摘要:
A negative electrode 10 for a nonaqueous secondary battery, has an active material layer 2 containing active material particles 2a. The active material layer 2 has a metallic material 4 deposited among the particles by electroplating. The negative electrode 10 has a large number of holes 5 open on at least one side thereof and extending through the thickness of the active material layer. The negative electrode 10 further has a pair of current collecting layers 3a and 3b adapted to be brought into contact with an electrolyte. The active material layer 2 is between the current collecting layers 3a and 3b. The holes 5 open on the negative electrode 10 preferably have an opening area ratio of 0.3% to 30%. At least one of the pair of the current collecting layers 3a and 3b preferably has a thickness of 0.3 to 10 μm.
摘要:
A negative electrode 10 for a nonaqueous secondary battery, has an active material layer 2 containing active material particles 2a. The active material layer 2 has a metallic material 4 deposited among the particles by electroplating. The negative electrode 10 has a large number of holes 5 open on at least one side thereof and extending through the thickness of the active material layer. The negative electrode 10 further has a pair of current collecting layers 3a and 3b adapted to be brought into contact with an electrolyte. The active material layer 2 is between the current collecting layers 3a and 3b. The holes 5 open on the negative electrode 10 preferably have an opening area ratio of 0.3% to 30%. At least one of the pair of the current collecting layers 3a and 3b preferably has a thickness of 0.3 to 10 μm.
摘要:
Disclosed is a negative electrode for a nonaqueous secondary battery included of a current collector and an active material structure containing an electro-conductive material having low capability of forming a lithium compound on at least one side of the current collector, the active material structure containing 5 to 80% by weight of active material particles containing a material having high capability of forming a lithium compound. The active material structure preferably has an active material layer containing the active material particles and a surface coating layer formed on the active material layer.
摘要:
A negative electrode for nonaqueous secondary batteries is disclosed. The negative electrode has a pair of current collecting surface layers of which the surfaces are adapted to be brought into contact with an electrolyte and at least one active material layer interposed between the surface layers. The active material layer contains particles of an active material having high capability of forming a lithium compound. The material constituting the surfaces is preferably present over the whole thickness of the active material layer to electrically connect the surfaces so that the electrode exhibits a current collecting function as a whole. The surface layers each preferably have a thickness of 0.3 to 10 μm.
摘要:
An anode for nonaqueous secondary batteries is disclosed. The anode has a pair of current collecting surface layers of which the surfaces are adapted to be brought into contact with an electrolytic solution and at least one active material layer interposed between the surface layers. The active material layer contains particles of an active material having high capability of forming a lithium compound. The material constituting the surfaces is preferably present over the whole thickness of the active material layer to electrically connect the surfaces so that the electrode exhibits a current collecting function as a whole. The surface layers each preferably have a thickness of 0.3 to 10 μm.
摘要:
Disclosed is a negative electrode for a nonaqueous secondary battery comprised of a current collector and an active material structure containing an electro-conductive material having low capability of forming a lithium compound on at least one side of the current collector, the active material structure containing 5 to 80% by weight of active material particles containing a material having high capability of forming a lithium compound. The active material structure preferably has an active material layer containing the active material particles and a surface coating layer formed on the active material layer.
摘要:
A negative electrode 10 for a nonaqueous secondary battery has an active material layer 12 containing active material particles 12a. The particles 12a are coated at least partially with a metallic material 13 having low capability of lithium compound formation. The active material layer 12 has voids located between the metallic material-coated particles 12a with a void fraction of 15% to 45%. The metallic material 13 on the surface of the particles is preferably present throughout the thickness of the active material layer. The active material particles 12a are preferably of a silicon-based material. The active material layer 12 preferably contains 1% to 3% by weight of an electroconductive carbon material based on the weight of the active material particles 12a.
摘要:
A negative electrode (10) for use in a non-aqueous electrolyte secondary battery comprises an active material layer (12) containing a particle (12a) of an active material. At least a part of the surface of the particle (12a) is coated with a metal material (13) having a poor ability of forming a lithium compound. A void is formed between the particles (12a) that are coated with the metal material (13). The active material layer has a void ratio of 15 to 45%. Preferably, the metal material (13) is present over the entire area of such a part of the surface of the particle that extends in the thickness-wise direction of the active material layer. Also preferably, the particle (12a) of the active material is composed of a silicone material, and the active material layer (12) contains a conductive carbon material in an amount of 1 to 3% by weight relative to the weight amount of the particle (12a) of the active material.
摘要:
A negative electrode 1 for nonaqueous secondary batteries characterized by having an active material layer 5 and a metallic lithium layer 3 both between a pair of current collecting surface layers 4. The negative electrode 1 has two negative electrode precursors 2 each composed of the current collecting surface layer 4 and the active material layer 5 on one side of the surface layer 4. The two negative electrode precursors 2 are united with their active material layers 5 facing each other and with the metallic lithium layer 3 sandwiched therebetween. A metallic material having low capability of forming a lithium compound penetrates through the whole thickness of the active material layer 5.
摘要:
A negative electrode 1 for nonaqueous secondary batteries characterized by having an active material layer 5 and a metallic lithium layer 3 both between a pair of current collecting surface layers 4. The negative electrode 1 has two negative electrode precursors 2 each composed of the current collecting surface layer 4 and the active material layer 5 on one side of the surface layer 4. The two negative electrode precursors 2 are united with their active material layers 5 facing each other and with the metallic lithium layer 3 sandwiched therebetween. A metallic material having low capability of forming a lithium compound penetrates through the whole thickness of the active material layer 5.