摘要:
A solution polymerisation process carried out continuously in a cascade produces high molecular weight gel-free ethylene terpolymers having on the one hand high resistance to fuels, oils and organic solvents and on the other hand high flexibility even at low temperatures when narrow ranges are adhered to in respect of solvent content, pressure, temperature control and degree of conversion.
摘要:
High molecular weight, gel-free ethylene/vinyl acetate copolymers may be prepared by the process of solution polymerization if a particular relationship of temperature/pressure is observed.
摘要:
Ethylene/vinyl acetate solution polymers with increased strength and low gel content may be prepared by the copolymerization of small quantities of acryloyl or methacryloyl compounds.
摘要:
Gel-free ethylene/vinyl acetate copolymers with a high content of copolymerized vinyl acetate and a high Mooney viscosity are produced by carrying out the polymerization in solution in the presence of 20 to 45% by weight tert.butanol, based on the reaction solution, at temperatures of 50.degree. to 80.degree. C. and under pressures of 300 to 450 bar using azo compounds in a cascade of stirred reactors with an average residence time of the reaction solution in the reactor cascade of 5 to 9 hours and a conversion of 50 to 70% by weight, based on the vinyl acetate used. The ethylene/vinyl acetate copolymers produced by the process according to the invention may be used for the production of vulcanizates having improved mechanical properties.
摘要:
The random, hydrogenated copolymers according to the present invention of unsubstituted conjugated dienes and substituted conjugated dienes, having a glass transition temperature of ≦−60° C., an enthalpy of fusion of ≦100 J/g and a content of residual double bonds in the range from 0 to 80%, are suitable for the production of rubber moldings of all kinds which have good resistance to ageing and high resilience at low temperatures. In particular, various tire components and industrial rubber articles may be mentioned as rubber moldings. The copolymers are also suitable for the rubber modification of brittle thermoplastics.
摘要:
The random, hydrogenated copolymers according to the present invention of unsubstituted conjugated dienes and substituted conjugated dienes, having a glass transition temperature of ≦−60° C., an enthalpy of fusion of ≦100 J/g and a content of residual double bonds in the range from 0 to 80%, are suitable for the production of rubber moldings of all kinds which have good resistance to ageing and high resilience at low temperatures. In particular, various tire components and industrial rubber articles may be mentioned as rubber moldings. The copolymers are also suitable for the rubber modification of brittle thermoplastics.
摘要:
The invention relates to a polychloroprene rubber which shows advantages over the prior art in the sum total of its performance properties, namely vulcanization rate, tensile strength, elongation at break, modulus, tear propagation resistance and thermal stability of the vulcanizate.
摘要:
The present invention relates to a composition comprising thermoplastic materials and crosslinked microgels which are not crosslinked by high-energy radiation, processes for its preparation, its use for the production of thermoplastically processable shaped articles and shaped articles produced from the composition.
摘要:
The invention relates to a composition containing at least one microgel, at least one carbon nanotube and at least one organic medium. Said organic medium can be cross-linked or non cross-linked.