摘要:
Disclosed is a method of manufacturing a pattern electrode which excels in electroconductivity, transparency and etching property and a pattern electrode, the method comprising a step of applying a metal particle containing solution onto a substrate to form a conductive layer, a step of pattern printing a metal particle removing solution on a portion of the conductive layer, which is to be removed, and a step of washing the resulting printed material, whereby the portion of the conductive layer on which the metal particle removing solution has been printed is removed to form a non-conductive portion.
摘要:
The present invention can easily provide a method of manufacturing a pattern electrode with excellent electroconductivity and excellent transparency and a pattern electrode manufactured according to the method. The method of manufacturing a pattern electrode is characterized in that it comprises the steps of forming on a substrate an electroconductive layer containing metal nanowires, and carrying out pattern printing on the electroconductive layer employing a metal nanowire removing solution, followed by washing with water.
摘要:
Disclosed is a method of manufacturing a pattern electrode which excels in electroconductivity, transparency and etching property and a pattern electrode, the method comprising a step of applying a metal particle containing solution onto a substrate to form a conductive layer, a step of pattern printing a metal particle removing solution on a portion of the conductive layer, which is to be removed, and a step of washing the resulting printed material, whereby the portion of the conductive layer on which the metal particle removing solution has been printed is removed to form a non-conductive portion.
摘要:
The present invention can easily provide a method of manufacturing a pattern electrode with excellent electroconductivity and excellent transparency and a pattern electrode manufactured according to the method. The method of manufacturing a pattern electrode is characterized in that it comprises the steps of forming on a substrate an electroconductive layer containing metal nanowires, and carrying out pattern printing on the electroconductive layer employing a metal nanowire removing solution, followed by washing with water.
摘要:
An optical cellulose ester film comprising a cellulose ester (A); at least one ester based plasticizer (B) selected from ester based plasticizers composed of a polyhydric alcohol and a univalent carboxylic acid, or ester based plasticizers composed of a polyvalent carboxylic acid and a monohydric alcohol; at least one stabilizer (C) selected from the group consisting of a phenol based stabilizer, a hindered amine based stabilizer, or a phosphorous based stabilizer; and a hydrogen bonding solvent (D).
摘要:
Disclosed is a method for producing a cellulose ester film wherein a film-forming material containing the following components A-C is heated and melted, and a cellulose ester film is formed therefrom by melt-casting. A: a cellulose resin, B: an ester compound obtained by condensing an organic acid represented by Formula (1) and a polyalcohol, and C: an aliphatic polyester or an aliphatic-aromatic copolymer.
摘要:
A process for producing a cellulose ester film that is produced by a melt casting method using no solvent at film formation, and that attains reduction of bright spot foreign matter, excelling in planarity, and that attains reduction of staining, excelling in dimensional stability. It is also intended to provide such a cellulose ester film, a polarizing plate and a liquid crystal display unit. There is provided a process for producing a cellulose ester film, characterized by forming into a film a material containing a cellulose ester and an ester compound of 1 to 7.5 distribution coefficient obtained by condensation of a polyhydric alcohol and an organic acid of the general formula: (1) according to a melt casting method.
摘要:
A method of producing a cellulose ester film comprising the steps of: (i) melting a cellulose ester containing 5.0% by weight or less of water at a temperature in the range of 150 to 300° C.; and (ii) melt casting the molten cellulose ester to form the cellulose ester film, wherein a compound having both a phenol moiety and a hindered amine moiety in the molecule is incorporated in the cellulose ester.
摘要:
A composition for melt casting film formation that excels in not only uniformity of retardation being an optical characteristic, especially uniformity of retardation in the direction of film width, but also contrast; and relevant thereto, an optical film, process for producing the optical film, polarization plate and liquid crystal display apparatus. Accordingly, there is provided a composition for melt casting film formation containing a cellulose ester in an amount of 50 mass % or more, characterized in that the free acid content of the composition is 50 ppm or less.
摘要:
A process for producing a cellulose ester film that is produced by a melt casting method using no solvent at film formation, and that attains reduction of bright spot foreign matter, excelling in planarity, and that attains reduction of staining, excelling in dimensional stability. It is also intended to provide such a cellulose ester film, a polarizing plate and a liquid crystal display unit. There is provided a process for producing a cellulose ester film, characterized by forming into a film a material containing a cellulose ester and an ester compound of 1 to 7.5 distribution coefficient obtained by condensation of a polyhydric alcohol and an organic acid of the general formula: (1) according to a melt casting method.