摘要:
There is provided a process for redispersing agglomerated noble metals such as platinum over the surface of certain tetrahedral crystalline oxides containing oxides of aluminum and phosphorus. Examples of such crystalline oxides include aluminophosphate (i.e. AlPO.sub.4 s), silicoaluminophosphates (i.e. SAPOs), ELAPSOs, MeAPOs, FeAPOs, TiAPOs and FCAPOs. The agglomerated noble metals may be redispersed by containing the supported noble metal with a suitable treating agent such as a stream of gas comprising molecular chlorine.
摘要:
An improved method for synthesis of improved silicoaluminophosphate SAPO-37 is provided. The method comprises (1) preparing a two-phase reaction mixture containing particular components and comprising both a liquid organic phase and a liquid aqueous phase; (2) heating the reaction mixture at a rate of from 5.degree. C. to 200.degree. C. per hour to a temperature of from 80.degree. C. to 200.degree. C.; agitating the reaction mixture in a manner sufficient to intimately admix said liquid organic and aqueous phases with each other; (4) once nucleation of the silicoaluminophosphate occurs, heating the agitated reaction mixture at rate of from 5.degree. C. to 200.degree. C. per hour to a temperature of from 100.degree. C. to 300.degree. C.; (5) maintaining the agitated reaction mixture at a temperature of from 100.degree. C. to 300.degree. C. and a pH of from 2 to 9 until crystals of the desired silicoaluminophosphate are formed; and (6) recovering silicoaluminophosphate material from the reaction mixture.
摘要:
A method for synthesizing a crystalline silicophosphoaluminate is provided. The composition has ion-exchange properties and is readily convertible to catalytically active material. The synthesis method requires an organic phase, and an aqueous phase. The silicon, phosphorus and aluminum components of the silicophosphoaluminate may, optionally, be replaced with other elements in the plus 4, 5 and 3 valence states, respectively.
摘要:
A new crystalline silicophosphoaluminate designated MCM-5 and having a particular crystal structure is provided. This crystalline material has ion-exchange properties and is readily convertible to catalytically active material.
摘要:
A catalytic composite comprising a combination of catalytically effective amounts of a platinum component, optionally a second metal component such as tin or rhenium, and a halogen component with a porous carrier support material is disclosed. The platinum, second metal (if present) and halogen components are present in the catalytic composite in amounts, calculated on an elemental basis, of about 0.2 to about 0.4 wt. percent platinum metal, about 0.2 to about 0.5 wt. percent the second metal, and 0.5 to about 1.5 wt. percent halogen. Moreover, the metallic components are substantially uniformly distributed throughout the porous carrier support material. The support material is spherical gamma alumina having a characteristic pore structure including "superpores" (200-10,000 nm or greater) interconnected with "mesopores" (5-20 nm), wherein 80% or more of the pore volume (N.sub.2) resides in pores of less than 150 .ANG..The principal use of the catalytic composite of the present invention is for hydrocarbon conversion, particularly in the reforming of a gasoline fraction.
摘要:
This invention relates to a new form of crystalline silicoaluminophosphate identified as SAPO-17, to a new and useful improvement in synthesizing said crystalline material and to use of said crystalline material prepared in accordance herewith as a catalyst for organic compound, e.g. hydrocarbon compound, conversion.
摘要:
A new composition comprising crystalline antimonophosphoaluminate, designated MCM-14, and the novel method for its synthesis are provided. The composition has ion-exchange properties and is readily convertible to catalytically active material. The synthesis method requires two liquid phases comprising a suitable organic or inorganic directing agent and specific reactants.
摘要:
A process for converting feedstock comprising hydrocarbon compounds to product comprising hydrocarbon compounds of lower molecular weight than said feedstock hydrocarbon compounds which comprises contacting said feedstock at conditions for said conversion with catalyst comprising crystals having a framework topology after heating at 110.degree. C. or higher giving an X-ray diffraction pattern with interplanar d-spacings at 16.4.+-.0.2 Angstroms, 8.2.+-.0.1 Angstroms, 6.21.+-.0.05 Angstroms, 6.17.+-.0.05 Angstroms, 5.48.+-.0.05 Angstroms and 4.74.+-.0.05 Angstroms, and without a significant interplanar d-spacing at 13.6-13.3 Angstroms.
摘要:
Disclosed is a vanadium trap for use in FCC which comprises a major amount of calcined kaolin clay, free magnesium oxide and an in situ formed magnesium silicate cement binder. Also disclosed are procedures for the preparation of the trap by forming a slurry in water of hydrous kaolin clay, magnesium oxide or magnesium hydroxide and sodium silicate, aging the slurry to form magnesium silicate in situ, optionally adding additional kaolin, colloidal silica or both, spray drying, and calcining the resulting spray dried microspheres without forming appreciable amounts of crystalline magnesium silicates or crystalline magnesium aluminates.
摘要:
Silicophosphoaluminates are crystallized from a two-phase reaction mixture comprising sources of silicon oxide, aluminum oxide and phosphorus oxide and a suitable directing agent. The silicophosphoaluminates produced have ion exchange properties and are readily convertible to catalytically active material.