摘要:
A method for the decomposition of chromium ore in a directly heated revolving tube is described, in which oxygen-containing gases are introduced into the revolving tube by means of below-bed nozzles.
摘要:
A method for manufacturing alkali chromates by the reacting of chromium ore with alkali compounds and oxidation in an atmosphere containing at least 50% oxygen is described, in which the mixture consisting of chromium ore, alkali compound and optionally leaning materials is heated in a first stage in an atmosphere containing not more than 5 vol. % oxygen to a temperature between 1000.degree. and 1 400.degree. C., and in a second stage is oxidized at a lower temperature of 900.degree. to 1 070.degree. C. with supply of an atmosphere containing at least 50% oxygen.
摘要:
The invention relates to a method for producing medicaments that contain vardenafil hydrochloride, essentially as trihydrate in solid form, and to medicaments that can be obtained according to this method
摘要:
An integrated process for the solution polymerization and subsequent halogenation of butyl rubber in a common medium is disclosed. The process comprises providing a solution polymerization reactor containing a C6 medium mixed with a monomer mixture comprising at least an isoolefin monomer and a multiolefin monomer in a mass ratio of monomer mixture to medium of from 61:39 to 80:20. Once polymerized, residual unreacted monomer mixture is separated from the rubber solution using a distillation process. The residual monomers may then be purified and recycled back into the reactor. The separated rubber solution is then halogenated. The process obviates the need for separating the rubber from the medium following polymerization, then re-dissolving it in another solvent for halogenation, thereby saving energy cost. The process optionally employs heat exchangers for the reactor feed streams to further reduce energy consumption.
摘要:
A cyclone reactor for producing a usable by-product as part of a recoverable slag layer, the reactor comprising a housing having an outer wall that defines a combustion chamber; an inlet configured to introduce a reactant into the reactor; a burner configured to combust the reactant in a flame zone near a central axis of the chamber; and an outlet configured to provide for the removal of the usable by-product from the housing; wherein the reactor is configured to combust a first portion of the reactant in an exothermic reaction in the flame zone; and wherein the reactor is configured to convert a second portion of the reactant in an endothermic reaction near the outer wall to produce the by-product as part of the slag layer.
摘要:
A process for the preparation of a catalyst for the production of carbon nanotubes, the use of the catalyst for the production of carbon nanotubes, and the carbon nanotubes obtained by this production process. The catalyst is prepared on the basis of at least two metals from the group: cobalt, manganese, iron, nickel and molybdenum from soluble precursor compounds by spray drying or spray granulation of the precursor compounds dissolved in a solvent, and subsequent calcination.
摘要:
A method for producing bisphenol A in prill form is disclosed. Molten bisphenol is top-fed into a prilling tower via a plate containing a plurality of nozzles. A gas coolant guided through a circuit is led into said tower in a counter flow direction. The prills are cooled to about room temperature, collected at the bottom of the tower and removed. Also disclosed is the device for carrying out the inventive method and the prills thus produced.
摘要:
A method for coating carrier particles for use in electrostatic developers is provided comprising the steps of:bringing the carrier particles to be coated in a vessel equipped with means for agitating the carrier particles, so that the carrier articles occupy less than 85% by volume of the vessel, and the agitation of the carrier particles is described by a Froude number between 0.2 and 20,adding a solution containing between 6 and 60% by weight with respect to the total volume of the solution of chemical compounds for coating the carrier particles in a solvent with a boiling point of A.degree. C. to the vessel at such a rate that, at any time, the solvent is present in an amount lower than 1.25 10.sup.-4 ml per cm.sup.2 of surface of the carrier particles to be coated,keeping the carrier particles in the vessel at a temperature of at most (A+10).degree. C., andcontinuously evacuating the solvent.
摘要:
An integrated process for the solution polymerization and subsequent halogenation of butyl rubber in a common medium is disclosed. The process comprises providing a solution polymerization reactor containing a C6 medium mixed with a monomer mixture comprising at least an isoolefin monomer and a multiolefin monomer in a mass ratio of monomer mixture to medium of from 61:39 to 80:20. Once polymerized, residual unreacted monomer mixture is separated from the rubber solution using a distillation process. The residual monomers may then be purified and recycled back into the reactor. The separated rubber solution is then halogenated. The process obviates the need for separating the rubber from the medium following polymerization, then re-dissolving it in another solvent for halogenation, thereby saving energy cost. The process optionally employs heat exchangers for the reactor feed streams to further reduce energy consumption.
摘要:
Finely divided particles can be provided in a simple manner and with good adhesion with a coating which is a polyfunctional organosilane and/or a hydrolysis product thereof, and/or a reaction product thereof with an organosilane which contains a hetero atom and/or with an alkoxide.