摘要:
A curable coating composition is disclosed comprising a resinous binder comprising (a) a reaction product of an epoxy-containing polymer with a compound containing phosphorus acid groups, the reaction product having reactive functional groups, and (b) a curing agent having functional groups reactive with the functional groups of (a). An electroconductive pigment is dispersed in (a) such that the weight ratio of the electroconductive pigment to (a) plus (b) is within the range of 0.5 to 9.0:1. When the curable coating composition is deposited and cured on a metal substrate, the cured coating is weldable.
摘要:
A corrosion resistant, alkali resistant coating composition is disclosed. The composition comprises a binder comprising a reaction product of an epoxy-containing material and a phosphorus-containing material together with a curing agent. Aminoplasts, especially melamine-based aminoplasts, are particularly suitable curing agents. A source of silicon can optionally be included. The compositions also provide excellent adhesion and can be used with or without a weldable primer. The compositions are applied to and cured on a metal substrate.
摘要:
A curable coating composition is disclosed comprising a resinous binder comprising (a) a reaction product of an epoxy-containing polymer with a compound containing phosphorus acid groups, the reaction product having reactive functional groups, and (b) a curing agent having functional groups reactive with the functional groups of (a). An electroconductive pigment is dispersed in (a) such that the weight ratio of the electroconductive pigment to (a) plus (b) is within the range of 0.5 to 9.0:1. When the curable coating composition is deposited and cured on a metal substrate, the cured coating is weldable.
摘要:
A corrosion resistant, alkali resistant coating composition is disclosed. The composition comprises a binder comprising a reaction product of an epoxy-containing material and a phosphorus-containing material together with a curing agent. Aminoplasts, especially melamine-based aminoplasts, are particularly suitable curing agents. A source of silicon can optionally be included. The compositions also provide excellent adhesion and can be used with or without a weldable primer. The compositions are applied to and cured on a metal substrate.
摘要:
A corrosion resistant, alkali resistant coating composition is disclosed. The composition comprises a binder comprising a reaction product of an epoxy-containing material and a phosphorus-containing material together with a curing agent. Aminoplasts, especially melamine-based aminoplasts, are particularly suitable curing agents. A source of silicon can optionally be included. The compositions also provide excellent adhesion and can be used with or without a weldable primer. The compositions are applied to and cured on a metal substrate.
摘要:
A corrosion resistant, alkali resistant coating composition is disclosed. The composition comprises a binder comprising a reaction product of an epoxy-containing material and a phosphorus-containing material together with a curing agent. Aminoplasts, especially melamine-based aminoplasts, are particularly suitable curing agents. A source of silicon can optionally be included. The compositions also provide excellent adhesion and can be used with or without a weldable primer. The compositions are applied to and cured on a metal substrate.
摘要:
Disclosed is a temporary, protective dry lubricating coating composition which when deposited and dried on a metallic substrate, is removable by contacting with an aqueous alkaline cleaning solution. The coating composition comprises (a) a wax present in an amount up to 20 weight percent; (b) a base-neutralized, acid functional polymer which is the polymerization reaction product of (i) a polymerizable, ethylenically unsaturated monomer having acid functionality and (ii) at least one polymerizable, ethylenically unsaturated monomer different from (i); and (c) an amine containing an acyclic moiety of from 8 to 30 carbon atoms, the amine being different from the base used to neutralize the acid functional polymer (b). The temporary protective coating is compatible with a wide range of adhesives and sealants used in the assembly of automobiles.
摘要:
Provided is a coating composition containing (a) a resinous binder composition including an epoxy-functional polymer; and (b) a solid particulate composition dispersed in the resinous binder composition including (i) an electrically conductive material and (ii) a corrosion inhibitive material. The electrically conductive material (i) and the corrosion inhibitive material (ii) are present in a weight ratio of the conductive material (i) to the corrosion inhibitive material (ii) ranging from 1:8 to 12:1. The composition is characterized in that when applied to a conductive substrate to form a coating thereon, the coating is weldable. Coated substrates and related methods are further provided.
摘要:
Disclosed are curable compositions such as adhesives and coatings containing as an adhesion promoter N-acyl amino acids having the structure: ##STR1## wherein n is 0 or 1, R.sup.1 is an alkyl or aryl group having from one to 10 carbon atoms optionally including --COOH, R.sup.2 is an alkylene or arylene group having from one to 10 carbon atoms, and R.sup.3 is H, --COOH, alkyl or aryl groups having from one to 10 carbon atoms, or carboxyl-substituted alkyl or aryl groups having from one to 10 carbon atoms.
摘要:
A weldable curable coating composition with improved intercoat adhesion is disclosed comprising a resinous binder comprising a polymer (A) with functional groups and a crosslinking agent with functional groups reactive with those of polymer (A); an electroconductive pigment; and an adhesion promoting compound comprising boron containing compounds. In an alternative embodiment, the adhesion promoting compound may comprise siloxane polymer reacted with aluminates, titanates, zirconates, silicates, siloxanes, silanes, and mixtures thereof, wherein each component is different.