摘要:
The invention provides an optical fiber coated with a Supercoating, wherein the Supercoating comprises at least two layers, wherein the first layer is a Primary Coating that is in contact with the outer surface of the optical fiber and the second layer is a Secondary Coating in contact with the outer surface of the Primary Coating, wherein the cured Primary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity: A) a % RAU of from about 84% to about 99%;B) an in-situ modulus of between about 0.15 MPa and about 0.60 MPa; and C) a Tube Tg, of from about −25° C. to about −55° C.; wherein the cured Secondary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity: A) a % RAU of from about 80% to about 98%; B) an in-situ modulus of between about 0.60 GPa and about 1.90 GPa; and C) a Tube Tg, of from about 50° C. to about 80° C.
摘要:
The invention relates to a Radiation Curable Secondary Coating composition for use on an Optical Fiber. The Radiation Curable Secondary Coating composition is a urethane-free Alpha Oligomer prepared by reaction of the following: (a) an acrylate compound selected from an alcohol-containing acrylate or alcohol-containing methacrylate compound, (b) an anhydride compound, (c) an epoxy-containing compound, (d) optionally an extender compound, and (e) optionally a catalyst. The invention also relates to a coated wire and to a coated optical fiber.
摘要:
A Radiation Curable Secondary Coating comprising A) a Secondary Coating Oligomer Blend, which is mixed with B) a first diluent; C) a second diluent; D) an antioxidant; E) a first photoinitiator; F) a second photoinitiator; and G) optionally a slip additive or a blend of slip additives; wherein said Secondary Coating Oligomer Blend comprises: α) an Alpha Oligomer, which is non-urethane; β) a Beta Oligomer; which is a urethane or non-urethane. γ) a Gamma Oligomer; wherein said Gamma Oligomer is an epoxy diacrylate.
摘要:
The invention relates to a Radiation Curable Secondary Coating composition for use on an Optical Fiber. The Radiation Curable Secondary Coating composition is a urethane-free Alpha Oligomer prepared by reaction of the following: (a) an acrylate compound selected from an alcohol-containing acrylate or alcohol-containing methacrylate compound, (b) an anhydride compound, (c) an epoxy-containing compound, (d) optionally an extender compound, and (e) optionally a catalyst. The invention also relates to a coated wire and to a coated optical fiber.
摘要:
The invention provides an optical fiber coated with a Supercoating, wherein the Supercoating comprises at least two layers, wherein the first layer is a Primary Coating that is in contact with the outer surface of the optical fiber and the second layer is a Secondary Coating in contact with the outer surface of the Primary Coating, wherein the cured Primary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity: A) a % RAU of from about 84% to about 99%;B) an in-situ modulus of between about 0.15 MPa and about 0.60 MPa; andC) a Tube Tg, of from about −25° C. to about −55° C.; wherein the cured Secondary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity: A) a % RAU of from about 80% to about 98%; B) an in-situ modulus of between about 0.60 GPa and about 1.90 GPa; and C) a Tube Tg, of from about 50° C. to about 80° C.
摘要:
A new radiation curable Secondary Coating for optical fibers is described and claimed wherein said composition comprises a Secondary Coating Oligomer Blend, which is mixed with a first diluent monomer; a second diluent monomer; optionally, a third diluent monomer; an antioxidant; a first photoinitiator; a second photoinitiator; and optionally a slip additive or a blend of slip additives; wherein said Secondary Coating Oligomer Blend comprises: α) an Omega Oligomer; and β) an Upsilon Oligomer; wherein said Omega Oligomer is synthesized by the reaction of α1) a hydroxyl-containing (meth)acrylate; α2) an isocyanate; α3) a polyether polyol; and α4) tripropylene glycol; in the presence of α5) a polymerization inhibitor; and α6) a catalyst; to yield the Omega Oligomer; wherein said catalyst is selected from the group consisting of dibutyl tin dilaurate; metal carboxylates, including, but not limited to: organobismuth catalysts such as bismuth neodecanoate; zinc neodecanoate; zirconium neodecanoate; zinc 2-ethylhexanoate; sulfonic acids, including but not limited to dodecylbenzene sulfonic acid, methane sulfonic acid; amino or organo-base catalysts, including, but not limited to: 1,2-dimethylimidazole and diazabicyclooctane; triphenyl phosphine; alkoxides of zirconium and titanium, including, but not limited to Zirconium butoxide and Titanium butoxide; and Ionic liquid phosphonium salts; and tetradecyl(trihexyl)phosphonium chloride; and wherein said Upsilon Oligomer is an epoxy diacrylate.
摘要:
The first aspect of the instant claimed invention is a method of formulating radiation curable Supercoatings for application to an optical fiber used in a telecommunications network. A Multi-layer Film Drawdown Method useful in the Method of formulating radiation curable Supercoatings is also described and claimed. Single mode Optical fibers coated with specific radiation curable Supercoatings are also described and claimed.