1.发明授权Water-based composition for fluororubber vulcanization and article coated with fluororubber 失效用于氟橡胶硫化的水基组合物和用氟橡胶涂覆的制品公开(公告)号：US06720381B1
公开(公告)日：2004-04-13
申请号：US10089865
申请日：2002-04-05
IPC分类号： C08K300
CPC分类号： C09D127/12 , C08L27/12 , C08L71/02 , C08L71/12 , C09D171/02 , C08L2666/14 , C08L2666/04
摘要： In an aqueous curing composition of a fluoroelastomer comprising a fluoroelastomer, a curing agent and a surfactant, a surfactant with which an amount of decomposition residues is 0.3% by weight or less after being baked at 300° C. for 30 minutes, for example, a polyoxyethylene alkyl ether or a polyoxyethylenepolyoxypropylene block polymer, is used as a surfactant. Such a composition can make use of the inherent characteristics of the fluoroelastomer.
摘要翻译： 在包含含氟弹性体，固化剂和表面活性剂的含氟弹性体的含水固化组合物中，在300℃下焙烧30分钟后，分解残留量为0.3重量％以下的表面活性剂，例如， 聚氧乙烯烷基醚或聚氧乙烯聚氧丙烯嵌段聚合物作为表面活性剂。 这种组合物可以利用含氟弹性体的固有特性。
-
公开(公告)号：US06764763B1
公开(公告)日：2004-07-20
申请号：US09623010
申请日：2000-08-25
IPC分类号： G03G1520
CPC分类号： C09D127/16 , C08K5/13 , C08L27/12 , C08L27/18 , C08L61/04 , C08L2205/02 , C09D127/12 , Y10S428/906 , Y10T428/2933 , Y10T428/294 , Y10T428/3154 , C08L2666/04 , C08L2666/14 , C08L2666/28
摘要： An aqueous fluoroelastomer curable composition comprising an aqueous fluoroelastomer dispersion and a basic polyol curing agent, and an article having a coating film formed from this composition. The aqueous fluoroelastomer curable composition has a long pot life although it is a one-fluid type aqueous dispersion, and forms a cured film having sufficient strength and heat resistance at a relatively low temperature in a short time.
摘要翻译： 一种包含含氟弹性体分散体和碱性多元醇固化剂的含氟弹性体固化性组合物和具有由该组合物形成的涂膜的制品。 含氟弹性体固化性组合物虽然是单流体型水分散体，但其使用寿命长，并且在短时间内在较低的温度下形成具有足够的强度和耐热性的固化膜。
-
3.发明授权Aqueous curing composition of fluoroelastomer and article coated with fluoroelastomer 失效含氟弹性体的水性固化组合物和涂有含氟弹性体的制品公开(公告)号：US06664336B1
公开(公告)日：2003-12-16
申请号：US09936272
申请日：2001-09-10
IPC分类号： C08L2722
CPC分类号： C09D127/16 , C08K5/0008 , C08L27/12 , C08L27/16 , C08L27/18 , C08L2205/02 , C09D127/12 , C09D127/18 , C08L2666/04
摘要： An aqueous curing composition of a fluoroelastomer containing a fluoroelastomer, a fluororesin, a curing agent, which further contains a surfactant which leaves 0.3 wt. % or less of a decomposition residue after being heated at 300° C. for 30 minutes and/or a polar solvent having a boiling point of 300° C. or less and a surface tension of at least 30 dyne/cm at room temperature. When a coating film is formed from this aqueous composition, a large amount of the fluororesin contained therein can be bled up on the surface of the coating film. Thus, the durability and non-tackiness of the coating film can be improved.
摘要翻译： 含氟弹性体的含氟弹性体的含水固化组合物，含氟弹性体，氟树脂，固化剂，其还含有0.3重量份的表面活性剂。 在室温下在300℃加热30分钟后，和/或沸点为300℃以下，极限溶剂的表面张力为30达因/厘米3以下的分解残渣的％以下。 当由该含水组合物形成涂膜时，其中所含的大量氟树脂可以在涂膜的表面上流出。 因此，可以提高涂膜的耐久性和非粘性。
-
4.发明授权公开(公告)号：US07550530B2
公开(公告)日：2009-06-23
申请号：US10558981
申请日：2004-06-01
IPC分类号： C08G75/02
CPC分类号： C09D127/16 , C08K5/0025 , C08L27/12 , C08L71/02 , Y10T428/2933 , C08L2666/02 , C08L2666/14
摘要： An aqueous fluoroelastomer curable composition including two liquids of a main material fluoroelastomer aqueous dispersion (I) and a fluoroelastomer-curing agent aqueous solution (II), wherein the above main material fluoroelastomer aqueous dispersion (I) is an aqueous dispersion having a pH of 6.5 to 8.5, comprising a fluoroelastomer (A), a dispersant (B), an acid acceptor (C) and a salt (D) composed of an acid with a pKa of 3 to 7 and a base with a pKa of 8 to 12, and the above fluoroelastomer-curing agent aqueous solution (II) is an aqueous solution including a fluoroelastomer-curing agent.
