摘要:
A glass fiber reinforced polymer which excels in mechanical properties and is suitable for use in a large-sized structural members, formed from a dispersion liquid by dispersing reinforcement glass fibers and particulate thermoplastic resin in a surfactant-containing aqueous medium in which bubbles of air are dispersed, forming a sheet-like web on a porous support plate, and applying heat and pressure to form a sheet. The reinforcement glass fibers include a silane coupling agent while the matrix resin has functional groups bonded to the silane coupling agent. The concentration of said functional groups is higher in the regions adjacent the surfaces of said reinforcement glass fibers than in regions farther removed therefrom, and said concentration progressively decreases in the direction away from said reinforcement glass fibers.
摘要:
A resin composition for a composite-type vibration-damping material which comprises a saturated copolyester having a weight average molecular weight of at least 10,000 and a softening point of 50.degree. to 150.degree. C. and a polyfunctional isocyanate compound as a cross-linking agent and which, when cross-linked, has a degree of gelation (degree of cross-linking) of at least 10% and a composite-type vibration-damping material produced by use of the resin composition, have excellent adhesive strength and formability.When the resin composition is admixed with a conductive substance, a vibration-damping material produced by use of the admixture has excellent spot-weldability in addition to the above-mentioned excellent properties.
摘要:
Flowability-improving particles are adhered to surfaces of iron powder through a binder to provide an iron-based powder for powder metallurgy which has excellent flowability and which is capable of uniformly filling a thin-walled cavity and compaction with high performance of ejection force.
摘要:
As a paper-made stampable sheet having a high rigidity and, if necessary, improved adhesiveness and non-permeability and a light weight stampable sheet shaped body made from this sheet and a method of producing the same, there are proposed a paper-made stampable sheet obtained by paper-making a mixture of thermoplastic resin and reinforcing fibers to obtain a sheet-like web, piling a thermoplastic resin film of a single layer or multi layer or an organic fiber nonwoven fabric having at least one excellent property selected from rigidity, non-permeability and adhesiveness on at least one-side surface of the sheet-like web in accordance with use purpose, compressing them under heating above a melting point of the thermoplastic resin constituting the web, cooling and solidifying at a compressed state as well as a light weight stampable sheet shaped body made from this sheet and a method of producing the same.
摘要:
Flowability-improving particles are adhered to surfaces of iron powder through a binder to provide an iron-based powder for powder metallurgy which has excellent flowability and which is capable of uniformly filling a thin-walled cavity and compaction with high performance of ejection force.
摘要:
In an iron-based powder, 0.01% to 5.0% by mass of a flaky powder having an average particle size of longitudinal size of 100 or less, a thickness of 10 μm or less, and an aspect ratio (longitudinal size-to-thickness ratio) of 5 or more with respect to the iron-based mixed powder is contained, whereby the flowability of an iron-based mixed powder is increased, the density of a green compact is increased, and ejection force is greatly reduced after compaction, thereby accomplishing an increase in product quality and a reduction in production cost.
摘要:
An iron-based powder mixture for powder metallurgy is provided, in which iron-based powder is blended with at least one selected from talc and steatite, and preferably further blended with metallic soap, thereby when a compacted body is sintered, furnace environment is not adversely affected, and excellent compaction performance is achieved even in a low temperature range of less than 100° C., and more preferably, an obtained sintered body has excellent machining performance.
摘要:
In an iron-based powder, 0.01% to 5.0% by mass of a flaky powder having an average particle size of longitudinal size of 100 or less, a thickness of 10 μm or less, and an aspect ratio (longitudinal size-to-thickness ratio) of 5 or more with respect to the iron-based mixed powder is contained, whereby the flowability of an iron-based mixed powder is increased, the density of a green compact is increased, and ejection force is greatly reduced after compaction, thereby accomplishing an increase in product quality and a reduction in production cost.
摘要:
In an iron-based powder, 0.01% to 5.0% by mass of oxide particles having an average size of 0.5 μm or more are contained, whereby the flowability of an iron-based mixed powder is increased and thereby the density of a green compact is increased, and ejection force is greatly reduced after compaction, thereby accomplishing an increase in product quality and a reduction in production cost.
摘要:
Flowability-improving particles containing 50 to 100% by mass of carbon black are adhered to surfaces of iron powder through a binder to provide an iron-based powder for powder metallurgy which has excellent flowability and which is capable of uniformly filling a thin-walled cavity, compaction with high ejection force, and maintaining sufficient strength of a sintered body in subsequent sintering.