摘要:
The invention relates to a Radiation Curable Secondary Coating composition for use on an Optical Fiber. The Radiation Curable Secondary Coating composition is a urethane-free Alpha Oligomer prepared by reaction of the following: (a) an acrylate compound selected from an alcohol-containing acrylate or alcohol-containing methacrylate compound, (b) an anhydride compound, (c) an epoxy-containing compound, (d) optionally an extender compound, and (e) optionally a catalyst. The invention also relates to a coated wire and to a coated optical fiber.
摘要:
Radiation curable coatings for use as a Primary Coating for optical fibers, optical fibers coated with said coatings and methods for the preparation of coated optical fibers. The present invention provides a radiation curable Primary Coating composition comprising: an oligomer; first diluent monomer; a second diluent monomer; a third diluent monomer; a first light stabilizer; a first photoinitiator; a second photoinitiator; an antioxidant; a second light stabilizer; and an adhesion promoter; wherein said oligomer is the reaction product of hydroxyl-containing acrylate; an isocyanate; a polyether polyol; a polymerization inhibitor; a catalyst; and a diluent; wherein said oligomer has a number average molecular weight of from at least about 4000 g/mol to less than or equal to about 15,000 g/mol; and wherein said catalyst is selected from the group consisting of copper naphthenate; cobalt naphthenate; zinc naphthenate; triethylamine; triethylenediamine; 2-methyltriethyleneamine; dibutyl tin dilaurate; metal carboxylates, including, but not limited to: organobismuth catalysts such as bismuth neodecanoate; zinc neodecanoate; zirconium neodecanoate; zinc 2-ethylhexanoate; sulfonic acids, including but not limited to dodecylbenzene sulfonic acid, methane sulfonic acid; amino or organo-base catalysts, including, but not limited to, 1,2-dimethylimidazole and diazabicyclooctane; triphenyl phosphine; alkoxides of zirconium and titanium, including, but not limited to Zirconium butoxide and Titanium butoxide; and Ionic liquid phosphonium salts; and tetradecyl(trihexyl) phosphonium chloride; and wherein a cured film of said radiation curable Primary Coating composition has a peak tan □ Tg of from about −25° C. to about −55° C.; and a modulus of from about 0.85 MPa to about 1.10 MPa.
摘要:
A free-radical radiation curable composition comprising:a) at least one compound containing from one to about six vinyl ether groups; andb) at least one compound containing a saturated backbone and at least one maleate or fumarate end group per molecule,wherein the ratio of vinyl ether groups to maleate or fumarate groups in the composition is in the range of about 5:1 to about 1:5.
摘要:
Photocurable liquid coating compositions adapted to provide primary coatings for optical glass fibers are disclosed. These compositions comprise polycarbonate-based acrylate-terminated polyurethane, an acrylate of an unsubstituted or C.sub.1 -C.sub.10 alkyl substituted phenol that is alkoxylated with a C.sub.2 -C.sub.4 alkylene oxide and at least one alkylacrylate having a T.sub.g below about -45.degree. C. Films produced from these ultraviolet light curable compositions are flexible and possess good water resistance and good wet adhesion.
摘要:
Ultraviolet curing oligomers and liquid coating compositions based thereon are disclosed which cure with ultraviolet light in the presence of a photoinitiator. The coating compositions can provide either a single coating for optical glass fiber which resists microbending difficulties down to around -40.degree. C., or a topcoat for overcoating softer buffer coatings which resist microbending down to around -60.degree. C. The coating compositions consist essentially of the linear polyacrylate-terminated polyurethane polyurea oligomer in admixture with an ultraviolet curable liquid acrylate or polyacrylate to provide the liquidity needed for application and to adjust the hardness or softness of the cured coating for the selected single coat or topcoat utility. The oligomer contains a linear polyurethane core terminated by urea formation with a polyhydroxy-functional amine containing a single isocyanate-reactive amino hydrogen atom. The plurality of hydroxy-terminated branches provided by the amine are capped with an acrylate-functional compound, and the several acrylate-functional branches increase the toughness and the cure speed.
摘要:
The invention relates to a Radiation Curable Secondary Coating composition for use on an Optical Fiber. The Radiation Curable Secondary Coating composition is a urethane-free Alpha Oligomer prepared by reaction of the following: (a) an acrylate compound selected from an alcohol-containing acrylate or alcohol-containing methacrylate compound, (b) an anhydride compound, (c) an epoxy-containing compound, (d) optionally an extender compound, and (e) optionally a catalyst. The invention also relates to a coated wire and to a coated optical fiber.
