larson-Miller parameter and a diagram correlating the Larson-Miller parameter and the porosity obtained from samples having the same composition as the ceramic; and a step of acquiring the physical property of the ceramic corresponding to the acquired porosity, based on the acquired porosity and a diagram correlating the porosity and the physical property obtained from samples having the same composition as the ceramic.
摘要:
A method is provided by which physical properties, in particular, the Young's modulus and thermal conductivity of a ceramic layer of a thermal barrier coating formed on a high-temperature member are accurately estimated in a short period of time. A method for estimating a physical property of a ceramic includes a step of calculating the Larson-Miller parameter from the time for which and the temperature at which the ceramic is heated; a step of acquiring the porosity of the ceramic corresponding to the calculated Larson-Miller parameter, based on the calculated Larson-Miller parameter and a diagram correlating the Larson-Miller parameter and the porosity obtained from samples having the same composition as the ceramic; and a step of acquiring the physical property of the ceramic corresponding to the acquired porosity, based on the acquired porosity and a diagram correlating the porosity and the physical property obtained from samples having the same composition as the ceramic.
摘要:
An alloy material having high-temperature corrosion resistance, which exhibits excellent oxidation resistance and ductility and can be applied to gas turbines used at ultra high temperatures, and a thermal barrier coating, a turbine member and a gas turbine each comprising the alloy material. An alloy material having high-temperature corrosion resistance, comprising, by weight, Co: 15 to 30%, Cr: 10 to 30%, Al: 4 to 15%, Y: 0.1 to 3%, and Re: 0.1 to 1%, with the balance being substantially Ni. Also, an alloy material having high-temperature corrosion resistance, comprising, by weight, Ni: 20 to 40%, Cr: 10 to 30%, Al: 4 to 15%, Y: 0.1 to 3%, and Re: 0.1 to 5%, with the balance being substantially Co.