摘要:
A process for converting feedstock comprising hydrocarbon compounds to product comprising hydrocarbon compounds of lower molecular weight than said feedstock hydrocarbon compounds which comprises contacting said feedstock at conditions for said conversion with catalyst comprising crystals having a framework topology after heating at 110.degree. C. or higher giving an X-ray diffraction pattern with interplanar d-spacings at 16.4.+-.0.2 Angstroms, 8.2.+-.0.1 Angstroms, 6.21.+-.0.05 Angstroms, 6.17.+-.0.05 Angstroms, 5.48.+-.0.05 Angstroms and 4.74.+-.0.05 Angstroms, and without a significant interplanar d-spacing at 13.6-13.3 Angstroms.
摘要:
This invention relates to a new synthetic crystalline microporous oxide material, a method for its preparation and use thereof in catalytic conversion of organic compounds. The new crystalline material exhibits a distinctive X-ray diffraction pattern.
摘要:
Natural and synthetic micorporous crystalline minerals that have a robust three-dimensional framework are modified by treatment with a molten salt that contains a component that reacts with the framework. Highly siliceous ZSM-5 and some aluminum phosphate compositions are catalytically activated by this method.
摘要:
A process is provided for converting light olefin to gasoline, distillate and lube range hydrocarbons which comprises contacting a lower olefin feedstock with acidic zeolite ZSM-48 at elevated pressure and temperature to provide product containing gasoline and distillate range hydrocarbons and a 650.degree. F.+ lube fraction.
摘要:
A spent acidic zeolite catalyst, e.g., ZSM-5 obtained from a hydrocarbon conversion process such as a catalytic dewaxing operation, is reactivated by contacting the spent catalyst with aqueous alkali metal carbonate and/or alkaline earth metal carbonate.
摘要:
Light olefins are converted to heavier hydrocarbon products, e.g., those boiling in the gasoline, distillate and/or lube range, over zeolite MCM-22 catalyst.
摘要:
Alumina-composited zeolite catalysts are activated by contact with an aqueous ammonium solution under ammonia gas pressure such that a pH of at least about 10 is maintained in the solution. The treated zeolite may thereafter be calcined without prior ammonium-exchange to provide the zeolite in the hydrogen form.
摘要:
C.sub.2 -C.sub.5 olefins and aromatics are prepared by catalytic conversion of lower aliphatic C.sub.1 -C.sub.4 oxygenates in the presence of a medium pore gallium containing zeolite catalyst having a ZSM-5 framework at elevated conversion temperatures. The process favors production of valuable unsaturated hydrocarbons and aromatics with low paraffin output.
摘要:
The ion-exchange capacity and acid catalytic activity of a ZSM-5 type zeolite are increased by treatment of a physical mixture of the zeolite and a solid source of aluminum with water in the presence of an alkali metal compound activating agent and an alkali metal salt of a mineral acid.