摘要翻译： 一种包含主要含氟弹性体水分散体（I）和含氟弹性体固化剂水溶液（II）的两种液体的含氟弹性体固化性组合物，其中上述主要含氟弹性体水分散体（I）是pH为6.5的水分散体 至8.5，包含含氟弹性体（A），分散剂（B），酸受体（C）和由pKa为3〜7的酸组成的盐（D）和pKa为8〜12的碱， 上述含氟弹性体固化剂水溶液（II）是含氟弹性体固化剂的水溶液。
-
公开(公告)号：US06325752B1
公开(公告)日：2001-12-04
申请号：US09485128
申请日：2000-02-04
IPC分类号： C08K322
CPC分类号： C08K3/22 , C09D127/12 , C08L27/12 , C08L2666/54
摘要： An aqueous coating composition comprising a fluororubber and, as an acid acceptor, at least one inorganic composite compound, for example, an inorganic composite oxide or an inorganic composite salt, in particular, an inorganic composite compound containing magnesium such as a hydrotalcite. Such an inorganic composite compound is not agglomerated to form secondary particles, when it is dispersed to primary particles, and can maintain the storage stability of the aqueous coating composition of a fluororubber.
摘要翻译： 包含氟橡胶和作为酸受体的至少一种无机复合化合物，例如无机复合氧化物或无机复合盐，特别是含有镁的无机复合化合物如水滑石的水性涂料组合物。 当将这种无机复合化合物分散在一次粒子中时，不会附聚而形成二次粒子，能够维持氟橡胶的水性涂料组合物的保存稳定性。
-
6.发明申请公开(公告)号：US20070060698A1
公开(公告)日：2007-03-15
申请号：US10558981
申请日：2004-06-01
IPC分类号： C08G75/02
CPC分类号： C09D127/16 , C08K5/0025 , C08L27/12 , C08L71/02 , Y10T428/2933 , C08L2666/02 , C08L2666/14
摘要： The present invention provides an aqueous fluoroelastomer curable composition which is excellent in storage stability. The present invention provides an aqueous fluoroelastomer curable composition comprising two liquids of a main material fluoroelastomer aqueous dispersion (I) and a fluoroelastomer-curing agent aqueous solution (II), wherein the above main material fluoroelastomer aqueous dispersion (I) is an aqueous dispersion having a pH of 6.5 to 8.5, comprising a fluoroelastomer (A), a dispersant (B), an acid acceptor (C) and a salt (D) composed of an acid with a pKa of 3 to 7 and a base with a pKa of 8 to 12, and the above fluoroelastomer-curing agent aqueous solution (II) is an aqueous solution comprising a fluoroelastomer-curing agent.
摘要翻译： 本发明提供一种储存稳定性优异的含氟弹性体固化性组合物。 本发明提供一种包含主要含氟弹性体水分散体（I）和含氟弹性体 - 固化剂水溶液（II）的两种液体的含氟弹性体固化性组合物，其中上述主要含氟弹性体水分散体（I）是具有 pH6.5〜8.5，由含氟弹性体（A），分散剂（B），酸受体（C）和由pKa为3〜7的酸构成的盐（D）和pKa为pKa的碱 8〜12，上述含氟弹性体固化剂水溶液（II）是含氟弹性体固化剂的水溶液。
-
7.发明授权Fluorine-containing coating composition, primer for ETFE-based coatings, and coated article 有权含氟涂料组合物，ETFE基涂料底漆和涂层制品公开(公告)号：US07192638B2
公开(公告)日：2007-03-20
申请号：US10476785
申请日：2002-05-09
CPC分类号： C09D127/18 , C08L63/00 , C08L79/08 , Y10T428/254 , Y10T428/3154 , C08L2666/04 , C08L2666/14 , C08L2666/02
摘要： A fluorine-containing coating composition obtainable by compounding a macromolecular material with an ethylene-tetrafluoroethylene copolymer having an average particle diameter of 1 to 30 μm. The macromolecular material is one occurring as a liquid or in a state dissolved in a solvent at below the melting initiating temperature of the ethylene-tetrafluoroethylene copolymer. Furthermore, a volume ratio between the ethylene-tetrafluoroethylene copolymer and the macromolecular material is 35:65 to 95:5.