摘要:
The invention provides an optical fiber coated with a Supercoating, wherein the Supercoating comprises at least two layers, wherein the first layer is a Primary Coating that is in contact with the outer surface of the optical fiber and the second layer is a Secondary Coating in contact with the outer surface of the Primary Coating, wherein the cured Primary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity: A) a % RAU of from about 84% to about 99%;B) an in-situ modulus of between about 0.15 MPa and about 0.60 MPa; andC) a Tube Tg, of from about −25° C. to about −55° C.; wherein the cured Secondary Coating on the optical fiber has the following properties after initial cure and after one month aging at 85° C. and 85% relative humidity: A) a % RAU of from about 80% to about 98%; B) an in-situ modulus of between about 0.60 GPa and about 1.90 GPa; and C) a Tube Tg, of from about 50° C. to about 80° C.
摘要:
An occlusion system, method, and apparatus which treats an aneurysm in a primary vessel such as an intracranial vessel. Aneurysm types treatable by means of this invention include bulge (sometimes referred to as a true aneurysm), dissecting aneurysms in which the layers of vessel wall are partially delaminated, and what are referred to a “false” aneurysm defined by a relatively small opening in the parent vessel wall fluridically coupled to a bulb-shaped sac, also defined by the vessel wall. The system includes an occlusion device configured for deployment in the parent vessel that restricts fluid flow to the aneurysm. A patch on the device covers the neck of the aneurysm. The system includes a marker in a defined relationship with the patch, which allows for axial and rotational positioning of the device.
摘要:
Radiation curable coatings for use as a Primary Coating for optical fibers, optical fibers coated with said coatings and processes for coating optical fibers. The radiation curable Primary Coating composition of the instant claimed invention includes an oligomer, a diluent monomer; a photoinitiator; an antioxidant; and an adhesion promoter; wherein said oligomer is the reaction product of: a hydroxyethyl acrylate; an aromatic isocyanate; an aliphatic isocyanate; a polyol; a catalyst; and an inhibitor, wherein said oligomer has a number average molecular weight of from at least about 4000 g/mol to less than or equal to about 15,000 g/μmol; and wherein said catalyst is selected from the group consisting of dibutyl tin dilaurate; metal carboxylates, including, but not limited to: organobismuth catalysts such as bismuth neodecanoate; zinc neodecanoate; zirconium neodecanoate; zinc 2-ethylhexanoate; sulfonic acids, including but not limited to dodecylbenzene sulfonic acid, methane sulfonic acid; amino or organo-base catalysts, including, but not limited to: 1,2-dimethylimidazole and diazabicyclooctane; triphenyl phosphine; alkoxides of zirconium and titanium, including, but not limited to Zirconium butoxide and Titanium butoxide; and Ionic liquid phosphonium salts; and tetradecyl(trihexyl)phosphonium chloride; and wherein a cured film of said radiation curable Primary Coating composition has a peak tan delta Tg of from about −25° C. to about −45° C. and a modulus of from about 0.50 MPa to about 1.2 MPa.
摘要:
A new radiation curable Secondary Coating for optical fibers is described and claimed wherein said composition comprises a Secondary Coating Oligomer Blend, which is mixed with a first diluent monomer; a second diluent monomer; optionally, a third diluent monomer; an antioxidant; a first photoinitiator; a second photoinitiator; and optionally a slip additive or a blend of slip additives; wherein said Secondary Coating Oligomer Blend comprises: α) an Omega Oligomer; and β) an Upsilon Oligomer; wherein said Omega Oligomer is synthesized by the reaction of α1) a hydroxyl-containing (meth)acrylate; α2) an isocyanate; α3) a polyether polyol; and α4) tripropylene glycol; in the presence of α5) a polymerization inhibitor; and α6) a catalyst; to yield the Omega Oligomer; wherein said catalyst is selected from the group consisting of dibutyl tin dilaurate; metal carboxylates, including, but not limited to: organobismuth catalysts such as bismuth neodecanoate; zinc neodecanoate; zirconium neodecanoate; zinc 2-ethylhexanoate; sulfonic acids, including but not limited to dodecylbenzene sulfonic acid, methane sulfonic acid; amino or organo-base catalysts, including, but not limited to: 1,2-dimethylimidazole and diazabicyclooctane; triphenyl phosphine; alkoxides of zirconium and titanium, including, but not limited to Zirconium butoxide and Titanium butoxide; and Ionic liquid phosphonium salts; and tetradecyl(trihexyl)phosphonium chloride; and wherein said Upsilon Oligomer is an epoxy diacrylate.