摘要翻译： 通过将高分子材料与平均粒径为1〜30μm的乙烯 - 四氟乙烯共聚物混合而获得的含氟涂料组合物。 大分子材料是在低于乙烯 - 四氟乙烯共聚物的熔融起始温度下以液体或溶解在溶剂中的状态存在的物质。 此外，乙烯 - 四氟乙烯共聚物和高分子材料之间的体积比为35:65至95:5。
-
公开(公告)号：US07208227B2
公开(公告)日：2007-04-24
申请号：US10504168
申请日：2003-01-28
CPC分类号： C09D127/18 , B05D7/52 , B32B15/08 , B32B27/28 , C08L79/08 , Y10T428/31504 , Y10T428/3154 , Y10T428/31678 , Y10T428/31699 , Y10T428/31721 , C08L81/00 , C08L2666/20
摘要： The present invention provides a lining member in which an ETFE is used and which shows good adhesion and can show a reduction in coating film defects. An ETFE-lining member comprising a substrate, a primer layer and a surface layer laminated in this order, wherein said substrate comprises a metal or a ceramic, said primer layer comprises an ETFE (A) and a binder component, and said surface layer comprises an ETFE (B) having fluorine content higher than that of the ETFE (A).
摘要翻译： 本发明提供一种其中使用ETFE并且显示出良好的粘合性并且可以显示涂膜缺陷减少的衬里构件。 一种ETFE衬里构件，其包括依次层叠的衬底，底漆层和表面层，其中所述衬底包括金属或陶瓷，所述底漆层包含ETFE（A）和粘合剂组分，所述表面层包含 氟含量高于ETFE（A）的ETFE（B）。
-
公开(公告)号：US20050147826A1
公开(公告)日：2005-07-07
申请号：US10504168
申请日：2003-01-28
CPC分类号： C09D127/18 , B05D7/52 , B32B15/08 , B32B27/28 , C08L79/08 , Y10T428/31504 , Y10T428/3154 , Y10T428/31678 , Y10T428/31699 , Y10T428/31721 , C08L81/00 , C08L2666/20
摘要： The present invention provides a lining member in which an ETFE is used and which shows good adhesion and can show a reduction in coating film defects. An ETFE-lining member comprising a substrate, a primer layer and a surface layer laminated in this order, wherein said substrate comprises a metal or a ceramic, said primer layer comprises an ETFE (A) and a binder component, and said surface layer comprises an ETFE (B) having fluorine content higher than that of the ETFE (A).
摘要翻译： 本发明提供一种其中使用ETFE并且显示出良好的粘合性并且可以显示涂膜缺陷减少的衬里构件。 一种ETFE衬里构件，其包括依次层叠的衬底，底漆层和表面层，其中所述衬底包括金属或陶瓷，所述底漆层包含ETFE（A）和粘合剂组分，所述表面层包含 氟含量高于ETFE（A）的ETFE（B）。
-
公开(公告)号：US5919851A
公开(公告)日：1999-07-06
申请号：US841943
申请日：1997-04-08
摘要： A paint composition comprising, as a leveling agent, 0.01 to 3.0 parts by weight of a polyfluorinated carbon chain-containing compound and 0.01 to 3.0 parts by weight of a silicone oil per 100 parts by weight of a film forming component and being capable of forming a film being excellent in water- and oil-repelling property and stain resistance, and painted articles being excellent in water- and oil-repelling property and stain resistance can be provided.
摘要翻译： 作为流平剂的涂料组合物，每100重量份成膜组分包含0.01至3.0重量份的含多氟化碳链的化合物和0.01至3.0重量份的硅油，并且能够形成 可以提供防水防油性和耐污染性优异的防水防油性和耐污染性优异的涂膜制品。
-
-
-
-
-
-
-
-
-
搜索结果
23 条记录 (耗时 0.019 秒)